Hardness characterisation of grey cast iron and its tribological performance in a contact lubricated with soybean oil

Abstract

The effect of hardness of grey cast iron flat specimen on its wear and friction on the contact were characterised with the presence of vegetable oil as biolubricant. Prior to the tribological test, the as-received grey cast iron flat specimen hardness was characterised. Friction and wear tests were then conducted using a ball-on-flat reciprocating sliding contact. The one-way analysis of variance (ANOVA) was used to determine the significance of friction and wear data with a 95% significance level. The wear scars after the test were then characterised by surface roughness and wear mechanism. The microstructure and elemental analysis were also reported. The average value of hardness was 210 HV with a large difference between minimum (185 HV) and maximum (250 HV) values. The friction and wear performance of grey cast iron specimens with soybean oil varied with its hardness. The specimens with higher hardness gave lower friction coefficient and greater wear resistance than the lower hardness specimens. The difference in coefficient of friction produced between high hardness specimens (COF = 0.122) and low hardness specimens (COF = 0.140) was 17%. In terms of mass loss, the low hardness specimens (mass loss = 50.38 mg) and the high hardness specimens (mass loss = 12.90 mg) produced a difference of 74%. It is shown that, with soybean oil lubricant, the grey cast iron specimen can produce wide range of tribological data especially on mass loss due to its hardness distribution. The influence of soybean oil lubrication in this work is less in improving the wear resistance (about 7%), but greater for friction reduction (about 24%) compared to an unlubricated grey cast iron surface. The hardness of grey cast iron specimen is an important parameter that needs to be specifically measured and controlled on the contact due to wide hardness distribution of grey cast iron may produce variation in tribological data.

Keywords

Hardness grey cast iron biolubricants wear

Get full access to this article

View all access options for this article.

References

Taylor

Eyre

. A review of piston ring and cylinder liner materials. Tribol Int 1979; 12: 79–89.

Glaeser

. Materials for tribology, Amsterdam, Netherlands: Elsevier, 1992.

Sugishita

Fujiyoshi

. The effect of cast iron graphites on friction and wear performance I: Graphite film formation on grey cast iron surfaces. Wear 1981; 66: 209–221.

Bian

Maj

Borland

. The unlubricated sliding wear of steels: The role of the hardness of the friction pair. Wear 1993; 166: 1–5.

Khruschov

. Principles of abrasive wear. Wear 1974; 28: 69–88.

Moore

. The relationship between the abrasive wear resistance, hardness and microstructure of ferritic materials. Wear 1974; 28: 59–68.

Mokhtar

MOA

Zaki

Shawki

GSA

. Effect of mechanical properties on frictional behaviour of metals. Tribol Int 1979; 12: 265–268.

Bowden

Tabor

Palmer

. The friction and lubrication of solids. Am J Phys 1951; 19: 428–429.

Mokhtar

MOA

. The effect of hardness on the frictional behaviour of metals. Wear 1982; 78: 297–304.

10.

BS EN 1561:2011. Founding grey cast iron.

11.

Shturmakov

Loper

Jr . Predictive analysis of mechanical properties in commercial gray iron. Am Foundry Soc 2002; 99: 609–615.

12.

Terheci

Manory

Hensler

. The friction and wear of automotive grey cast iron under dry sliding conditions, Part 1-Relationships between wear loss and testing parameters. Wear 1995; 180: 73–78.

13.

Rac

. Influence of load and speed on wear characteristics of grey cast iron in dry sliding — selection for minimum wear. Tribol Int 1985; 18: 29–33.

14.

Liu

Schissler

Mathia

. The influence of surface oxidation on the wear resistance of cast iron. Tribol Int 1995; 28: 433–438.

15.

Sugishita

Fujiyoshi

. The effect of cast iron graphites on friction and wear performance. Wear 1981; 68: 7–20.

16.

Angus

. Cast iron: Physical and engineering properties, London: Butterworth, 2013.

17.

Adedayo

. Relationship between graphite flake sizes and the mechanical properties of grey iron. Int J Mater Sci Appl 2013; 2: 94–98.

18.

Masjuki

Maleque

Kubo

et al.

Palm oil and mineral oil based lubricants - their tribological and emission performance. Tribol Int 1999; 32: 305–314.

19.

Imran

Masjuki

Kalam

et al.

Study of friction and wear characteristic of jatropha oil blended lube oil. Procedia Eng 2013; 68: 178–185.

20.

Castro

Perez

Erhan

et al.

A study of the oxidation and wear properties of vegetable oils: Soybean oil without additives. J Am Oil Chem Soc 2006; 83: 47–52.

21.

Adhvaryu

Erhan

. Epoxidized soybean oil as a potential source of high-temperature lubricants. Ind Crops Prod 2002; 15: 247–254.

22.

Dodos

Anastopoulos

Zannikos

. Tribological evaluation of biobased lubricant basestocks from cottonseed and soybean oils. SAE Int J Fuels Lubric 2010; 3: 378–385.

23.

Bartz

. Lubricants and the environment. Tribol Int 1998; 31: 35–47.

24.

Wilson

. Lubricants and functional fluids from renewable sources. Ind Lubric Tribol 1998; 50: 6–15.

25.

Hollinghurst

. High temperature lubrication requirements of European gasoline and diesel engines for cars. SAE Int 1974; 740973: 3057–3076.

26.

Bernard

. Fundamentals of fluid film lubrication, New York: Marcel Dekker, 2004.

27.

Hutchings

. Tribology: Friction and wear of engineering materials, London: Butterworth-Heinemann, 1992.

28.

Brown

. Foseco foundryman’s handbook, Oxford: Butterworth-Heinemann, 2000.

29.

Blau

. Interpretations of the friction and wear break-in behavior of metals in sliding contact. Wear 1981; 71: 29–43.

30.

Rigney

Hirth

. Plastic deformation and sliding friction of metals. Wear 1979; 53: 345–370.

31.

Buckley DH. Effect of carbon content on friction and wear of cast irons. NASA Technical Paper, 1977, p. 1052.

32.

Blau

. Friction science and technology: From concepts to applications, Boca Raton, FL: CRC Press, 2008.

33.

Rabinowicz

. Lubrication of metal surfaces by oxide films. ASLE Trans 1967; 10: 400–407.

34.

Moore

AJW

Tegart

WJM

. Relation between friction and hardness. Proc Roy Soc Lond Ser A 1952; 212: 452–458.

35.

Rigney

. The roles of hardness in the sliding behavior of materials. Wear 1994; 175: 63–69.

36.

Plint G. The sliding hertzian point contact in tribotesting: Understanding its limitations as a model of real systems. In: STLE 70th annual meeting & exhibition, 17–21 May 2015. Texas: STLE.

37.

Ponter

ARS

Hearle

Johnson

. Application of the kinematical shakedown theorem to rolling and sliding point contacts. J Mech Phys Solids 1985; 33: 339–362.

38.

Williams

. The influence of repeated loading, residual stresses and shakedown on the behaviour of tribological contacts. Tribol Int 2005; 38: 786–797.

39.

BS EN ISO 945-1: 2008. Microstructure of cast irons Part 1: Graphite classification by visual analysis, London: British Standards, 2008.

40.

Prasad

. Sliding wear response of a cast iron under varying test environments and traversal speed and pressure conditions. Wear 2006; 260: 1333–1341.

41.

Stott

Wood

. The influence of oxides on the friction and wear of alloys. Tribol Int 1978; 11: 211–218.

42.

Honary

Ritcher

. Biobased lubricants and greases: Technology and Products, Chichester: John Wiley and Sons, 2011.