This article studies experimentally the damage behaviors of a 59.5-m-long composite wind turbine blade under accelerated fatigue loads using acoustic emission technique. First, the spectral analysis using the fast Fourier transform is used to study the components of acoustic emission signals. Then, three important objectives including the attenuation behaviors of acoustic emission waves, the arrangement of sensors as well as the detection and positioning of defect sources in the composite blade by developing the time-difference method among different acoustic emission sensors are successfully reached. Furthermore, the clustering analysis using the bisecting K-means method is performed to identify different damage modes for acoustic emission signal sources. This work provides a theoretical and technique support for safety precaution and maintaining of in-service blades.
RasuoBDinulovicMVegA, et al. Harmonization of new wind turbine rotor blades development process: a review. Renew Sust Energ Rev2014; 39: 874–882.
2.
DNV-GL-ST-0376:2015. Rotor blades for wind turbines.
3.
ZhouHFDouHYQinLZ, et al. A review of full-scale structural testing of wind turbine blades. Renew Sust Energ Rev2014; 33: 177–187.
4.
LeeHGParkJ.Static test until structural collapse after fatigue testing of a full-scale wind turbine blade. Compos Struct2016; 136: 251–257.
5.
BaiXAnZHouY, et al. Health assessment and management of wind turbine blade based on the fatigue test data. Microelectronics Reliab2017; 75: 205–214.
6.
EderMABelloniFTesauroA, et al. A multi-frequency fatigue testing method for wind turbine rotor blades. J Sound Vib2017; 388: 123–140.
7.
YangJSPengCYXiaoJY, et al. Application of videometric technique to deformation measurement for large-scale composite wind turbine blade. Appl Energ2012; 98: 292–300.
8.
LiuPFChuJKLiuYL, et al. A study on the failure mechanisms of carbon fiber/epoxy composite laminates using acoustic emission. Mater Design2012; 37: 228–235.
9.
YuFMOkabeYWuQ, et al. A novel method of identifying damage types in carbon fiber-reinforced plastic cross-ply laminates based on acoustic emission detection using a fiber-optic sensor. Compos Sci Technol2016; 135: 116–122.
10.
LiuPFYangJPengXQ.Delamination analysis of carbon fiber composites under hygrothermal environment using acoustic emission. J Compos Mater2017; 51(11): 1557–1571.
11.
HanWQYingLGuAJ, et al. Damage modes recognition and Hilbert-Huang transform analyses of CFRP laminates utilizing acoustic emission technique. Appl Compos Mater2016; 23(2): 155–178.
12.
SayarHAzadiMGhasemi-GhalebahmanA, et al. Clustering effect on damage mechanisms in open-hole laminated carbon/epoxy composite under constant tensile loading rate, using acoustic emission. Compos Struct2018; 204: 1–11.
13.
ZhouWZhaoWZZhangYN, et al. Cluster analysis of acoustic emission signals and deformation measurement for delaminated glass fiber epoxy composites. Compos Struct2018; 195: 349–358.
14.
SaeedifarMNajafabadiMAZarouchasD, et al. Clustering of interlaminar and intralaminar damages in laminated composites under indentation loading using acoustic emission. Compos Part B-Eng2018; 144: 206–219.
15.
XuDLiuPFLiJG, et al. Damage mode identification of adhesive composite joint under hygrothermal environments using acoustic emission and machine learning. Compos Struct2019; 211(1): 351–363.
16.
NiezreckiCAvitabilePChenJ, et al. Inspection and monitoring of wind turbine blade-embedded wave defects during fatigue testing. Struct Health Monit2014; 13(6): 629–643.
17.
BealeCInalpolatMNiezreckiC.Active acoustic damage detection of structural cavities using internal acoustic excitations. Struct Health Monit. Epub ahead of print 14 March 2019. DOI: 10.1177/1475921719835761.
18.
WooSCGooNS.Analysis of the bending fracture process for piezoelectric composite actuators using dominant frequency bands by acoustic emission. Compos Sci Technol2007; 67(7–8): 1499–1508.
19.
Ramirez-JimenezCPapadakisNReynoldsN, et al. Identification of failure modes in glass/polypropylene composites by means of the primary frequency content of the acoustic emission event. Compos Sci Technol2004; 64(12): 1819–1827.
20.
GutkinRGreenCVangrattanachaiS, et al. On acoustic emission for failure investigation in CFRP: pattern recognition and peak frequency analyses. Mech Syst Signal Pr2011; 25(4): 1393–1407.
21.
FotouhiMHeidaryHAhmadiM, et al. Characterization of composite materials damage under quasi-static three-point bending test using wavelet and fuzzy C-means clustering. J Compos Mater2012; 46(15): 1795–1808.
22.
MailletEBakerCMorscherGN, et al. Feasibility and limitations of damage identification in composite materials using acoustic emission. Compos Part A-Appl Sci Manuf2015; 75: 77–83.
23.
Nag-ChowdhurySBellégouHPillinI, et al. Crossed investigation of damage in composites with embedded quantum resistive strain sensors (sQRS), acoustic emission (AE) and digital image correlation (DIC). Compos Sci Technol2018; 160: 79–85.