DP590 steel sheets were joined by friction stir spot welding using polycrystalline cubic boron nitride tool with an objective to produce bond diameters similar to conventional spot welding nuggets. A range of spindle rotation (400–2400 rev min−1) and plunge speeds (0·03–3·8 mm s−1) were exercised to attain defect free welds in 1·6 mm thick sheets. A bond diameter of 4t1/2, alike minimum nugget diameter criteria for resistance spot welds, resulted in superior mechanical properties than conventional spot welds. The heat inputs corresponding to different welding parameters influenced the weld microstructure, including grain size, phases and their morphology. The bond diameter was higher for higher heat inputs. However, low heat input welds with weld time cycles ∼4 s produced more refined microstructure and exhibited similar strengths even with reduced bond size. Plug type failure was associated with larger bond diameters (∼7·1 mm), while interfacial failure was observed with smaller welds (∼5·4 mm).
KonkolPJ, MathersCJA, JohnsonR and PickensJR: J. Ship Prod., 2003, 19, 159–164.
7.
HiranoS, OkamotoK, AotaK and InagakiM: ‘Metallurgical and mechanical properties of friction stir welded ultra-fine grained steel’, Proc. 5th Int. Symp. on ‘Friction stir welding’, Meta, France, September 2004, TWI. Paper No: P28, ISBN No: 1903761042.
8.
OzekcinA, JinHW, KooJY, BangaruNV and AyerR: Int. J. Offshore Polar Eng., 2004, 14, (4), 284–288.
9.
UejiR, FujiiH, CuiL, NishiokaA, KunishigeK and NogiK: Mater. Sci. Eng. A, 2006, A423, (1–2), 324–330.
10.
HaagensenPJ, MidlingOT and RanesM: Proc. 2nd Int. Conf. on ‘Computer methods and experimental measurements for surface treatment effects’, Milan, Italy, June 1995, Wessex Institute of Technology, 225–237.
11.
LienertTJ, GryllsRJ, GouldJE and FraserHL: Proc. 2nd Symp. held at the 1998 TMS Fall Meet.: ‘Hot deformation of aluminum alloys’, Rosemont, IL, USA, October 1998, TMS, 159–167.
12.
KinchenDG, LiZ and AdamsGP: Proc. 1st Int. Conf. on ‘Friction stir welding’, ‘Mechanical properties of friction stir welds in Al-Li 2195-T8’. Format: CD-ROM. Thousand Oaks, CA, USA, June 1999, TWI.
GhoshM, KumarK and MishraRS: Mater. Sci. Eng. A, 2011, A528, (28), 8111–8119.
33.
RodriguesP, PaulaAS and CamposMF: ‘Mechanical behaviour and microstructural evolution during hot rolling in pilot scale of low carbon steels with Mn additions’, Proc. 6th Brazilian Conf. on ‘Manufacturing engineering’, Caxias do Sul, RS, Brazil, April 2011, Associação Brasileira de Engenharia e Ciências Mecânicas, http://alvarestech.com/temp/cobef2011/grima.ufsc.br/cobef2011/media/trabalhos/COF11-0189.pdf
HicksonMR, HurleyPJ, GibbsRK, KellyGL and HodgsonPD: Metall. Mater. Trans. A, 2002, 33A, 1019–1026.
36.
FujiiH, CuiL, TsujiN, MaedaM, NakataK and NogiK: Mater. Sci. Eng. A, 2006, A429, 50–57.
37.
BabuSS: Curr. Opin. Solid State Mater. Sci., 2004, 8, 267–278.
38.
DallamCB and OlsonDL: Weld. J., 1989, 68, 198–205.
39.
IrieT, SatohS, HasiguchiK, TakahashiI and HashimotoO: ‘Metallurgical factors affecting the formability of cold-rolled high strength steel sheets’, Proc. 100th ISIJ Meet., Fukuoka, Japan, October 1980, Kyushu University, 793–801.