The influence of polypropylene fibers has been studied in different proportioning and fiber length to improve the performance characteristics of the lightweight cement composites. Fibers used in two different lengths (6mm and 12mm) and fiber proportions (0.15% and 0.35%) by cement weight in the mixture design. Hardened concrete properties such as: 7- and 28-day compressive strength, splitting tensile strength, flexural strength, water absorption, and shrinkage were evaluated.
Fiber addition was seen to enhance the physical and mechanical properties of lightweight concrete. Compared to unreinforced LWC, polypropylene (PP) reinforced LWC with fiber proportioning 0.35% and 12 mm fiber length, caused 30.1% increase in the flexural strength and 27% increase in the splitting tensile strength. Increased fiber availability in the LWC matrix, in addition to the ability of longer PP fibers to bridge on the micro cracks, are suggested as the reasons for the enhancement in mechanical properties.
BenturA., and MindessS., Fiber Reinforced Cementitious Composites. 2th ed. Landon and New York, Taylor & Francis, Essex, UK, 2007, p. 11–235.
2.
HoltE., and LeivoM., Cracking risks associated with early age shrinkage, Cem. Concr. Compos2004; 26(5), 52: 521–530.
3.
FangX. U., MingkaiZ., BeixingL., and WeiguoS., Influence of Mineral Admixtures on the Performance of Polymer Modified Porous Concrete, Journal of Wuhan University of Technology-Mater, 2010; 25(4), 624.
4.
ZolloRF. Fiber-reinforced Concrete, an Overview after 30 Years of Development. Cement and Concrete Composites1997; 19: 107–122.
5.
GaoJ., SunW., and MorinoK., Mechanical properties of steel fiber reinforced, high-strength lightweight concrete, Cem. Concr. Compos.1997; 19(4): 307–313.
6.
WassemanR., BenturA., Effect of lightweight fly ash aggregate microstructure on the strength of concrete, Cem. Concr. Res.1997; 27(4): 525–537.
7.
KayaliO., HaqueM.N., and ZhuB., Some characteristics of high strength fiber reinforced lightweight aggregate concrete, Cem. Concr. Compos.2003; 25(2): 207–213.
8.
BalendranR.V., ZhouF.P., NadeemA., and LeungA.Y.T., Influence of steel fibers on strength and ductility of normal and lightweight high strength concrete, Build. Environ.2002; 37: 1361–1367.
9.
MerikallioT., MannonenR., and PenttalaV., Drying of lightweight concrete produced from crushed expanded clay aggregate, Cem. Concr. Res.1996; 26(9): 1423–1433.
10.
MaysG.C., BarnesR.A., The performance of lightweight aggregate concrete structures in service, Struct. Eng.1991; 69(20): 351–361.
11.
ChenaB., and LiuJ., Contribution of hybrid fibers on the properties of the high-strength lightweight concrete having good workability, Cem. Concr. Res., 2005; 35: 913–917.
12.
Libre NicolasA., ShekarchiM., MahoutianM., and SoroushianP., Mechanical properties of hybrid fiber reinforced lightweight aggregate concrete made with natural pumice, Construction and Building Materials.2011; 25: 2458–2464.
13.
Perez-PenaM., and MobasherB., Mechanical properties of fiber reinforced lightweight concrete composites, Cement and Concrete Research, 1994; 24(6): 1121–1132.
14.
RitchieAGB, KayaliO., The effects of fibre reinforcement on lightweight aggregate concrete. In: NevilleA, editor. Proceedings of RILEM Symposium on Fibre Reinforced Cement and Concrete, the Construction Press Ltd; 1975: 247–56.
15.
DongJ. Kim, AntoineE. N., and SherifE.T., Comparative flexural behavior of four fiber reinforced cementitious composites”, Cement & Concrete Composites, 2008; 30(10): 917–928.
16.
AndrzejMB. Cement-Based Composites. 2th ed. New York, Taylor & Francis, 2009.
17.
SongP. S., HwangS., and SheuB. C., Strength properties of nylon- and polypropylene-fiber reinforced concretes, Cement And Concrete Research, 2005; 35: 1546–1550.
18.
AlhozaimyA. M., SoroushianP., and MirzaF., Mechanical properties of polypropylene fiber reinforced concrete and the effects of pozzolanic materials, Cement and Concrete Composites, 1996; 18: 85–92.
19.
TanyildiziH., Statistical analysis for mechanical properties of polypropylene fiber reinforced lightweight concrete containing silica fume exposed to high temperature, Materials and Design, 2009; 30: 3252–3258.
20.
SoroushianP, NagiM, HsuJ., Optimization of the use of lightweight aggregate in carbon fiber reinforced cement. ACI Mater J1992; 89(3): 267–76.
21.
BalendranR.V., ZhouF.P., NadeemA., and LeungA.Y.T., Influence of steel fibres on strength and ductility of normal and lightweight high strength concrete, Build. Environ.2002; 37: 1361–1367.
22.
MalischW. R., Polypropylene Fibers in Concrete, What do the test tell us?Concrete Construction, 1986; 31: 363–8.
23.
KraiiP. P., A Proposed test to determine the cracking potential due to drying shrinkage of concrete. Concrete construction, 1985; 30: 775–778.
24.
MindessS., & VondranG., Properties of concrete reinforced with fibrillated polypropylene fibers under impact loading. Cement and Concrete Research, 1988; 18: 109–15.
25.
HughesB. P., FattuhiN. I., Improving the toughness of high strength cement paste with fiber reinforcement, Composite, 1976; 7(4): 185–8.
26.
ShahS.P., SarigaphutiM., and KaragulerM.E., Comparison of shrinkage cracking performance of different types of fibres and wiremesh, in: Fiber Reinforced Concrete Developments and Innovations, ACI SP-142, 1994; 1–18.
27.
BanthiaN., AzzabiM., and PigeonM., Restrained shrinkage tests on fiber reinforced cementitious composites, in: Testing of Fiber Reinforced Concrete, ACI SP-155, 1995: 137–151.
28.
HanusF., FaureJ.C., and PfeiferG., High performance lightweight aggregate concrete in blast resisting structures, in: MalierYves (Ed.), High Performance Concrete, London, F&FN Spon, 1993, p. 495–509.
29.
ChenW., and BrouwersH.J.H., Alkali binding in hydrated Portland cement paste, Cement and Concrete Research.2010; 40: 716–722.
30.
Martinez-RamirezS., and PalomoA., Microstructure studies on Portland cement pastes obtained in highly alkaline environments, Cement and Concrete Research, 2001; 31(11): 1581–1585.
31.
ASTM C 39–2010, “Standard Test Method for Compressive Strength of Fiber Reinforced Concrete”, Annual Book of ASTM Standards.American Society for Testing and Materials, USA, 2010.
32.
ChenB., and LiuJ., Contribution of hybrid fibers on the properties of the high-strength lightweight concrete having good workability, Cement and Concrete Research, 2005; 35: 913–917.
33.
ASTM C1609-2010, “Standard Test Method for Flexural Performance of Fiber-Reinforced Concrete (Using Beam With Third-Point Loading)”, Annual Book of ASTM Standards.American Society for Testing and Materials, USA, 2010.
34.
ACI 544.1R-96, State-of-the-art report on fiber reinforced concrete, Farmington Hills, Michigan:American Concrete Institute, 2002.
35.
ASTM C496-2004, “Standard Test Method for Split Tensile Strength of Cylindrical Concrete Specimens”, Annual Book of ASTM Standards.American Society for Testing and Materials, USA, 2004.
36.
ASTM C1585-2004, “ASTM C1585 - 04e1 Standard Test Method for Measurement of Rate of Absorption of Water by Hydraulic-Cement Concretes”, Annual Book of ASTM Standards.American Society for Testing and Materials, USA, 2004.
37.
BayasiZ., and ZengJ., Properties of Polypropylene Fiber Reinforced Concrete, Materials Journal, 1993; 90(6): 605–610.
38.
AlanE.Richardson, Compressive strength of concrete with polypropylene fibre additions”, Structural Survey, Vol. 24 (2), 2006, 138–153.
39.
ASTM C426-2010, “ASTM C426-10 Standard Test Method for Linear Drying Shrinkage of Concrete Masonry Units”, Annual Book of ASTM Standards.American Society for Testing and Materials, USA, 2010.
40.
BalaguruP., and SlattumK., “Test Methods for Durability of Polymeric Fibers in Concrete and UV Light Exposure”, American Concrete Institute, Special Publication1995; 155: 115–136.
41.
BerkeN.S., and DallaireM.P., The effect of low addition rates of polypropylene fibres on plastic shrinkage cracking and mechanical properties of concrete, in: Fiber Reinforced Concrete Developments and Innovations, ACI SP-142, 1994: 19–42.
42.
BagherzadehR., SadeghiA.H., and LatifiM., Utilizing Polypropylene Fibers to Improve Physical and Mechanical Properties of Concrete, Textile Research Journal, 201182(1) 88–96.
43.
PakravanHR, JamshidiM, LatifiM.Performance of fibers embedded in a cementitious matrix. J Appl Polym Sci2010; 116: 1247–1253.