Here, the effect of thermo-oxidative aging on domestic T800 carbon fiber/epoxy resin composites was studied using mass loss rate curves, interface morphology, infrared spectroscopy, and dynamic mechanical property analysis. The composites were subjected to thermo-oxidative aging tests after low-velocity impact. Then, the effect of environmental factors on the damage area of the composites and the compression performance after impact were investigated. The results showed that the composites underwent physical and chemical aging at 185°C. Due to the short aging time, the mass loss rate slowly increased. After aging, thermo-oxidative aging caused the matrix to crack, and the sample cracks that formed after impact expanded, and the damage area also slightly increased. The residual compressive strength of the material fluctuated due to the competing reinforcing and destructive effects of the composite during thermo-oxidative aging; however, aging had little effect on the impact damage morphology and compression failure mode. Upon extending the aging time, thermo-oxidative aging caused the tanδ peak to gradually shift to a higher temperature, and the glass transition temperature (Tg) increased.
BakarMDukRPrzybyłekM, et al.Mechanical and thermal properties of epoxy resin modified with polyurethane. J Reinf Plast Comp2008; 28(17): 2107–2118.
4.
ZhangJZhangQMaHP, et al. Study of hydrothermal aging of carbon fiber/epoxy resin composites G827/5224,G803/5224. Eq Environ Eng2008; 5(03): 19–23.
5.
AtasCDoganA. An experimental investigation on the repeated impact response of glass/epoxy composites subjected to thermal ageing. Composites Part B2015; 75: 127–134.
6.
MaSHXuZXuL, et al.The influence of cyclic hygrothermal-thermal aging on the interfacial property of carbon fiber reinforced bismaleimide resin matrix composite. Highpolymer Mater Sci Eng2018; 34(3): 54–59.
7.
TsotsisTKKellerSLeeK, et al.Aging of polymeric composite samples for 5000 hours at elevated pressure and temperature. Compos Sci Technol2001; 61(1): 75–86.
8.
BehzadKMeysamEMohammadRN, et al.Experimental investigation on response and failure modes of 2D and 3D woven composites under low velocity impact. J Mater Sci2020; 55(3): 1069–1091.
9.
WangZBZhangTJFanJJ, et al.Moist heat aging behavior of T300/648 composites. Mater Mech Eng2015.
10.
LinZYXuXWZhuWY. Research on impact damage characteristics and compressive strength of composite laminates after impact. J Aeronaut Mater2011; 31(1): 73–80.
11.
DaoBHodgkinJKrstinaJ, et al.Accelerated aging versus realistic aging in aerospace composite materials. V. The effects of hot/wet aging in a structural epoxy composite. J Appl Polym Sci2010; 115(2): 901–910.
12.
LinYCXuC. Moisture sorption-desorption-resorption characteristics and its effect on the mechanical behavior of the epoxy system. Polyme2005; 46(25): 11994–12003.
13.
AhmadFHongJWChoiHS, et al.Hygro effects on the low-velocity impact behavior of unidirectional CFRP composite plates for aircraft applications. Compos Struct2016; 135: 276–285.
14.
ZhouSJiaYXXuL, et al.Study on the damage behavior of carbon fiber composite after low-velocity impact under hygrothermal aging. Appl Polym Sci2020; 138: e50289. DOI: 10.1002/app.50289.
15.
MaSHFeiBQXuL, et al.Influence of thermal-oxidative aging on property of carbon fiber bismaleimide resin composite. J Mater Eng2017; 45(12): 50–57.
16.
American Society for Testing and Materials. ASTM D7136/D7136M-2012 standard test method for measuring the damage resistance of fiber-reinforced polymer matrix composite to a drop-weight impact event. PA: ASTM International, 2012.
17.
American Society for Testing and Materials. ASTM D7137/D7137M-2017 standard test method for compressive residual strength properties of damaged polymer matrix composite plates. PA: ASTM International, 2017.
18.
WangSQDongSLGaoY. Thermal ageing effects on mechanical properties and barely visible impact damage behavior of a carbon fiber reinforced bismaleimide composite. Mater Des2017; 115: 213–223.
19.
XuLHeYMaSH, et al.Effects of hygrothermal and thermal-oxidative ageing on the open-hole properties of T800/high-temperature epoxy resin composites with different hole shapes. High Perform Polym2019. DOI: 10.1177/0954008319860892.
20.
VuDQGigliottiMLafarie-FrenotMC. Experimental characterization of thermo-oxidation-induced shrinkage and damage in polymer-matrix composites. Compos Part A Appl Sci Manuf2012; 43: 577–586.
21.
ZhangYP. Thermal oxygen aging mechanism of carbon fiber/epoxy resin composite materials. Beijing: Beijing University of Chemical Technology, 2007.
22.
LvXYWangRTLiuXH. Effect of thermal-oxidative aging on the mechanical properties of carbon fiber reinforced bis-maleimide composites. Adv Mater Res2010; 152/153: 829–833.
23.
LévêqueDSchiefferAMavelA. Analysis of how thermal aging affects the long-term mechanical behavior and strength of polymer-matrix composites. Compos Sci Technol2005; 65(3–4): 395–401.
24.
XuLHeYMaSH, et al.Effects of thermal-oxidative aging on the mechanical properties of open-hole T800 carbon fiber/high-temperature epoxy composites. High Perform Polym2019; 32(5): 494–505.
25.
FanWLiJL. Effects of thermo-oxidative aging on flexural properties of carbon fiber fabric reinforced polymer matrix composites. Acta Materiae Compos Sinica2015; 32(5): 1260–1270.
26.
SchoeppnerGTandonGRipbergerE. Anisotropic oxidation and weight loss in PMR-15 composites. Compos Part A-Appls2007; 38(3): 890–904.
27.
ShenZChenPHLiJS. Experimental study on the compressive failure mechanisms of damaged composite laminates. Acta Aeronaut Astronaut Sin1991; 12(3): 1–5.
ScarponiC. Impact testing on composites laminates and sandwich panels. J Compos Mater1996; 30(17): 1873–1911.
30.
SchiefferAMaireJLévêqueD. A coupled analysis of mechanical behaviour and ageing for polymer-matrix composites. Compos Sci Technol2002; 62(4): 543–549.
31.
XuZRAshbeeKHG. Photoelastic study of the durability of interfacial bonding of carbon fiber epoxy resin composites. J Mater Sci1994; 29(2): 394–403.
32.
ZhangMZuoCSunB. Thermal ageing degradation mechanisms on compressive behavior of 3-D braided composites in experimental and numerical study. Compos Struct2016; 140: 180–191.
33.
LiXJXuFHChenXW. Research on thermal oxygen aging of advanced polymer matrix composite materials. J Mater Eng1999; (12): 19–22.
34.
ChenWMWeiMWangCZ, et al.Study on hydrothermal properties of carbon fiber composites with multi-frequency dynamic mechanical thermal analysis. J Mater Eng2006; (S1): 355–359.
35.
BullionsTAMcGrathJELoosAC. Thermal-oxidative aging effects on the properties of a carbon fiber-reinforced phenylethynyl-terminated poly(etherimide). Compos Sci Technol2003; 63(12): 1737–1748.
36.
LiYLWanLQHuangFR, et al.Wet-heat aging behavior of carbon fiber/polytriazole resin composites. Fiber Reinf Plast/Compos2014; (11): 36–41.
37.
MaSHHeYHuiL, et al. Effects of hygrothermal and thermal aging on the low-velocity impact properties of carbon fiber composites. Adv Compos Mater2019; 29(9): 1–18, doi:10.1080/09243046.2019.1630054.
38.
GaoYHeSYangDZ, et al.Effect of vacuum thermo-cycling on physical properties of unidirectional M40J/AG-80 composites.Compos Part B-Eng2005; 36(4): 351–358.
RarBC. Temperature Effect during humid ageing on interfaces of glass and carbon fibers rein forced epoxy composites.Colloid Interf Sci2006; 298: 111–117.
41.
JangiSRHAkhondMAbsalanG. A field-applicable colorimetric assay for notorious explosive triacetone triperoxide through nanozyme-catalyzed irreversible oxidation of 3, 3′-diaminobenzidine. Microchim Acta2020; 187(8): 431.
42.
JangiSRHAkhondMDehghaniZ. High throughput covalent immobilization process for improvement of shelf-life, operational cycles, relative activity in organic media and enzymatic kinetics of urease and its application for urea removal from water samples. Process Biochem2020; 90: 102–112.