High strain isothermal compression tests at temperatures of 700–1200°C and strain rates of 0.1–50 s−1 were performed in a Gleeble-3800 thermal simulator to investigate the hot deformation behaviour of a high-alloy Cr–Co–Mo–Ni gear steel, and the constitution equation and hot processing map were established based on these experiments. The results show that the flow stress can be described by the constitutive equation in hyperbolic sine function, and the optimum hot working regions are at the temperature of 1000–1100°C and strain rate of 0.3–1.0 s−1. Optical microscopy observations of austenite grains indicate that dynamic recrystallisation occurs when the deformation temperature is over 900°C. The forging was successfully produced on the basis of the above-described researches.
WangK, YangMS, FanG, Investigation on mechanism of strength-toughening of heat and corrosion resistant bearing steel 16Cr14Co12Mo5. Iron Steel. 2011;46(10):75–79.
2.
HouZP, YangMS, ZhaoKY, Microstructure evolution research of Cr-Co-Mo-Ni gear and bearing steel under action of temperature and stress coupling. Iron Steel. 2014;49(4):80–85.
3.
GuoBF, JiHP, LiuXG, Research on flow stress during hot deformation process and processing map for 316LN austenitic stainless steel. J Mater Eng Perform. 2012;21(7):1455–1461. doi: 10.1007/s11665-011-0031-0
4.
MomeniA, DehghaniK.Characterization of hot deformation behavior of 410 martensitic stainless steel using constitutive equations and processing maps. Mater Sci Eng A. 2010;527(21–22):5467–5473. doi: 10.1016/j.msea.2010.05.079
5.
ChibaA, LeeSH, MatsumotoH, Construction of processing map for biomedical Co–28Cr–6Mo–0.16N alloy by studying its hot deformation behavior using compression tests. Mater Sci Eng A. 2009;513–514(11):286–293. doi: 10.1016/j.msea.2009.02.044
6.
RajR.Development of a processing map for use in warm-forming and hot-forming processes. Metall Trans A. 1981;12(6):1089–1097. doi: 10.1007/BF02643490
7.
PrasadYVRK, GegelHL, DoraivelusmSM, Modeling of dynamic material behavior in hot deformation: forging of Ti-6242. Metall Trans A. 1984;15(10):1883–1892. doi: 10.1007/BF02664902
8.
PrasadYVRK.Recent advances in the science of mechanical processing. Indian J Technol. 1990;28(6–8):435–451.
9.
PrasadYVRK.Dynamic materials model: basis and principles. Metall Mater Trans A. 1996;27(1):235–236. doi: 10.1007/BF02647765
10.
PrasadYVRK, SasidharaS.Hot working guide: A compendium of processing Map. Materials Park (OH): ASM International; 1997.
11.
PrasadYVRK, SeshacharyuluT.Modelling of hot deformation for microstructural control. Int. Mater Rev. 1998;43(6):243–258. doi: 10.1179/imr.1998.43.6.243
12.
LiuXG, JiHP, GuoH, Study on hot deformation behaviour of 316LN austenitic stainless steel based on hot processing map. Mater Sci Technol. 2013;20(1):24–29. doi: 10.1179/1743284712Y.0000000083
13.
FarnoushH, MomeniA, DehghaniK, Hot deformation characteristics of 2205 duplex stainless steel based on the behavior of constituent phases. Mater Des. 2010;31(1):220–226. doi: 10.1016/j.matdes.2009.06.028
14.
MomeniA, DehghaniK.Hot working behavior of 2205 austenite–ferrite duplex stainless steel characterized by constitutive equations and processing map. Mater Sci Eng A. 2011;528(3):1448–1454. doi: 10.1016/j.msea.2010.11.020
15.
VenugopalS, MannanSL, PrasadYVRK.Influence of state of stress on the processing map for hot working of stainless steel type AISI 304L: compression vs. torsion. Mater Sci Eng A. 1993;160(1):63–69. doi: 10.1016/0921-5093(93)90498-4
16.
MurtySVSN, RaoBN, KashyapBP.Identification of flow instabilities in the processing maps of AISI 304 stainless steel. J Mater Process Technol. 2005;166(2):268–278. doi: 10.1016/j.jmatprotec.2004.09.089
17.
TanSP, WangZH, ChengSC, Processing maps and hot workability of Super304H austenitic heat-resistant stainless steel. Mater Sci Eng A. 2009;517(1–2):312–315. doi: 10.1016/j.msea.2009.04.028
18.
LiuY, HuR, LiJS, Characterization of hot deformation behavior of Haynes230 by using processing maps. J Mater Process Technol. 2009;209(8):4020–4026. doi: 10.1016/j.jmatprotec.2008.09.024
19.
LiuJ, CuiZS, LiCX.Analysis of metal workability by integration of FEM and 3-D processing maps. J Mater Process Technol. 2008;205(1-3):497–505. doi: 10.1016/j.jmatprotec.2007.11.308
20.
SellarsCM, MctegartWJ.On the mechanism of hot deformation. Acta Metall. 1966;14(9):1136–1138. doi: 10.1016/0001-6160(66)90207-0
21.
WangBX, LiuXH, WangGD.Dynamic recrystallization behavior and microstructural evolution in a Mn–Cr gear steel. Mater Sci Technol. 2005;393(7):102–108.
22.
YangZM, WangRZ.Formation of ultra-fine grain structure of plain low carbon steel through deformation induced ferrite transformation. ISIJ Int. 2003;43(5):761–766. doi: 10.2355/isijinternational.43.761
23.
PolyakYEII, BreyginVD.Investigation of thermally activated processes during high-temperature deformation of engineering steel. Phys Met Metallogr. 1989;67(4):172–180.
24.
LiuYN, SongXL, LinJS.Yield strength and activation energy of steel. Ordn Mater Sci Eng. 1995;18(6):10–14.
25.
GorelikSS.Recrystallization in metals and alloys. Moscow: MIR Publishers; 1981.
26.
MengWJ.Investigations of grain and carbide evolution of high-alloy steel during hot deformation process [master's thesis]. Beijing: University of Science and Technology Beijing; 2015.
ZieglerH.Progress in solid mechanics. New York ( NY): John Wiley and Sons; 1963.
29.
ZengWD, ZhouYG, ZhouJ, Recent development of processing map theory. Rare Metal Mat. Eng. 2006;35(5):673–677.
30.
SunK, WangFC, ChengXW, Formation mechanics of adiabatic shear band for the different microstructures of TC6 alloy. Rare Metal Mater Eng. 2009;38(1):34–37.
31.
ZenerC, HollomonJH.Effect of strain rate upon plastic flow of steel. J Appl Phys. 1944;15(1):22–32. doi: 10.1063/1.1707363
32.
BelyakovA, MiuraH, SakaiT.Dynamic recrystallization under warm deformation of a 304 type austenitic stainless steel. Mater Sci Eng A. 1998;255(1–2):139–147. doi: 10.1016/S0921-5093(98)00784-9