In this article, magnetorheological colloid was adopted to coat a stainless steel substrate, which was cured under magnetic field to form magnetic roughness surface. Superhydrophobicity had been verified in the experiments, and the influential factors on the hydrophobic performance had been explored. A regular sawtooth structure model was proposed to relate the hydrophobicity with the formed surface microstructure. With the self-cleaning and bonding strength testing, the magnetic roughness surface is promising to keep sustainable superhydrophobicity in the self-cleaning or drag reduction applications.
AttaAMAl-LohedanHAEzzatAO, et al. (2016) Characterization of superhydrophobic epoxy coatings embedded by modified calcium carbonate nanoparticles. Progress in Organic Coatings101: 577–586.
2.
CassieABDBaxterS (1944) Wettability of porous surfaces. Transactions of the Faraday Society40: 546–551.
3.
ChenSWDongSWangXJ, et al. (2019) Magneto-induced surface morphologies in magnetorheological elastomer films: an analytical study. Smart Materials and Structures28: 045016.
4.
ConradiMKocijanA (2016) Fine-tuning of surface properties of dual-size TiO2 nanoparticle coatings. Surface and Coatings Technology304: 486–491.
5.
DuPWenJZhangZZ, et al. (2017) Maintenance of air layer and drag reduction on superhydrophobic surface. Ocean Engineering130: 328–335.
6.
FengLLiSLiY, et al. (2002) Super-hydrophobic surfaces: from natural to artificial. Advanced Materials14: 1857–1860.
7.
FihriABoveroEAl-ShahraniA, et al. (2017) Recent progress in superhydrophobic coatings used for steel protection: a review. Colloids and Surfaces520: 378–390.
8.
GaoXFJiangL (2004) Water-repellent legs of water striders. Nature432: 36.
9.
GlavanGSalamonPBelyaevaIA, et al. (2018) Tunable surface roughness and wettability of a soft magnetoactive elastomer. Journal of Applied Polymer Science135: 46221.
10.
HuangYFHuMJYiSP, et al. (2012) Preparation and characterization of silica/fluorinated acrylate copolymers hybrid films and the investigation of their icephobicity. Thin Solid Films520: 5644–5651.
11.
IrajizadPHasnainMFarokhniaN, et al. (2016) Magnetic slippery extreme icephobic surfaces. Nature Communications7: 13395.
12.
IslamMSAkterNKarimMR (2010) Preparation of superhydrophobic membranes by electrospinning of fluorinated silane functionalized pullulan. Colloids and Surfaces362: 117–120.
13.
LattheSSGuravABMarutiCS, et al. (2012) Recent progress in preparation of superhydrophobic surfaces: a review. Journal of Surface Engineered Materials and Advanced Technology2: 76–94.
14.
LeeSYimCKimW, et al. (2015) Magnetorheological elastomer films with tunable wetting and adhesion properties. ACS Applied Materials & Interfaces7: 19853–19856.
15.
LiuHGaoSWCaiJS, et al. (2016) Recent progress in fabrication and applications of superhydrophobic coating on cellulose-based substrates. Materials9: 124–160.
16.
MahadikSAPedrazaFVhatkarRS (2016) Silica based superhydrophobic coating for long-term industrial and domestic applications. Journal of Alloys and Compounds663: 487–493.
17.
PaluvaiNRHafeezHHanDH, et al. (2017) Preparation of a high hydrophobic aluminium surface by double zincating process. Journal of Adhesion Science and Technology31: 1061–1074.
18.
QingYQYangCNHuCB, et al. (2015) A facile method to prepare superhydrophobic fluorinated polysiloxane/ZnO nanocomposite coatings with corrosion resistance. Applied Surface Science326: 48–54.
19.
SongHJShenXQJiHY, et al. (2010) Superhydrophobic iron material surface with flower-like structures obtained by a facile self-assembled monolayer. Applied Physics A99: 685–689.
20.
SorokinVVSokolovBOStepanovGV, et al. (2018) Controllable hydrophobicity of magnetoactive elastomer coatings. Journal of Magnetism and Magnetic Materials459: 268–271.
21.
TaghvaeiEMoosaviANouri-BorujerdiA, et al. (2017) Superhydrophobic surfaces with a dual-layer micro- and nanoparticle coating for drag reduction. Energy125: 1–10.
22.
ten BrinkGHFoleyNZwaanD, et al. (2015) Roughness controlled superhydrophobicity on single nanometer length scale with metal nanoparticles. RSC Advances5: 28696–28702.
23.
TorabinejadVAliofkhazraeiMRouhaghdamAS, et al. (2017) The hydrophobicity of Ni-Fe alloy electrodeposits obtained at different current densities. Transactions of the Institute of Metal Finishing95: 190–196.
24.
WangHBChenEYJiaXB, et al. (2015) Superhydrophobic coatings fabricated with polytetrafluoroethylene and SiO2 nanoparticles by spraying process on carbon steel surfaces. Applied Surface Science349: 724–732.
25.
WenQDiJJiangL, et al. (2013) Zeolite-coated mesh film for efficient oil-water separation. Chemical Science4: 591–595.
26.
WenzelRN (1936) Resistance of solid surfaces to wetting by water. Industrial & Engineering Chemistry Research28: 988–994.
27.
XueCHLiYRZhangP, et al. (2014) Washable and wear-resistant superhydrophobic surfaces with self-cleaning property by chemical etching of fibers and hydrophobization. ACS Applied Materials & Interfaces6: 10153–10161.
28.
YangHPiPHCaiZQ, et al. (2010) Facile preparation of super-hydrophobic and super-oleophilic silica film on stainless steel mesh via sol-gel process. Applied Surface Science256: 4095–4102.
29.
YoungT (1805) An essay on the cohesion of fluids. Philosophical Transactions of the Royal Society95: 65–87.
30.
ZhangJHWangJMZhaoY, et al. (2008) How does the leaf margin make the lotus surface dry as the lotus leaf floats on water. Soft Matter4: 2232–2237.