When carbon steel is subjected to atmospheric corrosion, the surface texture of the base metal becomes rougher due to corrosion attack. In this study, three-dimensional surface roughness analysis of the base metal of carbon steel samples exposed outdoors was performed to investigate this aspect of atmospheric corrosion. Corrosion loss was found to depend mainly on the number of days of exposure, the carbon content of the base metal and the core void volume. A high correlation coefficient was obtained, which suggests that analysis of surface texture can also be used as a means for determining atmospheric corrosion degradation.
McKenzieMVassiePR: ‘Use of weight loss coupons and electrical resistance probes in atmospheric corrosion tests’, Br. Corros. J.198520117–124.
2.
CastanoJCBoteroCARestrepoAHAgudeloEACorreaEEcheverriaF: ‘Atmospheric corrosion of carbon steel in Columbia’, Corros. Sci.201052216–223.
3.
NatesanMVenkatachariGPalaniswamyN: ‘Kinetics of atmospheric corrosion of mild steel, zinc galvanised iron and aluminium at 10 exposure stations in India’, Corros. Sci.200648, 3584-3608.
4.
LanTTNThoaNTPNishimuraRTujinoYYokoiMMaedaY: ‘Atmospheric corrosion of carbon steel under field exposure in the southern part of Vietnam’, Corros. Sci.200648179–192.
5.
NatesanMVenkatachariGPalaniswamyN: ‘Corrosivity and durability maps of India’, Corros. Prev. Control20055243–55.
6.
HassiotisNPetropoulosG: ‘Influence of surface roughness on corrosion resistance of turned carbon steel parts’, Int. J. Mach. Mach. Mater.20061202–212.
7.
LinM.-CLinS.-CLeeT.-HHuangH.-H: ‘Surface analysis and corrosion resistance of different stainless steel orthodontic brackets in artificial saliva’, Angle Orthod.200676322–329.
8.
ZhangJYangDOuX: ‘Microstructures and properties of aluminum film and its effect on corrosion resistance of AZ31B substrate’, Trans. Nonferrous Met. Soc. China200818s312–s317.
9.
BelousKPÉidukYuYaPonomarevaÉP: ‘The effect of surface roughness on corrosion resistance of ceramics’, Glass Ceram.198542417–420.
10.
MoayedMHLaycockNJNewmanRC: ‘Dependence of the critical pitting temperature on surface roughness’, Corros. Sci.200345, 1203-1216.
11.
NairnJDSkennertonSGAtrensA: ‘Comparative atmospheric corrosion of primary and cold rolled copper in Australia’, J. Mater. Sci.200338995–1005.
HoerleSMazaudierFDillmanPhSantariniG: ‘Advances in understanding atmospheric corrosion of iron. II. Mechanistic modelling of wet–dry cycles’, Corros. Sci.200446, 1431-1465.
14.
EyringHRobertsonBChuCCAndersenT: ‘Atmospheric corrosion (theoretical model)’, Proc. Natl. Acad. Sci. USA197471245–247.
15.
OhtsukaTKomatsuT: ‘Enhancement of electric conductivity of the rust layer by adsorption of water’, Corros. Sci.200547, 2571-2577.
WeiFI: ‘Atmospheric corrosion of carbon steels and weathering steels in Taiwan’, Br. Corros. J.199126209–214.
18.
‘Metals and alloys: atmospheric corrosion testing. General requirement for field tests’BS EN ISO 8565BSILondon, UK1995.
19.
VenkatasamyD: ‘Atlas for Mauritius’1st edn; 1991Rose HillThe Editions de l'Ocean Indien.
20.
‘Method of removal of corrosion products from corrosion tests specimens of metals and alloys’BS 7545, BSI, London, UK1991.
21.
BluntLJiangX: ‘Advanced techniques for assessment of surface topography – development of the basis for 3D surface texture standards “Surfstand” (Kogan Page Science paper edition)’17–43; 2003LondonButterworth-Heinemann.
22.
HanWYuGWangZWangJ: ‘Characterisation of initial atmospheric corrosion carbon steels by field exposure and laboratory simulation’, Corros. Sci.200749, 2920-2935.
23.
MorcilloMFeliuSSimancasJ: ‘Deviation from bilogarithmic law for atmospheric corrosion of steel’, Br. Corros. J.19932850–52.