Tip Parameter Approximation and Fatigue Growth of Crack Towards Inclined Weld Interface Between Strength Mismatched Steels

Abstract

A Mode I crack growing at an angle other than 90° with respect to the interface of weld between strength mismatched steels in a bimetallic composite is investigated. The steels and the weld have nearly identical elastic and thermal expansion properties. As the crack in parent steel reaches near the interface of the weld, the plastic strain or yield zone at its tip spreads to the weld, which causes load transfer effect, due to strength mismatch across the weld interface, over the crack tip. Yield zone is modeled as Dugdale’s cohesive zone subjected to constant closing cohesive traction. Geometrical formulations are employed to approximate change in volume of parts of cohesive zone on either side of the interface resulting upon inclining the interface from the vertical. A computational model for crack tip in front of the perpendicular weld interface in linear elastic regime is modified to account for the effect of inclination of weld interface from the vertical. Crack tip stress intensity parameter is approximated from the model, cyclic value of which is used to assess the rate of fatigue crack growth towards the weld interface. The model is validated by experiments. Bimetallic compact tension specimens, prepared by electron beam welding of weak ASTM 4340 alloy and strong MDN 250 maraging steels at interface angles of 10° and 15° with the vertical, are subjected to high cycle fatigue. Growth rate of crack is found to dip substantially when it reaches near the interface of ultra strong weld. The results are compared with those of plain and bimetallic specimens with perpendicular weld interfaces. Inclination of weld interface from the vertical by nearly all the angles changes, albeit marginally, the values of crack tip parameter visà-vis those in the case of perpendicular weld interface. Theoretical and experimental results are in good agreement with each other.

Keywords

alloy steel bimetallic fatigue inclined weld interface maraging steel strength mismatch weld.

Get full access to this article

View all access options for this article.

References

Dugdale, D.S. ( 1960). Yielding of Steel Sheets Containing Slits, Journal of the Mechanics and Physics of Solids, 8: 100-104.

Ellyin, F. ( 1997). Fatigue Damage, Crack Growth and Life Prediction, London, Chapman and Hall, p. 335.

He, M.Y. and Hutchinson, J.W. ( 1989). Crack Deflection at an Interface Between Dissimilar Elastic Materials, International Journal of Solids and Structures , 25: 1053-1067.

Hellan, K. ( 1985). Introduction to Fracture Mechanics, New York, McGraw-Hill Book Company, p. 45.

Jiang, F. , Deng, Z.L. , Zhao, K. and Sun, J. ( 2003). Fatigue Crack Propagation Normal to a Plasticity Mismatched Bimaterial Interface, Materials Science and Engineering A , 356: 258-266.

Kikuchi, M. ( 1996). Ductile Crack Growth Behaviour of Welded Plate, International Journal of Fracture, 78: 347-362.

Kim, A.S. , Besson, J. and Pineau, A. ( 1999). Global and Local Approaches to Fracture Normal to Interfaces , International Journal of Solids and Structures, 36: 1845-1864.

Kim, A.S. , Suresh, S. and Shih, C.F. ( 1997). Plasticity Effects on Fracture Normal to Interfaces with Homogeneous and Graded Compositions, International Journal of Solids and Structures, 34: 3415-3432.

Knott, J.F. ( 1981). Fundamentals of Fracture Mechanics, London, Butterworths, p. 132.

10.

Milan, M.T. and Bowen, P. ( 2003). Experimental and Predicted Fatigue Crack Growth Resistance in Al 2124/Al 2124+35%SiC Bimaterial, International Journal of Fatigue, 25: 657.

11.

Murakami, Y. (ed.) (1987). Stress Intensity Factors Handbook, Oxford, Pergamon Press, Vol. 1, p. 110.

12.

Pippan, R. , Flechsig, K. and Reimelmoser, F.O. ( 2000). Fatigue Crack Propagation Behaviour in the Vicinity of an Interface Between Materials with Different Yield Stresses, Materials Science and Engineering A, 283: 225-233.

13.

Predan, J. , Gubeljak, N. and Koldnik, O. ( 2007). On the Local Variation of the Crack driving Force in a Double Mismatched Weld, Engineering Fracture Mechanics, 74: 1739-1757.

14.

Reimelmoser, F.O. and Pippan, R. ( 2000). The J-integral at Dugdale Cracks Perpendicular to Interfaces of Materials with Dissimilar Yield Stresses, International Journal of Fracture, 103: 397-418.

15.

Stahle, P. and Shih, C.F. ( 1992). Cracking in Thin Films and Substrates, In: Materials Research Society Symposium Proceedings, Boston, Vol. 239, pp. 567-572.

16.

Sugimura, Y. , Lim, P.G. , Shih, C.F. and Suresh, S. ( 1995a). Fracture Normal to a Bimaterial Interface: Effects of Plasticity on Crack-tip Shielding and Amplification, Acta Metallurgica et Materialia, 43: 1157-1169.

17.

Sugimura, Y. , Grondin, L. and Suresh, S. ( 1995b). Fatigue Crack Growth at Arbitrary Angles to Bimaterial Interfaces, Scripta Metallurgica et Materialia, 33: 2007-2012.

18.

Suresh, S. , Sugimura, Y. and Tschegg, E.K. ( 1992). The Growth of a Fatigue Crack Approaching a Perpendicularly-oriented , Bimaterial Interface, Scripta Metallurgica et Materialia , 27: 1189-1194.

19.

Ukadgaonker, V.G. , Bhat, S. , Jha, M. and Desai, P.B. ( 2008). Fatigue Crack Growth Towards the Weld Interface of Alloy and Maraging Steels, International Journal of Fatigue, 30: 689-705.

20.

Wang, B. and Siegmund, T. ( 2006). Simulation of Fatigue Crack Growth at Plastically Mismatched Bi-material Interfaces, International Journal of Plasticity , 22: 1586-1609.

21.

Wappling, D. , Gunnars, J. and Stahle, P. ( 1998). Crack Growth Across a Strength Mismatched Bimaterial Interface, International Journal of Fracture, 89: 223-243.