Studies on the causes of the embrittlement of Cu–31Zn–D·32P brass, in particular by scanning electron miscroscope, have been made. The occurrence of three kinds of fractures was found. The possibility of transition from the embrittled state to ductile state and back, depending on technological processing, was recognized. The kind of state is dependent on the morphology of phases and implies the types of fracture found.