The pressureless pyrolysis of poly(silylacetylene)siloxane precursor to silicon carbide (SiC) was studied. Poly(silylacetylene)siloxane was synthesized via organometallic condensation. The precursor resin was well soluble in acetone, toluene and tetrahydrofuran (THF), etc. Thermal cure was conducted readily at 180-250 °C to form a hard brittle solid, and the cure mechanism was radical polymerization of ethynyl groups. The ceramic yield of pyrolysis at 1500 °C was at about 67 wt.%. The molar ratio of Si/C in the SiC was found at 1:1.1-1:3 based on elements analysis. The results of x-ray diffraction (XRD) revealed the typical β-SiC structure in the poly(silylacetylene)siloxane derived ceramics.
SemenJ., and LoopJ.G., in: 14th Annual Conference on Composites and Advanced Ceramic Materials, Part 2 of 2: Ceramic Engineering and Science Proceedings, edited by WachtmanJ. B., Volume 11, Issue 9/10, Chapter 19, John Wiley & Sons, Inc. (2008).
2.
YajimaS., OkamuraK., HayashiJ., and OmoriM., J. Am. Ceram. Soc., 59 (1976) 324.
3.
YajimaS., HasegawaY., OkamuraK., and MatsuzawaT., Nature, 273 (1978) 527.
4.
SiobhanM., MohanJ.E., and MichaelJ.F., Ceram. Int., 25 (1999) 49.
5.
RushkinI.L., ShenQ., LehmanS.E., and InterranteL.V., Macromol., 30 (1997) 3141.
6.
LangguthK., BöckleS., MüllerE., and RoewerG., J. Mater. Sci., 30 (2001) 5973.
7.
CastroDe, and LuizD., U.S. Patent 5,256,488. (1993).
8.
HuJ.D., ZhengZ.M., MaT., ZhangZ.J., YeJ.P., WangD.Y., and XieZ.M.: J. Polym. Sci. Part A: Polym. Chem., 42 (2004) 2897.