The objective of this study was to evaluate the effect of the amount of added latex and accelerator on the strength development and chloride ion penetration properties of concrete used for the repair of concrete pavement. Such pavement must be re-opened to traffic 3 days after repairing. The target values of the latex-modified repair concrete were as follows: a compressive strength of 22 MPa and a flexural strength of 4.5 MPa after 3 days, and a compressive strength of 27 MPa and chloride ion penetration value of < 2,000 coulombs after 28 days. In this study, latex was added at 0, 5, 10, and 15% of the cement weight, and the accelerator was added at 0 and 1% of the cement weight. The test results indicated that the mixes with accelerator and latex contents of 10 and 15% satisfied the target strength and chloride ion penetration values for the 3-day traffic opening requirement.
KimD.H., and ParkC.G., Strength, permeability and durability of hybrid fiber-reinforced concrete containing styrene butadiene latex, Journal of Applied Polymer Science, 129(3) (2013) 1499–1505.
2.
SprinkelM., Latex-modified concrete overlay containing Type K cement, Virginia Transportation Research Council, VA, FHWA/VTRC 05-R26, 2005.
3.
SprinkelM., High Early Strength Latex Modified Concrete Overlay, Virginia Transportation Research Council: VA, Report VTRC 88-R12, 1998.
4.
YunK.K., and ChoiP., Causes and controls of cracking at bridge deck overlay with very-early strength latex –modified concrete, Construction and Building Materials, 56, (2014) 53–62.
5.
WonJ.P., KimJ.M., LeeS.J., LeeS.W., and ParkS.K., Mix proportion of high-strength, roller-compacted, latex-modified rapid-set concrete for rapid road repair, Construction and Building Materials, 25(4), (2011) 1796–1800.
6.
LangloisM., PigeonM., BissonnetteB, and AllardD., Concrete International, 16, (1994), 39.
7.
WonJ.P., KimJ.H., ParkC.G., and KangJ.W., Shrinkage cracking of styrene butadiene polymeric emulsion-modified concrete using rapid-hardening cement, Journal of Applied Polymer Science, 112(4) (2009) 2229–2234.
8.
WonJ.P., KimJ.H., LeeS.W., and ParkC.G., Durability of Low-Heat, Ultra Rapid-Hardening, Latex Modified Polymer Concrete, Progress in Rubber, Plastics and Recycling Technology, 25(2) (2009) 91–102.
9.
SprinkelM., Very-early-strength latex-modified concrete over-lays, Virginia Transportation Research Council, VA, TAT99-TAR3, 1998.
10.
BalaguruP. N., and BhattD., Rapid hardening concrete, Final Report, FHWA, Washington DC, Report No. FHWA 2001–03, 2000.
11.
Korea Expressway Corporation, Construction Material Quality and Standard for Highway Construction, Korea Expressway Corporation, Seongnam, Republic of Korea, 2005.
12.
AASHTO, Standard Specification of Rigid Pavement, American Association of State Highway and Transportation Officials, Washington, DC, 1998.
13.
Kim D.H. and Park C.G., Permeability, Abrasion, and Impact Resistance of Latex-Modified Fibre Reinforced Concrete for Precast Concrete Pavement Application, Progress in Rubber Plastics and Recycling Technology, 29(4), (2013) 239–254.
14.
BullJ.W., and WoodfordC.H., Design of precast concrete pavement units for rapid maintenance of runways, Computers & Structures, 64(1-4), (1997), 857–864.
15.
AckroydR.F., and BullJ.W., The design of precast concrete pavements on low bearing capacity subgrades, Computers and Geotechnics, 1(4) (1985) 279–291.
16.
BuchN., Precast Concrete Panel Systems for Full-Depth Pavement Repairs: Field Trials. Final Report, FHWA, Washington DC, Report No. FHWA-HIF-07-019), 2007.
17.
LaneR., and KazmierowskiT., Use of Innovative Pre-Cast Concrete Slab Repair Technology in Canada. Proceedings of the 8th International Conference on Concrete Pavements, (2005) 771–789.
18.
BuchNeeraj, Van DamThomas J., PetersonKarl, and SutterLarry, Evaluation of high-early strength PCC mixtures used in full depth repairs, Construction and Building Materials, 22(3) (2008) 162–174.
19.
GhafooriNader, DiawaraHamidou, BeasleyShane, Resistance to external sodium sulfate attack for early-opening-to-traffic Portland cement concrete, Cement and Concrete Composites, 30(5) (2008) 444–454.
20.
ASTM.Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens, ASTM C39; American Society for Testing and Materials: Philadelphia, 2005.
21.
ASTM, Test Method for Flexural Strength of Concrete (Using Simple Beam with Third-Point Loading), ASTM C496, American Society for Testing and Materials: Philadelphia, 2005.
22.
ASTM.Standard Test Method for Electrical Indication of Concrete's Ability to Resist Chloride Ion Penetration, ASTM C1202; American Society for Testing and Materials: Philadelphia, 2010.