Nickel aluminide coating produced on γ -TiAl alloy by high activity aluminising process

Abstract

Ni aluminide diffusion coatings on the surface of γ-TiAl alloy were produced by electroplating a Ni layer followed by a single step high activity aluminising carried out in Ar+H₂ atmosphere with a mixture of Al, NH₄Cl and Al₂O₃ powders at 1000°C for 5 h. The effect of initial thickness for Ni layer on microstructure of produced Ni aluminide coating was highlighted. The thickness of initial Ni layer was changed to 4–20 μm. In the case of the Ni layer with thickness of 4 μm, only a little amount of NiAl phase was formed in a TiAl₃ matrix. However, the microstructure of coating, in the case of the Ni layer with thickness of 8 μm, consisted of an outer layer of two phases (NiAl+TiAl₃), an intermediate layer of TiAl₃ and an interdiffusion layer. For thicker initial Ni layers (16 and 20 μm), beside the latter coating microstructure, a continuous surface layer of NiAl phase was observed. Isothermal oxidation tests on these aluminide coatings reveal that the oxidation resistance of the aluminide coatings increases with increase in initial thickness of Ni layer.