Improving vibration weld joint strength through process and equipment modifications

Abstract

Vibration welding is a process used to join thermoplastic components. Currently, under optimised low pressure welding, the weld strength of butt joints of unreinforced polymer can be equivalent to the strength of unwelded material. However, in short glass fibre reinforced polymer, the optimised weld strength is significantly lower than that of unwelded material and is closer to the strength of the resin matrix. This lower strength is attributable to the unfavourable orientation of the short glass fibres in the weld zone. The fibres tend to align parallel and in the plane of the weld zone and thus provide no reinforcement in the direction perpendicular to the weld zone. In the present work the impact of various modifications to the existing vibration welding technology was examined, with the objective of increasing the current achievable weld strength of glass reinforced nylon. The introduction of a secondary vibratory motion perpendicular to the weld plane during welding resulted in strengths 20% higher than those of samples welded using the standard vibration welding process.

Keywords

VIBRATION WELDING NYLON STRENGTH

Get full access to this article

View all access options for this article.

References

Stokes

V. K.

: J. Polym. Eng. Sci., 1988, 28, 728–739.

Stokes

V. K.

: J. Polym. Eng. Sci., 1988, 28, 989–997.

Stokes

V. K.

: J. Polym. Eng. Sci, 1988, 28, 998–1008.

Mah

and Bates

P. J.

: ‘Microstructure of vibration welded nylon 66’, Society of Plastic Engineers Annual Technical Conference, Dallas, TX, USA, May 2001.

Laflamme

: ‘Advances in joining technology to vibration welding of carpet and fabric to interior door panels and other interior components’, Paper 980996, Society of Automotive Engineers, Detroit, MI, 1998.

Tucker

B. D.

: ‘Improving vibration weld joint strength through process and equipment modifications’, MEng. thesis, Royal Military College of Canada, Kingston, Ont., Canada, 2001.

Macdonald

J. J.

: ‘Meltdown-time profiles of vibration welded nylon 66 compounds’ Society of Plastic Engineers Annual Technical Conference, Dallas, TX, USA, May 2001.

Giese

and Ehrenstein

G. W.

: ‘Identification of phase 3 in the vibration welding process’, Society of Plastics Engineers Annual Technical Conference, New Orleans, LA, USA, 1993.

Potente

and Uebbing

: J. Thermoplast. Compos. Mater., 1993, 6, 147–159.

10.

Schlarb

A. K.

and Ehrenstein

G. W.

: J. Polym. Eng. Sci., 1989, 29, 1677–1682.

11.

Potente

, Uebbing

and Lewandowski

: J. Thermoplast. Compos. Mater., 1993, 6, 2–17.

12.

Froment

I. D.

: ‘Vibration welding nylon 6 and nylon 66 – a comparative study’, Society of Plastics Engineers Annual Technical Conference, Boston, MA, USA, 1995.

13.

Kagan

, Lui

S. C.

and Smith

G. R.

: ‘The optimized performance of linear vibration welded nylon 6 and nylon 66 butt joints’, Society of Plastics Engineers Annual Technical Conference, Indianapolis, IN, USA, 1996.

14.

Potente

and Uebbing

: J Thermoplast. Compos. Mater., 1993, 6, 2–17.

15.

Mccrum

N. G.

, Buckley

C. P.

and Bucknall

C. B.

: ‘Principles of polymer engineering’, 257; 1997, Oxford, UK, Oxford University Press.

16.

‘Standard test method for tensile properties of plastics’, Standard D638–03, ASTM, West Conshohocken, PA, USA, 2003.

17.

‘Plastics – determination of tensile properties – part 2: test conditions for moulding and extrusion plastics’, Standard ISO 527, ISO, Geneva, Switzerland, 1993.

18.

Mah

J. C.

: ‘Evaluation of vibration welds in an automotive air intake manifold’, MEng. thesis, Queen's University, Kingston, Ont., Canada, 2002.