Cold metal transfer (CMT) welding is a promising process to improve the mechanical characteristics of the hard to weld 7075-T6 aluminium alloy owing to its unique advantages in contrast to conventional metal inert gas welding process. The welded joints, using ER5356, were identified and characterised by means of optical microscopy, scanning electron microscopy and energy dispersive spectroscopy. Mechanical properties were measured by tensile and hardness tests. Results indicate that CMT provides better joint tensile strength and ductility compared to metal inert gas welding. The softness in the heat affected zone was very low, but a big hardness gap was recognised in the welded metal compared to base metal. The joint had mechanical property coefficients of 77%, 60% and 69% for yield strength, ultimate tensile strength and elongation respectively.
CrossC. E., OlsonD. L. and LiuS.: ‘Aluminum welding’, in ‘Handbook of aluminum. Vol. 1: physical metallurgy and processes’, (eds. TottenG. E. and MacKenzieD. S.., 1, 481–532; 2003, New York, Marcel Dekker Inc.
6.
RafiH. K., RamG. D. J., PhanikumarG. and PrasadR. K.: ‘Microstructure and tensile properties of friction welded aluminum alloy AA7075-T6’, Mater. Des., 2010, 31, 2375–2380.
7.
da SilvaA. A. M., ArrutiE., JaneiroG., AldanondoE., AlvarezP. and EcheverriaA.: ‘Material flow and mechanical behaviour of dissimilar AA2024-T3 and AA7075-T6 aluminium alloys friction stir welds’, Mater. Des., 2011, 32, 2021–2027.
8.
SevimI., HayatF., KayaY., KahramanN. and S¸ahinS.: ‘The study of MIG weldability of heat-treated aluminum alloys’, Int. J. Adv. Manuf. Technol., 2013, 66, 1825–1834.
9.
KearnsW. H.: ‘Metals and their weldability’4. 7th edn, 316–387; 1982, Doral, FL, American Welding Society.
10.
KalpakjianS. and SchmidS. R.: ‘Joining processes and equipment’, in ‘Manufacturing engineering and technology’, 5th edn, 936–1016; 2006, Upper Saddle River, NJ, Pearson Education.
11.
AntonssonG.: ‘Springer handbook of mechanical engineering’, 656–672; 2008, Berlin, Springer.
12.
RosadoT., AlmeidaP., PiresI., MirandaR. and QuintinoL.: ‘Innovation in arc welding’, in ‘Proc. 5°Congresso de Engenharia de Moçambique’, Maputo, September1, 1–18; 2008.
13.
PickinC. G. and YoungK.: ‘Evaluation of cold metal transfer (CMT) process for welding aluminium alloy’, Sci. Technol. Weld. Join., 2006, 11, 583–585.
14.
CaoR., JingM., FengZ. and ChenJ. H.: ‘Cold metal transfer welding-brazing of magnesium to pure copper’, Sci. Technol. Weld. Join., 2014, 19, 451–460.
15.
CaoR., SunJ. H. and ChenJ. H.: ‘Mechanisms of joining aluminium A6061-T6 and titanium Ti–6Al–4V alloys by cold metal transfer technology’, Sci. Technol. Weld. Join., 2013, 18, 425–433.
16.
LinJ., MaN., LeiY. and MurakawaH.: ‘Shear strength of CMT brazed lap joints between aluminum and zinc-coated steel’, J. Mater. Process. Technol., 2013, 213, 1303–1310.
17.
ZhouY. and LinQ.: ‘Wetting of galvanized steel by Al 4043 alloys in the first cycle of CMT process.’, J. Alloys Compd, 2014, 589, 307–313.
18.
ShangJ., WangK., ZhouQ., ZhangD., HuangJ. and LiG.: ‘Microstructure characteristics and mechanical properties of cold metal transfer welding Mg/Al dissimilar metals’, Mater. Des., 2012, 34, 559–565.
19.
AhmadR. and BakarM. A.: ‘Effect of a post-weld heat treatment on the mechanical and microstructure properties of AA6061 joints welded by the gas metal arc welding cold metal transfer method’, Mater. Des., 2011, 32, 5120–5126.
20.
BeytullahG., ErdincK., EmelT.S S. and AydinS. I. K.: ‘Mechanical and microstructural properties of robotic cold metal transfer (CMT) welded 5083-H111 and 6082-T651 aluminum alloys’, Mater. Des., 2014, 54, 207–211.
21.
ShuaF., LvY., LiuY., XuaF., SunZ., HeaP. and XuaB.: ‘Residual stress modeling of narrow gap welded joint of aluminum alloy by cold metal transferring procedure’, Constr. Build. Mater., 2014, 54, 224–235.
22.
FrappierR., BenoitA., PaillardP., BaudinT., Le GallR. and DupuyT.: ‘Quantitative infrared analysis of welding processes: temperature measurement during RSW and CMT-MIG welding’, Sci. Technol. Weld. Join., 2014, 19, 38–43.
23.
Deutsche Norm: ‘Prüfung metallischer Werkstoffe–Zugproben’, Deutsches Institut für Normung DIN 50125; 2009.
24.
StasikM. C. and WagonerR. H.: ‘Forming of tailor-welded aluminum blanks’, Int. J. Form. Processes, 1998, 1, 9–33.
25.
TuJ. F. and PaleocrassasA. G.: ‘Fatigue crack fusion in thin-sheet aluminum alloys AA7075-T6 using low-speed fiber laser welding’, J. Mater. Process. Technol., 2011, 95–112.
26.
SivashanmugamM., JothiS. C., KumarT. and SathishkumarM.: ‘Investigation of microstructure and mechanical properties of GTAW and GMAW joints on AA7075 aluminum alloy’, Int. J. Des. Manuf. Technol., 2009, 3, 56–62.
27.
BalasubramanianV., RavisankarV. and ReddyG. M.: ‘Influences of pulsed current welding and post weld aging treatment on fatigue crack growth behaviour of AA7075 aluminium alloy joints’, Int. J. Fatigue, 2008, 30, 405–416.
28.
AshtonR. F., WesleyR. P. and DixonC. R.: ‘The effect of porosity on 5086-H116 aluminum alloy welds’, Weld. J., N.D., 95s–98s.
29.
PetrovD. A.: ‘Aluminium–magnesium–zinc’, in ‘Ternary alloys’, (eds. PetzowG. and EffenbergG..,7, 57–71; 1993, Materials Park, OH, ASM International.
30.
LiangH., ChenS. -L. and ChangY. A.: ‘A thermodynamic description of the Al–Mg–Zn system’, Metall. Mater. Trans. A, 1997, 28A, 1725–1734.
31.
MaT. and den OudenG.: ‘Softening behaviour of Al–Zn–Mg alloys due to welding’, Mater. Sci. Eng. A, 1999, A266, 198–204.
32.
HwangR. Y. and ChouC. P.: ‘The study on microstructural and mechanical properties of weld heat affected zone of 7075-T6 aluminum alloy’, Scr. Mater., 1998, 38, 215–221.
33.
Lech-GregaM., HawrylkiewiczS., RichertM. and SzymańskiW.: ‘Structural parameters of 7020 alloy after heat treatment simulating the welding process’, Mater. Charact., 2001, 46, 251–257.
34.
SivashanmugamM., ManoharanN., AnanthapadmanabanD. and KumarS. R.: ‘Investigation of microstructure and mechanical properties of GTAW and GMAW joints on AA7075 aluminum alloy’, Int. J. Des. Manuf. Technol., 2009, 3, 56–62.
35.
WuS. C., YuX., ZuoR. Z., ZhangW. H., XieH. L. and JiangJ. Z.: ‘Porosity, element loss, and strength model on softening behaviour of hybrid laser arc welded Al–Zn–Mg–Cu alloy with synchrotron radiation analysis’, Weld. J., 2013, 92, 64s–71s.
36.
SivashanmugamM., KumarK. A., NavasR. K. B. and AhamedM. A. E.: ‘Effect of process parameters on tensile strength in gas metal arc welded joints aa7075-t6 aluminum alloy using regression and response surface model’, Int. J. Res. Eng. Technol., 2014, 3, 163–166.
37.
KinseyB. and WuX.: ‘Tailor welded blanks for advanced manufacturing’, 31–32; 2011, Cambridge, UK, Woodhead Publishing.
38.
DixitU. S. and NarayananR. G.: ‘Metal forming: technology and process modelling’, 134–135; 2013, New Delhi, Tata McGraw Hill Education Private Limited.
39.
TemmarM., HadjiM. and SahraouiT.: ‘Effect of post-weld aging treatment on mechanical properties of tungsten inert gas welded low thickness 7050°aluminium alloy joints’, Mater. Des., 2011, 32, 3532–3536.
40.
LiuC., NorthwoodD. O. and BholeS. D.: ‘Tensile fracture behavior in CO2 laser beam welds of 7075-T6 aluminum alloy’, Mater. Des., 2004, 25, 573–577.
41.
SivarajP., KanagarajanD. and BalasubramanianV.: ‘Effect of post weld heat treatment on tensile properties and microstructure characteristics of friction stir welded armour grade AA7075-T651aluminium alloy’, Defence Technol., 2014, 10, 1–8.
42.
RajakumarS., MuralidharanC. and BalasubramanianV.: ‘Optimization of the friction-stir-welding process and tool parameters to attain a maximum tensile, strength of AA7075–T6 aluminium alloy’, P.I. Mech. Eng. B-J. Eng. Manuf., 2010, 224, 1175–1191.
43.
RajakumarS., MuralidharanC. and BalasubramanianV.: ‘Influence of friction stir welding process and tool parameters on strength properties of AA7075-T6 aluminium alloy joints’, Mater. Des., 2011, 32, 535–549.
44.
ZadpoorA. A., SinkeJ., BenedictusbR. and PietersbR.: ‘Mechanical properties and microstructure of friction stir welded tailor-made blanks’, Mater. Sci. Eng. A, 2008, A494, 281–290.