In this work, the influence of hydrothermal ageing on performances of CFRP single lap bonded joints subjected to two types of pre-treatments was investigated. The first is a degreasing pre-treatment, while the second if a laser texturing pre-treatment through a CO2 laser system. The study considered the influence of an aggressive environment on geometrical deviations and mechanical performances of the bonded joints. Measurements showed that adherends were more susceptible to water uptake after ageing, allowing an increase in laminate thickness of about 2.5%. Lap shear tests were carried out and a decrease in obtained mechanical performances was observed only for the degreased specimens, confirming the effectiveness of the adopted laser texturing to reduce ageing effects. Moreover, the proposed laser texturing pre-treatment for bonding is a sustainable process too because reduces the volume of the removed material efficiently with reduced costs.
TaoRAlfanoMLubineauG.In situ analysis of interfacial damage in adhesively bonded composite joints subjected to various surface pretreatments. Compos Part A Appl Sci Manuf2019; 116: 216–223.
2.
BelliniCParodoGPoliniW, et al. Experimental investigation of hydrothermal ageing on single lap bonded CFRP joints. Procedia Struct Integr2018; 9: 101–107.
3.
MatsuzakiRTsukamotoNTaniguchiJ.Mechanical interlocking by imprinting of undercut micropatterns for improving adhesive strength of polypropylene. Int J Adhes Adhes2016; 68: 124–132.
4.
PociusAV.Adhesion and adhesives technology. München, Germany: Carl Hanser Verlag, 2012.
5.
da SilvaLFMFerreiraNMAJRichter-TrummerV, et al. Effect of grooves on the strength of adhesively bonded joints. Int J Adhes Adhes2010; 30: 735–743.
6.
BudheSBaneaMDde BarrosS, et al. An updated review of adhesively bonded joints in composite materials. Int J Adhes Adhes2017; 72: 30–42.
7.
SorrentinoLMarfiaSParodoG, et al. Laser treatment surface: an innovative method to increase the adhesive bonding of ENF joints in CFRP. Compos Struct2020; 233: 111638.
8.
SorrentinoLParodoGTurchettaS.Influence of laser treatment on end notched flexure bonded joints in carbon fiber reinforced polymer: experimental and numerical results. Materials2022; 15: 910.
9.
SathiyamurthyRDuraiselvamM.Selective laser ablation of CFRP composite to enhance adhesion bonding. Mater Manuf Process2019; 34: 1296–1305.
10.
PalmieriFLHopkinsJWohlCJ, et al. Laser surface preparation of epoxy composites for secondary bonding: optimization of ablation depth. In: International SAMPE technical conference, 2015.
11.
KappesRSSchönfeldFLiC, et al. A study of photothermal laser ablation of various polymers on microsecond time scales. Springerplus2014; 3: 489.
12.
WuCWWuXQHuangCG.Ablation behaviors of carbon reinforced polymer composites by laser of different operation modes. Opt Laser Technol2015; 73: 23–28.
13.
SorrentinoLTurchettaSBelliniC.In process monitoring of cutting temperature during the drilling of FRP laminate. Compos Struct2017; 168: 549–561.
14.
SorrentinoLTurchettaSParodoG.Drilling of glare laminates: effect of cutting parameters on process forces and temperatures. Int J Adv Manuf Technol2022; 120: 645–657.
15.
ReitzVMeinhardDRuckS, et al. A comparison of ir- and UV-laser pretreatment to increase the bonding strength of adhesively joined aluminum/CFRP components. Compos Part A Appl Sci Manuf2017; 96: 18–27.
16.
LeoneCPapaITagliaferriF, et al. Investigation of CFRP laser milling using a 30W Q-switched Yb:YAG fiber laser: effect of process parameters on removal mechanisms and HAZ formation. Compos Part A Appl Sci Manuf2013; 55: 129–142.
17.
LiXHouWHanB, et al. Investigation on the continuous wave mode and the MS pulse mode fiber laser drilling mechanisms of the carbon fiber reinforced composite. Polymers2020; 12: 706.
18.
RiveiroAQuinteroFLusquiñosF, et al. Experimental study on the CO2 laser cutting of carbon fiber reinforced plastic composite. Compos A Appl Sci Manuf2012; 43: 1400–1409.
19.
ShyhaI.An investigation into CO2 laser trimming of CFRP and GFRP composites. Procedia Eng2013; 63: 931–937.
20.
GräfSStaupendahlGKrämerA, et al. High precision materials processing using a novel Q-switched CO2 laser. Opt Lasers Eng2015; 66: 152–157.
21.
BelliniCParodoGSorrentinoL.Effect of operating temperature on aged single lap bonded joints. Def Technol2020; 16: 283–289.
22.
BaneaMDSilvaLFMDCampilhoRDSG. Effect of temperature on tensile strength and mode i fracture toughness of a high temperature epoxy adhesive. J Adhes Sci Technol2012; 26: 939–953.
23.
QinGNaJMuW, et al. Effect of continuous high temperature exposure on the adhesive strength of epoxy adhesive, CFRP and adhesively bonded CFRP-aluminum alloy joints. Compos B Eng2018; 154: 43–55.
24.
ZavattaNRondinaFFalaschettiMP, et al. Effect of thermal ageing on the mechanical strength of carbon fibre reinforced epoxy composites. Polymers2021; 13: 2006.
25.
McConnellBKPethrickRA.A dielectric study of hydrolytic ageing and the effects of periodic freezing in carbon fibre reinforced plastic jointed structures. Int J Adhes Adhes2010; 30: 214–224.
26.
HuPShiZWWangXX, et al. Strength degradation of adhesively bonded single-lap joints in a cyclic-temperature environment using a cohesive zone model. J Adhes2015; 91: 587–603.
27.
RudawskaANalepaJMüllerM.The effect of degreasing on adhesive joint strength. Adv Sci Technol Res J2017; 11: 75–81.
28.
SorrentinoLParodoGTurchettaS.CFRP laser texturing to increase the adhesive bonding: morphological analysis of treated surfaces. J Adhes2021; 97: 1322–1335.
29.
SorrentinoLParodoGGiulianoG.Lightweight structures: an innovative method to uniform the thickness of metal sheets by patchwork blanks. Int J Mater Manuf2022; 5: 20–28.
30.
RashediASridharITsengKJ.Fracture characterization of glass fiber composite laminate under experimental biaxial loading. Compos Struct2016; 138: 17–29.
31.
BelliniCParodoGPoliniW, et al. Influence of hydrothermal ageing on single lap bonded CFRP joints. Frat ed Integrità Strutt2018; 12: 173–182.
32.
BoutarYNaïmiSMezliniS, et al. Effect of surface treatment on the shear strength of aluminium adhesive single-lap joints for automotive applications. Int J Adhes Adhes2016; 67: 38–43.
33.
QinZYangKWangJ, et al. The effects of geometrical dimensions on the failure of composite-to-composite adhesively bonded joints. J Adhes2021; 97: 1024–1051.