The effect of material characteristics and mould parameters on the thermoforming of thick polypropylene sheets

Abstract

Two grades of 5 mm thick polypropylene (PP) sheets, one having linear polymer chains (PP-TF-1) and the other having long-chain branches (PP-TF-2), were drape formed, using moulds of different parameters. Single-sided heating of sheet was found to be suitable only at lower depths of draw. Double-sided heating gave good part shape conformance at all depths of draw. PP-TF-2 was found to have lower crystallinity than PP-TF-1, suggesting that it would have a lower sagging tendency and would give parts with more uniform wall thickness distribution. This was confirmed in formability studies. At higher depths of draw, an increase in draft angle was found to give more uniform wall thickness distribution, maintaining reasonable values of wall thickness. At lower depths of draw, draft angle was found to have no influence on product quality. Irrespective of material characteristics and other mould parameters, only moulds with generous values of corner radii gave strong corners.

Keywords

Thermoforming formability polypropylene crystallinity draft angle corner radius

Get full access to this article

View all access options for this article.

References

Throne

. Thermoforming, New York: Hanser Publishers, 1986.

Muccio

. Plastic part technology, Ohio: ASM International, 1991.

Yang

Hung

. Optimising the thermoforming process of polymeric foams: An approach by using the Taguchi method and the utility concept. Int J Adv Manuf Technol 2004; 24: 353–360.

Encyclopedia of Polymer Science and Technology. Processing & finishing of polymeric materials, vol. 2. New Jersey: Wiley, 2011.

Ayhan

Zhang

. Wall thickness distribution in thermoformed food containers produced by a Benco asceptic packaging machine. Polymer Eng Sci 2000; 40: 1–10.

Aroujalian

Ngadi

Emond

. Wall thickness distribution in plug-assist vacuum formed strawberry containers. Polym Eng Sci 1997; 37: 178–182.

Labeas

Watiti

Katsiropoulos

. Thermomechanical simulation of infrared heating diaphragm forming process for thermoplastic parts. J Thermoplast Compos Mater 2008; 21: 353–370.

Schmidt

Maoult

Monteix

. Modeling of infrared heating of thermoplastic sheet used in thermoforming process. J Mater Process Technol 2003; 143–144: 225–231.

Yousefi

Bendada

Diraddo

. Improved modeling for the reheat phase in thermoforming through an uncertainty treatment of the key parameters. Polym Eng Sci 2002; 42: 1115–1129.

10.

Dharia A. Applications of thermoformability analyzer. SPE, ANTEC. 2006.

11.

Throne

. Technology of thermoforming, Munich: Hanser Publishers, 1996.

12.

Lau

Bhattacharya

Field

. Melt strength of polypropylene: Its relevance to thermoforming. Polym Eng Sci 1998; 38: 1915–1923.

13.

Cruz

Jr . The sag process in modified polypropylene. J Plast Film Sheet 1995; 11: 190–203.

14.

Morye

. A comparison of the thermoformability of a PPE/PP blend with thermoformable ABS. Part 1: Small deformation methods. Polym Eng Sci 2005; 45: 1369–1376.

15.

Lau

Bhattacharya

Field

. Influence of rheological properties on the sagging of polypropylene and abs sheet for thermoforming applications. Polym Eng Sci 2000; 40: 1564–1570.

16.

Gotsis

Zeevenhoven

Hogt

. The effect of long chain branching on the processability of polypropylene in thermoforming. Polym Eng Sci 2004; 44: 973–982.