Resistance spot welding experiments were conducted on dissimilar material combination of HSLA350/DP600 steels. The welds were characterised using optical and scanning electron microscopy. The fusion zone of the dissimilar material spot weld was predominantly martensitic with some bainite. Mechanical properties were also determined by tensile shear, cross tension and fatigue tests. The performance of dissimilar material spot weld was different from that of the similar ones in each of the HSLA350 and DP600 steels and exhibited different heat affected zone hardness. The DP600 weld properties played a dominating role in the microstructure and tensile properties of the dissimilar material spot welds. However, the fatigue performance of the dissimilar welds was similar to that of the HSLA350 welds. Fatigue tests on the dissimilar material spot welds showed that the 5·5 mm diameter nugget exhibited higher fatigue strength than the 7·5 mm diameter nugget.
‘Advanced high strength steel (AHSS) application guideline, Version. 3’; 2006, Middletown, OH, International Iron and Steel Institute Committee on Automotive Applications.
2.
KhanM.I., KuntzM. L. and ZhouY.: Sci. Technol. Weld. Joining, 2008, 13, 294–304.
HernandezV. H. B., MichaelL. K., NormanY. Z., ChanR. K. and ScotchmerN.: Proc. XIII Conf. on ‘Sheet metal welding’, Detroit, MI, May 2008, American Welding Society, Paper 1–3.
5.
SunZ. and KarppiR.: Mater. Process. Technol., 59, 1996, 257–267.
6.
KacarR. and HasanbasogluA.: Mater. Design, 2007, 28, 1794–1800.
7.
HasanbasogluA. and KacarR.: J. Mater. Sci. Technol., 2006, 22, 375–81.
8.
AleniusM., PohjanneP., SomervuoriM. and HänninenH.: Weld. J., 2006, 85, 305s–313s.
9.
SunX., StephensE. V., KhaleelM. A., ShaoH. and KimchiM.: Weld. J., 2004, 83, 188-S–195–S.
10.
‘Specification for automotive weld quality resistance spot welding of steel’, AWS D8·1M, New York, American National Standard, 2007.
11.
‘Method of fatigue testing for spot welded joint’; JIS-3138, Japan, Japanese Standards Association, 1989.
12.
MaryaM. and GaydenX. Q.: Weld. J., 2005, 84, 172-s–182–s.
13.
‘Technical transfer dispatch no. 6 – Body structure materials, ULSAB-AVC Consortium’; 2001, South Field, MI, American Iron and Steel Institute
14.
ShomeM. and MohantyO. N.: Metall. Mater. Trans. A, 2006, 37A, 2159–2169.
15.
EasterlingK.: ‘Introduction to physical metallurgy of welding’, 2nd edn, 76–89, 191–209; 1992, London, Butterworth Heinemann.
16.
GouldJ. E., KhuranaS. P. and LiT.: Weld. J., 2006, 85, 111-s–116–s.
17.
TumuluruM. D.: Weld. J., 2006, 85, 31–37.
18.
JoaquinA., ElliotA. A. and JiangC.: Weld. J., 2007, 86, 24–27.
19.
MaC., ChenD. L., BholeS. D., BoudreauG., LeeA. and BiroE.: Mater. Sci. Eng. A, 2008, A485, 334–346.
20.
KhanM. S., BholeS. D., ChenD. L, BoudreauG., BiroE. and DeventerJ. V.: Proc. XIII Conf. on ‘Sheet metal welding’, Detroit, MI, May 2008, American Welding Society, Paper 1–4.