Experimental failure analysis and mechanical performance evaluation of fiber-metal sandwich laminates interleaved with polyamide-6,6 interlayers through the combined usage of acoustic emission,thermography and microscopy techniques

Abstract

Fiber-metal laminates are hybrid sandwich composite structures made of thin metallic sheets and layers of fiber-reinforced plastics. In this study, for the first time, the effects of polyamide 66 nonwoven interlayers on the tensile, three-point bending, interlaminar shear strength, and low velocity impact responses of fiber-metal laminates are investigated by coupling acoustic emission, thermography, and microscopy techniques. The fiber-metal laminates are interleaved with polyamide 66 nonwoven fabrics at two different areal weight density, namely, 17 gsm (grams per square meter) and 50 gsm. The tensile, bending, interlaminar shear strength, and low velocity impact tests are carried out in accordance with the ASTM standards. During the tensile and flexural tests, acoustic emission data are collected to understand damage types occurring under various loading conditions and, in turn, clearly shed light on the performance of polyamide 66 for interfacial strengthening in fiber-metal laminates. The results of acoustic emission investigation are correlated with the optical and scanning electron microscope-based microscopic analysis. It is shown that the interlaminar shear strength of fiber-metal laminates can be increased significantly (about 42%) by using polyamide 66 nonwoven interlayers. The impacted fiber-metal laminate specimens are examined to determine damage area and length using the lock-in thermography method. It is found that the polyamide 66 interlayers decrease the debonded length and damaged area up to 39 and 32%, respectively. The tensile and flexural strength and modulus of the fiber-metal laminate are not significantly affected by the presence of polyamide 66 interlayers, except a negligible drop in the value of tensile and flexural strength by 6 and 4%, respectively. The polyamide 66 interlayers are proved to be very successful in enhancing plastic deformation ability of the matrix and bonding efficiency between aluminum and composite sections.

Keywords

Composite fiber-metal laminates interleaving PA 66 interlayers mechanical properties low-velocity impact damage acoustic emission thermography SEM

Get full access to this article

View all access options for this article.

References

Roebroeks

. Fibre-metal laminates: recent developments and applications. Int J Fatigue 1994; 16: 33–42.

Yang

. The mechanical behavior of GLARE laminates for aircraft structures. JOM 2005; 57: 72–79.

Vogelesang

Vlot

. Development of fibre metal laminates for advanced aerospace structures. J Mater Process Technol 2000; 103: 1–5.

Zarei

Brugo

Belcari

et al. Low velocity impact damage assessment of GLARE fiber-metal laminates interleaved by Nylon 6,6 nanofiber mats. Compos Struct 2017; 167: 123–131.

Sinmazçelik

Avcu

Bora

et al. A review: fibre metal laminates, background, bonding types and applied test methods. Mater Des 2011; 32: 3671–3685.

Chandrasekar

Ishak

Jawaid

et al. An experimental review on the mechanical properties and hygrothermal behaviour of fibre metal laminates. J Reinf Plast Comp 2017; 36: 72–82.

Sadighi

Alderliesten

Benedictus

. Impact resistance of fiber-metal laminates: a review. Int J Impact Eng 2012; 49: 77–90.

Sharma

Khan

Parameswaran

. Experimental and numerical investigation on the uni-axial tensile response and failure of fiber metal laminates. Compos Part B-Eng 2017; 125: 259–274.

Mathivanan

Balakrishnan

Krishnan

. Metal thickness, fiber volume fraction effect on the tensile properties, debonding of hybrid laminates. J Reinf Plast Comp 2010; 29: 2128–2140.

10.

Reyes

Cantwell

. The mechanical properties of fibre-metal laminates based on glass fibre reinforced polypropylene. Compos Sci Technol 2000; 60: 1085–1094.

11.

et al. Open-hole tensile progressive damage and failure prediction of carbon fiber-reinforced PEEK-titanium laminates. Compos Part B-Eng 2016; 91: 65–74.

12.

et al. Bending failure mechanism and flexural properties of GLARE laminates with different stacking sequences. Compos Struct 2018; 187: 354–363.

13.

Hinz

Omoori

Hojo

et al. Damage characterisation of fibre metal laminates under interlaminar shear load. Compos Part A-Appl S 2009; 40: 925–931.

14.

Hinz

Heidemann

Schulte

. Damage evaluation of Glare® 4B under interlaminar shear loading at different temperature conditions. Adv Compos Lett 2005; 14: 47–55.

15.

Liu

et al. Interlaminar failure behavior of GLARE laminates under short-beam three-point-bending load. Compos Part B-Eng 2016; 97: 361–367.

16.

Zhang

Chaisombat

et al. Hybrid composite laminates reinforced with glass/carbon woven fabrics for lightweight load bearing structures. Mater Des 2012; 36: 75–80.

17.

Beylergil

Tanoglu

Aktas

. Enhancement of interlaminar fracture toughness of carbon fiber-epoxy composites using polyamide-6,6 electrospun nanofibers. J Appl Polym Sci 2017; 134:45244.

18.

Beylergil

Tanoglu

Aktas

. Effect of polyamide-6,6 (PA 66) nonwoven veils on the mechanical performance of carbon fiber/epoxy composites. Compos Struct 2018; 194: 21–35.

19.

Quan

Mischo

et al. Improving the electrical conductivity and fracture toughness of carbon fibre/epoxy composites by interleaving MWCNT doped thermoplastic veils. Compos Sci Technol 2019; 182: 107775.

20.

Beylergil

Tanoglu

Aktas

. Modification of carbon fibre/epoxy composites by polyvinyl alcohol (PVA) based electrospun nanofibers. Adv Compos Lett 2016; 25: 69–76.

21.

Beylergil

Tanoglu

Aktas

. Mode-I fracture toughness of carbon fiber/epoxy composites interleaved by aramid nonwoven veils. Steel Compos Struct 2019; 31: 113–123.

22.

Lee

Noguchi

Kim

et al. Effect of interleaved non-woven carbon tissue on interlaminar fracture toughness of laminated composites, part I: mode II. J Compos Mater 2002; 36: 2153–2168.

23.

Palazzetti

Zucchelli

Trendafilova

. The self-reinforcing effect of Nylon 6,6 nano-fibres on CFRP laminates subjected to low velocity impact. Compos Struct 2013; 106: 661–671.

24.

Akangah

Lingaiah

Shivakumar

. Effect of Nylon-66 nano-fiber interleaving on impact damage resistance of epoxy/carbon fiber composite laminates. Compos Struct 2010; 92: 1432–1439.

25.

Paipetis AS and Aggelis DG. Damage Assessment in fibrous composites using acoustic emission, acoustic emission, Wojciech Sikorski, IntechOpen, www.intechopen.com/books/acoustic-emission/damage-assessment-in-fibrouscomposites-using-acoustic-emission (2012, accessed 16 April 2020).

26.

Ramirez-Jimenez

Papadakis

Reynolds

et al. Identification of failure modes in glass/polypropylene composites by means of the primary frequency content of the acoustic emission event. Compos Sci Technol 2004; 64: 1819–1827.

27.

Sause

MGR

Gribov

Unwin

et al. Pattern recognition approach to identify natural clusters of acoustic emission signals. Pattern Recogn Lett 2012; 33: 17–23.

28.

Flament

Salvia

Berthel

et al. Local strain and damage measurements on a composite with digital image correlation and acoustic emission. J Compos Mater 2016; 50: 1989–1996.

29.

Ersoy

Mehdikhani

et al. Multi-instrument in-situ damage monitoring in quasi-isotropic CFRP laminates under tension. Compos Struct 2018; 196: 163–180.

30.

Tabrizi

Kefal

Zanjani

JSM

et al. Experimental and numerical investigation on fracture behavior of glass/carbon fiber hybrid composites using acoustic emission method and refined zigzag theory. Compos Struct 2019; 223: 110971.

31.

Bohmann

Schlamp

Ehrlich

. Acoustic emission of material damages in glass fibre-reinforced plastics. Compos Part B-Eng 2018; 155: 444–451.

32.

Yilmaz

Yildiz

. A study on correlating reduction in Poisson’s ratio with transverse crack and delamination through acoustic emission signals. Polym Test 2017; 63: 47–53.

33.

Pawar

Gaikhe

Tewari

et al. Analysis of hole quality in drilling GLARE fiber metal laminates. Compos Struct 2015; 123: 350–365.

34.

Al-Azzawi

ASM

McCrory

Kawashita

et al. Buckling and postbuckling behaviour of Glare laminates containing splices and doublers, part 1: instrumented tests. Compos Struct 2017; 176: 1158–1169.

35.

Ammar

Karra

El Mahi

et al. Mechanical behavior and acoustic emission technique for detecting damage in sandwich structures. Appl Acoust 2014; 86: 106–117.

36.

Pashmforoush

Khamedi

Fotouhi

et al. Damage classification of sandwich composites using acoustic emission technique and k-means Genetic Algorithm. J Nondestruct Eval 2014; 33: 481–492.

37.

Bussiba

Kubiec

Ifergane

et al. Damage evolution and fracture events sequence in various composites by acoustic emission technique. Compos Sci Technol 2008; 68: 1144–1155.

38.

ASTM D2344. In annual book of ASTM standards. Philadelphia, PA: American Society for Testing and Materials, 2013.

39.

ASTM D790-10. In annual book of ASTM standards. Philadelphia, PA: American Society for Testing and Materials, 2010.

40.

ASTM D3039/D3039M-17. Standard test method for tensile properties of polymer matrix composite materials. West Conshohocken, PA: ASTM International, 2017.

41.

De Baere

Van Paepegem

Quaresimin

et al. On the tension–tension fatigue behaviour of a carbon reinforced thermoplastic, part I: limitations of the ASTM D3039/D3479 standard. Polym Test 2011; 30: 625–632.

42.

De Baere

Van Paepegem

Hochard

et al. On the tension–tension fatigue behaviour of a carbon reinforced thermoplastic, part II: evaluation of a dumbbell-shaped specimen. Polym Test 2011; 30: 663–672.

43.

Ester M, Kriegel HP, Sander J, et al. A density-based algorithm for discovering clusters in large spatial databases with noise. In: E. Simoudis, J. Han, and U Fayyad (Eds.), KDD’96: proceedings of the second international conference on knowledge discovery and data mining, 1996, pp. 226–231.

44.

Tran

Drab

Daszykowski

. Revised DBSCAN algorithm to cluster data with dense adjacent clusters. Chemometr Intell Lab 2013; 120: 92–96.

45.

Rajkumar

Krishna

Narasimhamurthy

et al. Investigation of tensile and bending behavior of aluminum based hybrid fiber metal laminates. Proc Mater Sci 2014; 5: 60–68.

46.

Zanjani

JSM

Okan

Letofsky-Papst

et al. Repeated self-healing of nano and micro scale cracks in epoxy-based composites by tri-axial electrospun fibers including different healing agents. RSC Adv 2015; 5: 73133–73145.

47.

Khalili

SML

Daghigh

Farsani

. Mechanical behavior of basalt fiber-reinforced and basalt fiber metal laminate composites under tensile and bending loads. J Reinf Plast Comp 2011; 30: 647–659.

48.

Botelho

Silva

Pardini

et al. A review on the development and properties of continuous fiber/epoxy/aluminum hybrid composites for aircraft structures. Mat Res 2006; 9: 247–256.

49.

Gul

Kausar

Mehmood

et al. Progress on epoxy/polyamide and inorganic nanofiller-based hybrids: introduction, application, and future potential. Polym Plast Technol 2016; 55: 1842–1862.

50.

Jiang J, Ye C, Zhang Z, et al. Acoustic emission testing on aluminum alloy pressure vessels. In: Shen G, Wu Z and Zhang J (Eds.), Advances in acoustic emission technology. Springer proceedings in physics. Cham: Springer, 2017, pp.179.

51.

Wisner

Mazur

Perumal

et al. Acoustic emission signal processing framework to identify fracture in aluminum alloys. Eng Fract Mech 2019; 210: 367–380.

52.

Ridruejo

Gonzalez

Llorka

. Micromechanisms of deformation and fracture of polypropylene nonwoven fabrics. Int J Solids Struct 2011; 48: 153–162.