Acceptor doped barium titanate ceramic samples were prepared and exposed to oxygen activity gradients at elevated temperatures. When an oxygen activity gradient is imposed on such a pellet, a pin junction is formed. In situ measurements of the I–V relations were performed under various oxygen activity gradients. These measurements show very strong memory effects. An explanation of this behaviour is suggested based on the assumption of enhanced mobility of metal vacancies due to the oxygen activity gradient.
LongS. A. and BlumenthalR. N.: J. Am. Ceram. Soc., 1971, 54, 577.
2.
SeuterA. M. J. H.: Philips Res. Rep. Suppl, 1974, 3, 1.
3.
ChanN. H., SharmaR. K. and SmythD. M.: J. Am. Ceram. Soc., 1981, 64, 556.
4.
TsurY. and RandallC. A.: J. Am. Ceram. Soc., 2001, 84, 2147.
5.
TsurY. and RandallC. A.: ‘A universal analytical approach to the defect chemistry of A±213±403 perovskites’, in ‘High temperature corrosion and materials chemistry’, (ed. P.Y. Hou et al), 502-13; 2000, Pennington, NJ, Electrochemical Society.
6.
YooH.-I., SongC.-R. and LeeD.-K.: J. Electroceram., 2002, 8, 5.
7.
KolodiazhnyiT., PetricA. and NiewczasM.: Phys. Rev. B, 2003, 68B, 085205.
8.
MoosR. and HärdtlK. H.: J. Am. Ceram. Soc., 1995, 78, 2569.
9.
SasakiK. and MaierJ.: J. Appl. Phys., 1999, 86, 5422.
10.
TsurY.: Interface Sci., 2001, 9, 163.
11.
YaseenH., BaltianskiS. and TsurY.: J. Am. Ceram. Soc., 2006,89, 1584.
12.
RiessI.: J. Phys. Chem. Solids, 1986, 47, 129.
13.
RiessI.: Phys. Rev. B, 1987, 35B, 5740.
14.
RiessI.: Solid State Ionics, 1995, 75, 59.
15.
SmythD. M.: ‘The defect chemistry of metal oxides’; 2000, New York, Oxford University Press.
16.
KrogerF. A. and VinkH. J.: Solid State Phys., 1956, 3, 307.
17.
TsurY., RiessI.: Phys. Rev. B, 1999, 60B, 8138.
18.
TsurY. and RiessI.: Solid State Ionics, 1999, 119, 37.
19.
TsurY. and RandallC. A.: ‘Charge-compensation in BaTiO3’, Proc. 12th IEEE Int. Symp. on ‘Applications of ferroelectrics’, Eds. S.K. Streiffer, B. J. Gibbons and T. Tsurumi, IEEE,Vol. 1, 151-154 (2001).
20.
JeongJ. H., ParkM. G. and HanY. H.: J. Electroceramics, 2004, 13, 805.
21.
YooH.-I., SongC. R. and LeeD. K.: J. Eur. Ceram. Soc., 2004,24, 1259.
22.
LeeY. S. and YooH.-I.: Solid state Ionics, 2002, 150, 373
23.
BuscagliaM. T., BuscagliaV., VivianiM., NanniP. and HanuskovaM.: J. Eur. Ceram. Soc., 2000, 20, 1997.
24.
DunbarT. D., WarrenW. L., TuttleB. A., RandalC. A. and TsurY.: J. Phys. Chem. B, 2004, 108B, 908.
25.
RodewaldS., FleigJ. and MaierJ.: J. Am. Ceram. Soc., 2000, 83, 1969.
26.
LeviR. D. and TsurY.: Adv. Mater., 2005, 17, 1606.