Liquation cracking in partial penetration aluminium welds: Assessing tendencies to liquate,crack and backfill

Abstract

Aluminium alloys are susceptible to liquation cracking in the partially melted zone (PMZ), where grain boundary liquation occurs during welding. Alloys 2024, 6061 and 7075 were gas-metal arc welded with fillers 1100 and 4043, and liquation cracking near the weld root was examined. Curves of temperature (T) versus solid fraction (f_S), based on the Scheil equation for Al-Cu-Mg-Mn-Si-Zn alloys, were calculated for the solidifying PMZ and weld metal at the fusion boundary. Judging from the freezing temperature range and the liquid fraction, these curves suggested that liquation decreases in the order of 7075, 2024 and 6061, consistent with experiments. They also suggested that 1100 increases the weld metal f_S, thus promoting liquation cracking (by strengthening the solidifying and contracting weld metal that pulls the PMZ) and discouraging backfilling (by reducing the interdendritic liquid), while 4043 does the opposite except during PMZ terminal solidification in 7075 and 2024. These are consistent with experiments.

Keywords

LIQUATION CRACKING BACKFILLING PARTIAL PENETRATION

Get full access to this article

View all access options for this article.

References

Kou

: ‘Welding metallurgy’, 2nd edn, 151, 160–163, 303–339; 2003, New York, NY, John Wiley and Sons.

Dudas

J. H.

and Collins

F. R.

: Weld. J., 1966, 45, (6), 241s–249s.

Metzger

G. E.

: Weld. J., 1967, 46, (10), 457s–469s.

Steenbergen

J. E.

and Thornton

H. R.

: Weld. J., 1970, 49, (2), 61s–68s.

Gittos

N. F.

and Scott

M. H.

: Weld. J., 1981, 60, (6), 95s–103s.

and Den Ouden

: Int. J. Joining Mater. (Denmark), 1999, 11, (3), 61–67.

Katoh

and Kerr

H. W.

: Weld. J., 1987, 66, (12), 360s–368s.

Kerr

H. W.

and Katoh

: Weld. J., 1987, 66, (9), 251s–259s.

Miyazaki

, Nishio

, Katoh

, Mukae

and Kerr

H. W.

: Weld. J., 1990, 69, (9), 362s–371s.

10.

Gitter

, Maier

, Muller

and Schwellinger

: Proc. 5th Int. Conf. on ‘Aluminum weldments’, (ed. D. Kosteas, R. Ondra and F. Ostermann), 4.1.1; 1992, Munich, Germany, Technische Universita Munchen.

11.

Powell

G. L. F.

, Baughn

, Ahmed

, Dalton

J. W.

and Robinson

: Proc. Int. Conf. on ‘Materials in welding and joining’; 1995, Parkville, Vic., Australia, Institute of Metals and Materials Australasia.

12.

Ellis

M. B. D.

, Gittos

M. F.

and Hadley

: Weld. Inst. J. (UK), 1997, 6, (2), 213–255.

13.

Schillinger

D. E.

, Betz

I. G.

, Hussey

F. W.

and Markus

: Weld. J., 1963, 42, 269s–275s.

14.

Young

J. G.

: Weld. J., 1968, 47, (10), 451s–461s.

15.

Lippold

J. C.

, Nippes

E. F.

and Savage

W. F.

: Weld. J., 1977, 56, (6), 171s–178s.

16.

Huang

, Kou

and Purins

J. R.

: Proc

Merton C.

Flemings Symp. on ‘Solidification processing’, (ed. R. Abbaschian, H. Brody and A. Mortensen), 229; 2001, Warrendale, PA, The Mineral, Metals and Materials Society.

17.

Huang

and Kou

: Weld. J., 2000, 79, (5), 113s–120s.

18.

Huang

and Kou

: Weld. J., 2002, 81, (10), 211s–222s.

19.

Huang

and Kou

: Weld. J., 2001, 80, (2), 46s–53s.

20.

HUANG

and S. kou: Weld. J., 2001, 80, (1), 9s–17s.

21.

Borland

J. C.

and Rogerson

J. H.

: Br. Weld. J., 1963, 8, 494–499.

22.

Savage

W. F.

and Lundin

C. D.

: Weld. J., 1965, 44, (10), 433s–442s.

23.

Savage

W. F.

and Lundin

C. D.

: Weld. J., 1966, 45, (11), 497s–503s.

24.

Huang

and Kou

: Weld. J., 2003, 82, (7), 184s–194s.

25.

The Aluminum Association: ‘Aluminum standards and data’, 15; 1982, Washington, DC, The Aluminum Association.

26.

Flemings

M. C.

: ‘Solidification processing’, 34–36, 160–162, 246–252 and Appendix B; 1974, New York, NY, McGraw-Hill.

27.

Pandat, computer software developed by CompuTherm LLC, Madison, WI.

28.

Zhao

, White

D. R.

and Debroy

: Int. Mater. Rev., 1999, 44, (5), 238–266.

29.

Zhao

and Debroy

: Met. Mater. Trans. B, 2001, 32B, (1), 163–172.

30.

Chou

C. P.

, Lu

C. H.

, Aoh

J. N.

and H. P. kao: ‘International trends in welding science and technology’, (ed. S. A. David and J. M. Vitek), 763–767; 1993, Materials Park, OH, ASM International.

31.

‘Fact Sheet – Choosing shielding for GMA welding’: Weld. J., 2000, 79, (1), 18.