Sage Journals: Discover world-class research

Abstract

The behaviour of 17-4 precipitation hardening (PH) stainless steel was studied using the hot compression test at temperatures of 950–1150°C with strain rates of 0·001–10 s⁻¹. The stress–strain curves were plotted by considering the effect of friction. The work hardening rate versus stress curves were used to reveal whether or not dynamic recrystallisation (DRX) occurred. Using the constitutive equations, the activation energy of hot working for 17-4 PH stainless steel was determined as 337 kJ mol⁻¹. The effect of Zener–Hollomon parameter Z on the peak stress and strain was studied using the power law relation. The normalised critical stress and strain for initiation of DRX were found to be 0·89 and 0·47 respectively. Moreover, these behaviours were compared to other steels.

Keywords

HOT WORKING DYNAMIC RECRYSTALLISATION CRITICAL STRESS ACTIVATION ENERGY WORK HARDENING RATE CONSTITUTIVE EQUATIONS

Get full access to this article

View all access options for this article.

References

Mirzadeh

and Najafizadeh

: Mater. Chem. Phys., 2009, 116, 119–124.

Isogawa

, Yoshida

, Hosoi

and Tozawa

: J. Mater. Process. Technol, 1998, 74, 298–306.

Abbasi

S. M.

and Shokuhfar

: Mater. Lett., 2007,61, 2523–2526.

‘Corrosion-resistant, bars, wire, forgings, tubing, and rings 16Cr-4.0Ni’, AMS 5643Q, SAE International, Warrendale, PA, USA, 2003.

Herbertz

and Wiegels

: Stahl Eisen, 1981, 101, 89–92.

Jonas

J. J.

, Quelennec

, Jiang

and Martin

: Acta Mater., 2009, 57, 2748–2756.

Ebrahimi

and Najafizadeh

: J. Mater. Process. Technol.,2004, 152,136–143.

Hot deformation behaviour of precipitation hardening stainless steel

Abstract