In this paper, the growth rate of crack opening displacement (COD) in ceramic-matrix composites (CMCs) was investigated using the micromechanical approach. Two damage states of interface partial and complete debonding were considered in determining the CODs and growth rate of CODs considering synergistic effects of fiber bridging and broken. Experimental CODs and growth rate of CODs in SiC/SiC minicomposites with low and high fiber contents were predicted using the developed micromechanical model. Effects of composite constitutive properties, e.g., fiber volume fraction, interface properties and fibers properties, and damage state (i.e., the matrix crack spacing) on the growth rate of CODs and internal damages (e.g., interface debonding ratio and fibers failure probability) were discussed. Relationships between the CODs, growth rate of CODs, and interface debonding ratio were established.
LiL. Characterization of multi-step cyclic-fatigue hysteresis behavior of 2D SiC/SiC composite using inverse tangent modulus. Ceram Int2024; 50: 4392–4403.
3.
LiuXLiL. Design, fabrication and testing of aeroengine ceramic-matrix composite Components. Singapore: Springer Nature, 2024, https://doi.org/10.1007/978-981-97-6109-8.
4.
GlassDE. Ceramic matrix composite (CMC) thermal protection systems (TPS) and hot structures for hypersonic vehicles. The 15th AIAA International Space Planes and Hypersonic Systems and Technologies Conference 28 April 2008 - 01 May 2008, Dayton, Ohio, https://doi.org/10.2514/6.2008-2682.
5.
LiL. Research progress on application and airworthiness compliance validation of ceramic-matrix composites in aeroengines. Acta Materiae Compositae Sinica2025; 42: 54–87.
6.
LiuXGuoXXuY, et al.Cyclic thermal shock damage behavior in CVI SiC/SiC high-pressure turbine twin guide vanes. Materials (Basel)2021; 14: 6104.
7.
BoyleRJGnanaselvamPParikhAH, et al.Design of stress constrained SiC/SiC ceramic matrix composite turbine blades. ASME Turbo Expo 2020: Turbomachinery Technical Conference and Exposition, September 21–25, 2020, Virtual, Online. https://doi.org/10.1115/GT2020-15067.
8.
LangenbrunnerNBWeaverMDunnMG, et al.Dynamic response of a metal and a CMC turbine blade during a controlled rub event using a segmented shroud. J Eng Gas Turbines Power2015; 137: 062504.
9.
LiL. High-temperature matrix cracking, opening and closure in ceramic-matrix composites. Boca Raton: CRC Press, 2023, https://doi.org/10.1201/9781032638508.
10.
SevenerKMTracyJMChenZ,et al.Crack opening behavior in ceramic matrix composites. J Am Ceram Soc2017; 100: 4734–4747.
11.
LiL. Stress-dependent matrix crack opening in SiC/SiC composites: theory and analytical prediction. Compos Interfaces2023; 30: 685–707.
12.
YangCJiaF. Crack opening model for unidirectional ceramic matrix composites at elevated temperature. Ceram Int2018; 44: 17167–17173.
13.
JanowskiMBockKMoosburger-WillJ. Fracture of all-oxide ceramic composites: crack path analysis by surface strain monitoring. Int J Appl Ceram Technol2024; 21: 2663–2670.
14.
DetwilerKHuntROpilaE. In-situ observation of micro-cracking in a SiC/BN/SiC ceramic matrix composite under tension. Open Ceramics2023; 14: 100366.
15.
HilmasAMSevenerKMHalloranJW. Damage evolution in SiC/SiC unidirectional composites by X-ray tomography. J Am Ceram Soc2020; 103: 3436–3447.
16.
JordanSPJeffsSPNewtonCD, et al.Matrix crack networks in SiC/SiC composites: In-situ characterization and metrics. Proceedings of ASME Turbo Expo 2021 Turbomachinery Technical Conference and Exposition GT2021, June 7-11, 2021, Virtual, Online. https://doi.org/10.1115/GT2021-03796.
17.
FathalianMDarbanHPostekE. Atomistic insights into tensile damage of functionally graded Al-SiC composites. Int J Mech Sci2025; 288: 110012.
18.
LiL. Modeling the monotonic and cyclic tensile stress-strain behavior of 2D and 2.5D woven C/SiC ceramic-matrix composites. Mech Compos Mater2018; 54: 165–178.
VerschatseOMikforoozMClerckK,et al.Analysis of fiber-matrix interface debonding under normal loading using in-situ microscopy and cruciform-shaped single glass fiber composite specimens. Compos Sci Technol2025; 263: 111089.
21.
SpilkerKLebensohnRAJacobsenG,et al.A mean field homogenization model for the mechanical response of ceramic matrix composites. Compos Struct2025; 352: 118630.
22.
LiL. A micromechanical crack opening displacement model for fiber-reinforced ceramic-matrix composites considering matrix fragmentation. Theor Appl Fract Mech2021; 112: 102875.
23.
LiL. An approach to estimate crack opening displacement in 2D plain-woven SiC/SiC composite considering different matrix cracking modes. Proce Inst Mech Eng, Part L: J Mater: Des Appl2022; 236: 2017–2026.
24.
FathalianMPostekETahaniM,et al.A comprehensive study of Al2O3 mechanical behavior using density functional theory and molecular dynamics. Molecules2024; 29: 1165.
25.
ChateauCGelebartLBornertM, et al.Modeling of damage in unidirectional ceramic matrix composites and multi-scale experimental validation on third generation SiC/SiC minicomposites. J Mech Phys Solids2014; 63: 298–319.
26.
SimonCRebillatFHerbV,et al.Monitoring damage evolution of SiCf/[Si-B-C]m composites using electrical resistivity: crack density-based electromechanical modeling. Acta Mater2021; 124: 579–587.
27.
LiL. Modeling first matrix cracking stress of fiber-reinforced ceramic-matrix composites considering fiber fracture. Theor Appl Fract Mech2017; 92: 24–32.
28.
LiL. Modeling stress-dependent matrix multiple fracture of fiber-reinforced ceramic-matrix composites considering fiber oxidation and fracture. Compos Interfaces2021; 28: 329–361.
29.
LiL. Comparisons of interface shear stress degradation rate between C/SiC and SiC/SiC ceramic-matrix composites under cyclic fatigue loading at room and elevated temperatures. Compos Interfaces2017; 24: 171–202.
30.
ArslanKGunesR. Penetration mechanics of ceramic/metal functionally graded plates under ballistic impact: an experimental perspective. Compos Struct2024; 331: 117897.
31.
LvXLiLSunJ, et al.Microstructure and tensile behavior of (BN/SiC)n coated SiC fibers and SiC/SiC minicomposites. J Eur Ceram Soc2023; 43: 1828–1842.
32.
LiL. Hysteresis-based identification approach for crack opening and closure stress in SiC/SiC fiber-reinforced ceramic-matrix composites. Int J Fatigue2022; 162: 106945.
33.
LiuHLiLYangJ, et al.Characterization and modeling damage and fracture of Prepreg-MI SiC/SiC composite under tensile loading at room temperature. Appl Compos Mater2022; 29: 1167–1193.
34.
LiL. Synergistic effects of temperature, oxidation, loading frequency and stress-rupture on damage evolution of cross-ply ceramic-matrix composites under cyclic fatigue loading at elevated temperatures in oxidizing atmosphere. Eng Fract Mech2017; 175: 15–30.
35.
MuirCSwaminathanBMusaffarAK, et al.In situ crack opening displacement growth rates of SiC/SiC ceramic matrix minicomposites. J Eur Ceram Soc2023; 43: 3950–3958.
36.
SwaminathanBMcCarthyNRAlmansourAS, et al.Microscale characterization of damage accumulation in CMCs. J Eur Ceram Soc2021; 41: 3082–3093.