The corrosion evolution of carbon steel exposed to an actual industrial atmosphere was investigated. The characteristics of the rust that formed on the steel were analysed by mass-loss measurement, X-ray diffraction, scanning electron microscopy and electrochemical techniques. Mass-loss results showed that the long-term corrosion kinetics of carbon steel can be divided into four stages, and that the corrosion rate varies during the different corrosion stages. This corrosion-rate fluctuation is attributed to the increase in the ambient temperature and the change in the composition of the rust layer formed on the steel surface. The reciprocal of charge transfer resistance (Rct) can be used to represent the corrosion rate. The backward-facing specimens were found to be more suitable as the objects to investigate the corrosion evolution. The evolution of the rust layer that formed on the steel is also discussed.
NatesanMVenkatachariGPalaniswamyN.Kinetics of atmospheric corrosion of mild steel, zinc, galvanized iron and aluminium at 10 exposure stations in India. Corros Sci. 2006; 48: 3584–3608. doi: 10.1016/j.corsci.2006.02.006
2.
WangJWangZYKeW.Characterization of rust formed on carbon steel after exposure to open atmosphere in Qinghai salt lake region. Corros Eng Sci Technol. 2012; 47: 125–130. doi: 10.1179/1743278211Y.0000000034
3.
KamimuraTHaraSMiyukiH.Composition and protective ability of rust layer formed on weathering steel exposed to various environments. Corros Sci. 2006; 48: 2799–2812. doi: 10.1016/j.corsci.2005.10.004
4.
TownsendHE.Effects of alloying elements on the corrosion of steel in industrial atmospheres. Corros. 2001; 57: 497–501. doi: 10.5006/1.3290374
5.
NishimuraTKatayamaHNodaKEffect of Co and Ni on the corrosion behavior of low alloy steels in wet/dry environments. Corros Sci. 2000; 42: 1611–1621. doi: 10.1016/S0010-938X(00)00018-4
6.
MaYTLiYWangFH.Corrosion of low carbon steel in atmospheric environments of different chloride content. Corro Sci. 2009; 51: 997–1006. doi: 10.1016/j.corsci.2009.02.009
7.
KamimuraTKashimaKSugaeKThe role of chloride ion on the atmospheric corrosion of steel and corrosion resistance of Sn-bearing steel. Corros Sci. 2012; 62: 34–41. doi: 10.1016/j.corsci.2012.04.049
8.
WangJWangZYKeW.Corrosion behavior of weathering steel in diluted Qinghai salt lake water in a laboratory accelerated test that involved cyclic wet/dey conditions. Mater Chem Phys. 2010; 124: 952–958. doi: 10.1016/j.matchemphys.2010.07.069
9.
TamuraH.The role of rusts in corrosion and corrosion protection of iron and steel. Corros Sci. 2008; 50: 1872–1883. doi: 10.1016/j.corsci.2008.03.008
10.
RodriguezJJSAlvarezCMGonzalezJEG.EIS characterization of the layer of corrosion products on various substrates in differing atmospheric environments. Mater Corros. 2006; 57: 350–356. doi: 10.1002/maco.200503872
11.
HanWYuGCWangZYCharacterization of initial atmospheric corrosion carbon steels by field exposure and laboratory simulation. Corros Sci. 2007; 49: 2920–2935. doi: 10.1016/j.corsci.2007.01.009
12.
HanWPanCWangZYInitial atmospheric corrosion of carbon steel in industrial environment. J Mater Eng Perform. 2015; 24: 864–874. doi: 10.1007/s11665-014-1329-5
13.
PanCHanWWangZYEvolution of initial atmospheric corrosion of carbon steel in an industrial atmosphere. J Mater Eng Perform. 2016; 25: 5382–5390. doi: 10.1007/s11665-016-2312-0
14.
MaYTLiYWangFH.The atmospheric corrosion kinetics of low carbon steel in a tropical marine environment. Corros Sci. 2010; 52: 1796–1800. doi: 10.1016/j.corsci.2010.01.022
MaYTLiYWangFH.Weatherability of 09CuPCrNi steel in a tropical marine environment. Corros Sci. 2009; 51: 1725–1732. doi: 10.1016/j.corsci.2009.04.024
17.
PérezFRBarreroCAWalkerARHEffects of chloride concentration, immersion time and steel composition on the spinel phase formation. Mater Chem Phys. 2009; 117: 214–223. doi: 10.1016/j.matchemphys.2009.05.045
18.
DongJHHanEHKeW.Introduction to atmospheric corrosion research in China. Sci Technol Adv Mater. 2007; 8: 559–565. doi: 10.1016/j.stam.2007.08.010
19.
AsamiKKikuchiM.In-depth distribution of rusts on a plain carbon steel and weathering steels exposed to coastal-industrial atmosphere for 17 years. Corros Sci. 2003; 45: 2671–2688. doi: 10.1016/S0010-938X(03)00070-2
20.
NishimuraTKatayamaHNodaKElectrochemical behavior of rust formed on carbon steel in a wet/dry environment containing chloride ions. Corros. 2000; 56: 935–941. doi: 10.5006/1.3280597
21.
HaoLZhangSXDongJHEvolution of corrosion of MnCuP weathering steel submitted to wet/dry cyclic tests in a simulated coastal atmosphere. Corros Sci. 2012; 58: 175–180. doi: 10.1016/j.corsci.2012.01.017
22.
ChengYLZhangZCaoFHA study of the corrosion of aluminum alloy 2024-T3 under thin electrolyte layers. Corros Sci. 2004; 46: 1649–1667. doi: 10.1016/j.corsci.2003.10.005
23.
MisawaTAsamiKHashimotoKThe mechanism of atmospheric rusting and the protective amorphous rust on low alloy steel. Corros Sci. 1974; 14: 279–289. doi: 10.1016/S0010-938X(74)80037-5
24.
ChenYYTzengHJWeiLICorrosion resistance and mechanical properties of low-alloy steels under atmospheric conditions. Corros Sci. 2005; 47: 1001–1021. doi: 10.1016/j.corsci.2004.04.009
25.
ChandlerKAStannersJE.Proceeding of the Second International Congress on Metallic Corrosion, NACE, New York, Houston, TX; 1963, p. 325.