Abstract
Amplicon sequencing is applied to monitor microbial species residing in the biofilm that formed on steel surface submerged in surface water along the Ghent Terneuzen canal, stretching 31 kms from Belgium to the Netherlands. Temporal and spatial differences in the biofilm microbiota were revealed by 16S rRNA composition analysis. The loss-of-mass from S235 steel coupons showed uniform corrosion rates ranging from 242 to 906 g/m2 after 3 months. Notably, enhanced pitting corrosion was seen at one specific location near ‘Heide’ affecting the surface with depths up to 1210 µm after 6 months. We presume the excessive steel deterioration in micro-cavities is associated with microbial activity of iron-oxidising bacteria (IOB) and sulphur-reducing bacteria (SRB), such as Shewanella spp. and Gallionella spp., respectively, as redox-active species. Indications for microbially induced corrosion (MIC) are highlighted at sites with apt microbial composition, irrespective of physico-chemical water parameters. Coupons affected by high corrosion and assumed MIC did not stand out in terms of species richness and alpha diversity did not increase, suggesting partial take-over of the microbial community by IOB or SRB.
Keywords
Get full access to this article
View all access options for this article.
References
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.