Al–Mg–Si alloys are known to be highly susceptible to solidification cracking. Weldability results of laminated AA6061-T6 plates are presented in this paper when welded in full penetration keyhole mode using a 1030 nm, 10 kW Yb:YAG disk laser welding source with different welding conditions. Making use of the controlled restraint weldability (CRW) cracking test, a boundary has been established between crack and no crack conditions for different preloads. The originality of the CRW test is the cross-shaped test coupon that partitions the pre-stress unequally along the welding path. The CRW is proven capable of ranking the solidification cracking behaviour of weld metals deposited under different welding conditions.
MousaviMG, CrossCE, GrongØ: ‘Effect of scandium and titanium-boron on grain refinement and hot cracking of aluminum alloy 7108’, Sci. Technol. Weld. Join., 1999, 4, (6), 381–388.
6.
EskinDG, KatgermanL: ‘A Quest for a new hot tearing criterion’, Metall. Mater. Trans. A, 2007, 38A, (7), 1511–1519.
7.
EskinDG, SuyitnoWH, KatgermanL: ‘Mechanical properties in the semi-solid state and hot tearing of aluminum alloys’, Prog. Mat. Sci., 2004, 49, 629–711.
8.
CrossCE: ‘On the origin of weld solidification cracking’, in: ‘Hot cracking phenomena in welds’, 3–18; 2005, Springer Pub.
9.
SuyitnoWHKool, KatgermanL: ‘Hot tearing criteria evaluation for direct-chill casting of an Al-4·5 Pct Cu alloy’, Metall. Mater. Trans. A, 2005, 36A, (6), 1537–1546.
10.
CrossCE, ConiglioN: ‘Weld solidification cracking: critical conditions for crack initiation and growth’, in ‘Hot cracking phenomena in welds II’, 39–58; 2008, Springer.
11.
ConiglioN, CrossCE: ‘Initiation and growth mechanisms for weld solidification cracking’, Int. Mat. Rev., In Press.
12.
SaveikoVN: ‘Theory for hot cracking’, Russ. Cast Prod, 1961, 453–456.
13.
DickhausCH, OhmL, EnglerS: ‘Mechanical properties of solidifying shells of aluminum alloys’, AFS Trans., 1994, 101, 677–684.
14.
LahaieDJ, BouchardM: ‘Physical modeling of the deformation mechanisms of semisolid bodies and a mechanical criterion for hot tearing’, Metall. Mater. Trans. B, 2001, 32B, (8), 697–705.
15.
PelliniWS: ‘Strain theory for hot tearing’, Foundry, 1952, 80, 125–199.
16.
ProkhorovNN: ‘The problem of the strength of metals while solidifying during welding’, Svar. Proiz., 1956, 6, 5–11.
17.
SendaT, MatsudaF, TakanoG, WatanabeK, KobayashiT, MatsuzakaT: ‘Experimental investigations on solidification crack susceptibility for weld metals with trans-varestraint test’, Trans JWS, 1971, 2, (2), 141–162.
18.
PumphreyWI, JenningsPH: ‘A consideration of the nature of brittleness at temperature above the solidus in castings and welds in aluminum alloys’, J. Inst. Met., 1948, 75, 235–256.
19.
BorlandJC: ‘Generalized theory of super solidus cracking in welds and castings – an initial development’, Brit. Weld. J., 1960, 7, (8), 508–512.
20.
RappazM, DrezetJM, GremaudM: ‘A new hot tearing criterion’,
Metall. Mater. Trans.A, 1999, 30A, 449–455.
21.
ConiglioN, CrossCE: ‘Mechanisms for solidification crack initiation and growth in aluminum welding’, Metall. Mater. Trans. A, 2009, 40A, 2718–2728.
22.
ChihoskiRA: ‘The character of stress field around a weld arc moving on aluminum sheet’, Weld. J., 1972, 51, (1), 9s–18s.
23.
ChihoskiRA: ‘Expansion and stress around aluminum Weld puddles’, Weld. J., 1979, 58, (9), 263s–276s.
24.
ZachariaT: ‘Dynamic stresses in weld metal hot cracking’, Weld. J., 1994, 73, (7), 164s–172s.
25.
KannengiesserTh, McInerneyT, FlorianW, BöllinghausTh, CrossCE: ‘The influence of local weld deformation on hot cracking susceptibility’, in ‘Mathematical modeling of weld phenomena 6’, 803–817; 2002, London, Maney.
26.
MurakawaH, SerizawaH, ShibaharaM: ‘Prediction of welding hot cracking using temperature dependent interface element’, in ‘Mathematical modeling of weld phenomena 7’, 539–554; 2003, Maney.
27.
WilliamsJA, SingerARE: ‘Deformation, strength, and fracture above the solidus temperature’, J. Inst. Met., 1968, 96, 5–12.
28.
SuyitnoWHKool, KatgermanL: ‘Micro-mechanical model of hot tearing at triple junctions in DC casting’, Mater. Sci. Forum, 2002, 396–402, 179–184.
29.
GrandfieldJF, DavidsonCJ, TaylorJA: ‘Application of a new hot tearing analysis to horizontal direct chill cast magnesium alloy AZ91’, in ‘Light metals 2001’, 895–901; 2001, Warrendale, PA, TMS.
30.
BracciniM, MartinCL, SuéryM, BréchetY: ‘Relation between the Mushy Zone rheology and hot tearing phenomena in Al-Cu alloys’, in ‘Modeling of casting, welding, and advanced solidification processes IX’, 19–24; 2000, Aachen, Shaker Verlag.
CrossCE, ConiglioN, SchemppP, MousaviM: ‘Critical conditions for weld solidification crack growth’, in ‘Hot cracking phenomena in welds III’, 25–41; 2011, Springer.
33.
RobinoCV, ReeceM, KnorovskyGA, DuPontJN, FengZ: ‘Prediction of maximum crack length in longitudinal varestraint testing’, Proc. 7th Int. Conf. on ‘Trends in welding research’, 313–318; 2005, Materials Park, OH, ASM International.
SchobbertH, BöllinghausTh, WolfM: ‘Hot cracking resistance of laser and hybrid welded austenitic stainless steels’, in ‘Trends of welding research’, 76–81; 2003, Materials Park, OH, ASM International.
36.
NishimotoK, MoriH: ‘Hot cracking susceptibility in laser weld metal of high nitrogen stainless steels’, Sci. Technnol. Adv. Mater., 2004, 5, 231–240.
37.
WeiseS: ‘Hiessrissbildung beim Laserstrahlschweissen von Baustählen’, thesis, University of Bremen, 1998.
38.
CrossCE, ConiglioN, WestingEM, GumenyukA: ‘Laser weldability of stainless steel’, in ‘Hot cracking phenomena in welds III’, 131–144; 2011, Springer.
39.
CieslakMJ, FuerschbachPW: ‘On the weldability, composition, and hardness of pulsed and continuous Nd:YAG laser welds in aluminum alloys 6061, 5456, and 5086’.Met. Trans. B, 1988, 19B, 319–329.
40.
PloshikhinV, PrikhodovskyA, MakhutinM, IlinA, ZochHW: ‘Integrated mechanical-metallurgical approach to modeling of solidification cracking in welds’, in ‘Hot cracking phenomena in welds’, 223–244; 2005, Springer.
41.
HuangA, ZhangH, LiuJ, YuW, LiZ, LiH: ‘Study on solidification crack criterion during laser welding pure aluminum and ZL114A aluminum alloy’, Adv. Mater. Res., 2011, 308–310, 852–858.
42.
JenningsPH, SingerARE, PumphreyWI: ‘Hot shortness of some high-purity alloys in the systems aluminum-copper-silicon and aluminum-magnesium-silicon’, J. Inst. Met., 1948, 74, 227–248.
43.
CicalăE, DuffetG, AndrzejewskiH, GreveyD, IgnatS: ‘Hot cracking in Al-Mg-Si alloy laser welding – operating parameters and their effects’, Mater. Sci. Eng. A, 2005, A395, 1–9.
44.
FabregueD, DeschampsA, SuéryM, ProudhonH: ‘Hot tearing during butt welding of 6xxx Al alloys: process optimisation and 2D/3D characterisation of hot tears’, in ‘Hot cracking phenomena in welds II’, 241–253; 2007, Springer.
45.
YoonJW, LeeYS, LeeKD, ParkKY: ‘Effect of filler wire composition on the Nd:YAG laser weldability of 6061 aluminum alloy’, Mater. Sci. Forum, 2005, 475–479, 2591–2594.
46.
DrezetJM, MathierV, AllehauxD: ‘Finite element modelling of laser beam welding of aluminum alloys with special attention to hot cracking in transient regimes’, in ‘Mathematical modelling of weld phenomena 8’, 137–152; 2006, Verlag der Techn. Univ. Graz.
47.
DrezetJM, KurzW, LimaMSF: ‘On the use of double laser source for crack-free welds of aluminum alloys’, Proc. LASERAP'6, 2007.
48.
DrezetJM, LimaMSF, WagniereJD, RappazM, KurzW: ‘Crack-free aluminium alloy welds using a twin laser process’, Proc. IIW Int. Conf., Verlag der Techn. Univ. Graz, 87–94, 2008.
49.
MichaudEJ, KerrHW, WeckmanDC: ‘Temporal pulse shaping and solidification cracking in laser welded Al-Cu alloys’, in ‘Trends in welding research (Proc. 4th Int. Conf)’, 153–158; 1995, ASM.
50.
ZhangJ, WeckmanDC, ZhouY: ‘Effect of temporal pulse shaping on cracking susceptibility of 6061-T6 aluminum Nd:YAG laser welds’, Weld. J., 2008, 87, (1), 18s–30s.
51.
MatsudaF, NagakawaH, NakataK, OkadaH: ‘The VDR cracking test for solidification crack susceptibility on weld metals and its application to aluminum alloys’, Trans. JWRI, 1979, 8, 85–95.
52.
ConiglioN, CrossCE: ‘Weld parameter and minor element effects on solidification crack initiation in aluminum’, in ‘Hot cracking phenomena in welds II’, 277–310; 2008, Springer.
53.
WilkenK, KleistnerH: ‘Remarks on the classification and evaluation of hot cracking tests’, IIW-Doc. IX-1379–85, International Institute of Welding, Paris, 1985.
54.
GoodwinGM: ‘Development of a new hot cracking test – the Sigmajig’, Weld. J., 1987, 66, 33s–38s.
55.
ConiglioN, CrossCE, MichaelTh, LammersM: ‘Defining a critical weld dilution to avoid solidification cracking in aluminum’, Weld. J., 2008, 87, (8), 237s–247s.
56.
HouldcroftPT: ‘A simple cracking test for use with argon-arc welding’, Brit. Weld. J., 1955, 2, 471–475.