A study was carried out of the characteristics of electrode degradation in resistance spot welding of aluminium, and its influence on weld quality. Based on analysis of electrode life test results, an imaging approach was developed to determine quantitatively the status of electrode degradation, in which three parameters were defined to represent the tip surface characteristics, namely, relative radius, edge concentration, and eccentricity. This image analysis revealed a clear relationship between these defined electrode surface features and the weld quality, based on which a reasonable understanding was achieved of the causes of weld quality deterioration in electrode life tests.
WilliamsN. T.: Weld. World, 1984, 22, (1/2), 28–34.
2.
MatsumotoJ. and MochizukiH.: Weld. Int., 1994, 8, (6), 438–444.
3.
RivettR. M. and WestgateS. A.: Met. Constr., 1980, 12, (10), 510–517.
4.
GlagolaM. A. and RoestC. A.: ‘Nickel plated electrodes for spot welding aluminum’, Report 760167, SAE technical paper, Detroit, MI, USA, 1976.
5.
IkedaR., YasudaK., HashiguchiK., OkitaT. and YahabaT.: Proc. Int. Body Engineering Conf. (IBEC ’95) on ‘Advanced technologies and processes’, Detroit, MI, USA, October 1995, 144–151; Warrendale, PA, SAE.
6.
LeoneG. L. and AltshullerB.: ‘Improvement on the resistance spot weldability of aluminum body sheet’, Report 840292, SAE technical paper, Detroit, MI, USA, 1984.
7.
RivettR. M.: ‘Spot welding electrode life tests on aluminium sheet – effect of parent metal composition and surface treatment’, Report 132, The Welding Institute, Abington, Cambridge, UK, 1980.
8.
PatrickE. P. and SpinellaD. J.: Proc. AWS Sheet Metal Welding Conf., Section VII, Troy, MI, October 1996, American Welding Society, paper B4.
9.
FukumotoS., LumI., BiroE., BoomerD. R. and ZhouY.: Weld. J., 82, (11), 307s–312s.
10.
DiltheyU. and HickenS.: Schweissen Schneiden, 1998, 50, 34–38.
11.
LumI., FukumotoS., BiroE., BoomerD. R. and ZhouY.: Metall. Mater. Trans. A, 2003, 34A, (1), 217–226.
12.
HaoM., NewtonC. J., ThorntonM. C. and OsmanK. A.: Proc. Int. Body Engineering Conf. (IBEC ’97) on ‘Body assembly and manufacturing’, Warren, MI, USA, September 1997, 81–87; Warrendale, PA, SAE.