Laboratory experiments and small-scale industrial trials have indicated that the optimum composition range for tin-magnesium bronze is copper, 4·60–5·25wt-% tin, 0·90–1·20wt-% magnesium, and that the most satisfactory methods of manufacturing the alloy in the wrought form are likely to be by cold working suitably heat-treated continuous-cast or hot-extruded sections. During a more detailed examination of the properties of the alloy it has been shown, for example, that after solution treatment followed by a cold reduction of 80% and final precipitation hardening, rolled strip has a tensile strength of over 800 MN/m2 (113 × 103Ibf/in2, 50·5 tonf/in2), a 0·2% proof stress of about 650 MN/m2 (90 × 103 Ibf/in2, 40·1 tonf/in2), a hardness of ∼270 HV, and an electrical conductivity of over 40% IACS. The resistance of this strip to stress corrosion cracking appeared to be similar to that of a cold-worked nickel-silver alloy. Some attempts have been made further to improve the properties of the alloy, but no significant improvement over the values above appears to be easily obtainable.
Get full access to this article
View all access options for this article.