A Ti containing interstitial free steel was warm rolled in the temperature range 500–800°C, using wedge shaped slabs to produce a range of strains in a single rolling test. Some plane strain compression tests, under similar conditions, were carried out to obtain accurate stress–strain data. Variations in substructural features including subgrain sizes, subgrain aspect ratios, and misorientations between subgrains were quantitatively measured by TEM. Close correlation was observed between mechanical behaviour and variations in the substructure at different temperatures. At the lower temperature (500°C), the material showed cold worked characteristics, but as the deformation temperature was increased the effects of recovery became more pronounced, and hot working behaviour was obvious in the flow stress as well as in the substructural observations at 800°C.
Get full access to this article
View all access options for this article.
References
1.
NILSSONK. I. and JOHNSSONE.: in ‘Metallurgy of vacuum-degassed steel products’, (ed. PradhanR.), 143-160; 1990, Warrendale, PA, TMS.
2.
OBARAT., SATOHS., NISHIDAM., and IRIET.: Scand. J. Metall., 1984, 13, 201–213.
3.
GOODENOWR. H. and HELDJ. F.: Metall. Trans., 1970, 1, 2507–2515.
4.
SATOHS., OBARAT., NISHIDAM., and HUET.: in ‘Technology of continuously annealed cold-rolled sheet’, (ed. PradhanR.), 151-166; 1985, Warrendale, PA, TMS-AIME.
5.
GOODMANS. R., MOULDP. R., and SIPLEJ. C.: in ‘Technology of continuously annealed cold-rolled sheet steel’, (ed. PardhanR.), 167-183; 1985, Warrendale, PA, TMS-AIME.
6.
HOOKR. E., HECKLERA. J., and ELIASJ. A.: Metall. Trans. A, 1975, 6A, 1683–1692.
7.
HUTCHINSONW. B.: Int. Met. Rev., 1984, 29, 25–42.
8.
DARMANNC. and ENGLB.: Proc. 7th Riso Int. Symp. on Metallurgy and Metal Science: ‘Annealing processes — recovery recrystallization and grain growth’, (ed. HansenN., et al), Roskilde, Denmark, September 1986, Riso National Labora-tory,279–284.
9.
KRAUSSG., WILSHYNSKYD. O., and MATLOCKD. K.: Proc. Int. Symp. on Interstitial Free Steel Sheet: ‘Processing, fabrication and properties’, (ed. CollinsL. E. and BaragarD. L.), Ottawa, ON, Canada, August 1991, Metallurgical Society of CIM,1–14.
10.
GUPTAI. and BHATTACHARYAD.: Proc. Int. Conf. on ‘Metallurgy of vacuum-degassed steel products’, (ed. PradhanR.), 43-72; 1990, Warrendale, PA, TMS.
NAKAMURAT. and ESAKAK.: Proc. Int. Conf. on ‘Physical metallurgy of thermomechanical processing of steels and other metals’, THERMEC-88, Tokyo, Japan, June 1988, Iron and Steel Institute of Japan,644–651.
13.
SENUMAT. and YADAH.: Proc. Int. Conf. on ‘Physical metallurgy of thermomechanical processing of steels and other metals’, THERMEC-88, Tokyo, Japan, June 1988, Iron and Steel Institute of Japan,636–643.
14.
HASHIMOTOS., YAKUSHIJIT., KASHIMAT., and HOSOMIK.: Proc. Int. Conf. on ‘Physical metallurgy of thermomechanical processing of steels and other metals’, THERMEC-88, Tokyo, Japan, June 1988, Iron and Steel Institute of Japan,652–659.
15.
SENUMAT., SAITOH., USHIODAK., YOSHINAGAN., and YADAH.: J. Jpn Inst. Met., 1990, 54, 403.
16.
SENUMAT. and KAWASAKIK.: ISIJ Int., 1994, 34, 51–60.
17.
AKBARIG. H., SELLARSC. M., and WHITEMANJ. A., Acta Mater., 1997, 45, 5047–5058.
18.
DULYD., BAXTERG. J., SHERCLIFFH. R., WHITEMANJ. A., SELLARSC. M., and ASHBYM. F.: Acta Mater., 1996, 44, 2947–2962.
19.
KOBAYASHIH.: ISIJ Int., 1992, 32, 873–881.
20.
MCQUEENH. J., WONGW. A., and JONASJ. J.: Can. J. Phys., 1967, 45, 1225–1235.
21.
EXELLS. F. and WARRINGTOND. H.: Philos. Mag., 1972, 26, 1121–1136.
22.
HARTLEYA. J.PhDthesis, University of Sheffield, UK, 1972.
23.
MCQUEENH. J. and JONASJ. J.: in ‘Treatise on materials science and technology’,Vol. 6, ‘Deformation of metals’, 393-493; 1975, New York, Academic Press.
24.
JONASJ. J., SELLARSC. M., and W. J. MCG.TEGART: Metall. Rev., 1969,14, 1–24.
25.
KEHA. S. and WEISSMANNS. C.: in ‘Electron microscopy and strength of crystals’, (ed. ThomasG. and WashburnJ.), 231; 1963, New York, Interscience.
26.
BARDALA., LINDSETHI., VATNEH. E., and NESE.: Proc. 16th Riso Int. Symp. on Materials Science: ‘Microstructural and crystallographic aspects of recrystallization’, Roskilde, Denmark, September 1995, Riso National Laboratory,261–266.
27.
HuH., RATHB. B., and VANDERMEERR. A.: in ‘Recrystallization 90’, (ed. ChandraT.), 3-16; 1990, Warrendale, PA, TMS.
28.
SELLARSC. M. and ZHUQ.: in ‘Hot deformation of aluminium alloys II’, (ed. BielerT. R. et al.), 185-197; 1988, Warrendale, PA, TMS.
29.
CASTRO-FERNANDEZF. R. and SELLARSC. M.: Philos. Mag. A, 1989, A60,487–506.
30.
BAXTERG. J., FURUT., ZHUQ., WHITEMANJ. A., and SELLARSC. M.: Acta Mater., 1999,47, 2367–2376.