Composite action of the track slab and the self-compacting concrete filling layer subjected to train-induced fatigue load: An experimental investigation

Abstract

To investigate the composite performance of the track slab and the self-compacting concrete filling layer in the China Railway Track System III slab track structure, six segmental specimens comprising either one or a pair of sleepers were fabricated by dividing a full-scale slab track structure. Fatigue tests in the transverse bending perpendicular to the rail were conducted on four slab track specimens supported on rubber plates simulating the subgrade, to a maximum of five million applied load cycles. It was observed in the fatigue tests that longitudinal cracks first appeared on the top surface of the track slab at the mid-span of the specimen. Splitting cracks appeared later from the anchorage ends of the transverse prestressed tendons to the top surface of track slab. Delamination of the track slab–filling layer interface developed with increasing number of cycles. Static three-point bending tests were also conducted on both fatigue-damaged and control composite plate specimens to evaluate the effect of fatigue damage on the composite performance of the track slab and the filling layer. In the static tests, significant deformation developed in the fatigue-damaged specimens from the start of loading, and the fatigue damage and interface delamination adversely affected the composite action of the track slab and the filling layer. Static loads corresponding to new cracking of the fatigue-damaged composite plates were reduced by 20–30%, and the load corresponding to the initial interlayer slip reduced by 25–62% compared with the control specimens. The interfacial bond strength between the track slab and the filling layer is the first line of defense against the interlayer slip, and the dowel action of the interlayer connection reinforcement is the second line of defense. Roughening by multitooth chiseling on the track slab and an increase in the ratio of interlayer connection reinforcements are both effective ways to enhance the composite action of the track slab and the filling layer.

Keywords

Ballastless track track slab self-compacting concrete cooperative working fatigue test damage composite structure

Get full access to this article

View all access options for this article.

References

Robinson

Kapoor

. Fatigue in railway infrastructure, Padstow: CRC Woodhead Publishing Limited, 2009.

Zarembski

. Effect of rail section and traffic on rail fatigue life. Area Bull 1979; 80: 514–527.

Eisenmann

. Stress distribution in the permanent way due to heavy axle load and high speeds. Proc AREA 1970; 71: 24–59.

Peng

Wang

Yue

. Damage evolution theory and life evaluating method for prestressed sleeper. J China Railw Soc 2001; 5: 70–74. (in Chinese).

TB/T 1878-2002. Fatigue test method of prestressed concrete sleeper, Beijing: China Railway Press, 2002. . (in Chinese).

Zhong

Xie

Jia

. Experimental study on application of high performance concrete sleeper. Railw Eng 2005; 11: 58–61. (in Chinese).

Nash

Wang

. Is high speed rail an appropriate solution to China’s rail capacity problems? J Transp Geogr 2014; 40: 100–111.

Ando

Sunaga

Aoki

et al.

Development of slab tracks for Hokuriku Shinkansen lines. Q Rep RTRI 2001; 42: 35–41.

Robertson

Masson

Sedran

et al.

Advantages of a new ballastless trackform. Constr Build Mater 2015; 92: 16–22.

10.

Gautier

P-E

. Slab track: review of existing systems and optimization potentials including very high speed. Constr Build Mater 2015; 92: 9–15.

11.

Zhao

Wang

et al.

Research and application of independently innovative CRTS III ballastless slab track system. Railw Tech Innovat 2015; 2: 40–43. (in Chinese).

12.

Chinese high speed network to double in latest master plan. Railway Gazette, 21 July 2016.

13.

Markine VL and Esveld C (eds). Assessment of high-speed slab track design. In: The eleventh international conference on civil, structural and environmental engineering computing, 2006.

14.

Jiang

Lin

. Experimental study on high-speed railway ballastless track. China Railw 2000; 7: 22–24. (in Chinese).

15.

Chapeleau

et al.

Study of ballastless track structure monitoring by distributed optical fiber sensors on a real-scale mockup in laboratory. Eng Struct 2013; 56: 1751–1757.

16.

Poveda

et al.

A numerical study on the fatigue life design of concrete slabs for railway tracks. Eng Struct 2015; 100: 455–467.

17.

Tarifa

et al.

Full-scale fatigue tests of precast reinforced concrete slabs for railway tracks. Eng Struct 2015; 100: 610–621.

18.

Yuan

et al.

Sealed-space-filling SCC: a special SCC applied in high-speed rail of China. Constr Build Mater 2016; 124: 167–176.

19.

. Study on the fatigue property of CRTS III slab track, Chengdu: Southwest Jiaotong University, 2011. . (in Chinese).

20.

Gao

Zhao

et al.

Analysis on design scheme of CRTS III slab track structure on roadbed. J Tongji Univ (Nat Sci) 2013; 6: 848–855. (in Chinese).

21.

Sun

Duan

Yang

. Static response analysis of CRTS III ballastless track structure. J Railw Eng Soc 2013; 11: 32–39. (in Chinese).

22.

Sun

Duan

Gao

. Comparison of structural analysis models for slab ballastless track in high-speed railway. J Southeast Univ (Nat Sci Ed) 2013; 43: 938–943. (in Chinese).

23.

Wang

Yin

Zhu

et al.

Dynamic analysis of CRTS III slab track-subgrade system under impact load. Sci Sin (Technol) 2014; 7: 722–728. (in Chinese).

24.

Zhu

Zeng

et al.

Experimental study on the mechanical characteristics of CRTS III slab ballastless track under train load. J Railw Sci Eng 2016; 13: 1229–1233. (in Chinese).

25.

Liu

Jin

et al.

Fatigue testing of CRTS III ballastless slab track structures under transverse bending. J Southwest Jiaotong Univ 2018; 53: 23–30. (in Chinese).

26.

GB/T 50081-2002. Standard for test method of mechanical properties on ordinary concrete, Beijing: China Architecture & Building Press, 2003. . (in Chinese).

27.

JTG E60-2008. Field test methods of subgrade and pavement for highway engineering, Beijing: China Communications Press Co. Ltd, 2008. . (in Chinese).

28.

TB 10621-2014. Code for design of high speed railway, Beijing: China Railway Publishing House, 2014. . (in Chinese).

29.

Kaewunruen

Remennikov

. Progressive failure of prestressed concrete sleepers under multiple high-intensity impact loads. Eng Struct 2009; 31: 2460–2473.

30.

Building code requirements for structural concrete (ACI 318M-14) and commentary. Farmington Hills: American Concrete Institute, 2014.