Investigation of the Durability Characteristics of Fiber Reinforced Plastic (FRP) Materials in Concrete Environment

Abstract

Commercially available fiber reinforced plastic (FRP) materials were used in this investigation. Accelerated laboratory tests were performed mostly on samples conditioned in simulated concrete pore solution to evaluate the long-term durability characteristics. Most glass fiber reinforced plastic (GFRP) bars were tested after conditioning to evaluate the changes in tensile strength and stiffness with respect to the unconditioned samples. Mass uptake/absorption of alkaline solution and morphological changes of FRP specimens were also studied. The acceleration test regime used in this investigation can be used as a method for determining the durability characteristics of FRP materials in a concrete environment and for the selection of FRP products for demonstration projects before finalizing the design codes and specifications. A simple mass uptake measurement under accelerated test conditions can be used as a first-step screening procedure to eliminate poor-quality products from further testing.

Keywords

fiber reinforced plastics (FRP)durability accelerated test concrete reinforcement concrete pore solution

References

Gentry, T. R. . L. C. Bank , A. Barkatt , and L. Prian . 1996. Accelerated Test Methods to Determine the Long-Term Behaviour of Composite Highwvay Structures Subject to Environmental Loading. Paper ID 866 Symposium On Composite Materials in Non-Aerospace Applications, ASTM STP 1323, ASTM. West Conshohocken. PA.

Gerriste, A. 1992. Durability Criteria for Non-Metallic Tendons in an Alkaline Environment. Proceedings of the 1st International Conference on Advanced Composite Materials in Bridges and Structures, Sherbrooke. Quebec, Canada. Edited by K. W. Neale and P. Labossire , Canadian Society of Civil Engineering, Montreal, Canada.

Goodman. S. and A. Coomarasamy . 1997. Basalt Fibre Reinforced Plastic Grids as Potential Concrete Reinforcement. Research and Development Branch Report (to be published), Ministry of Transportation Ontario, Ontario, Canada.

Mochizuki, S. , Y. Matsuzaki , and M. Sugita . 1993. Evaluation Items and Methods of FRP Reinforcement as Structural Elements. International Symposium on Fibre-Reinforced-Plastic Reinforcement for Concrete Structures, Edited by Antonio Nanni and Charles W. Dolan , American Concrete Institute, Detroit, MI.

Proctor, B. A. , D. R. Oakley and K. L. Litherland . 1982. Developments in the Assessment and Performance of GRC over 10 years. Composites, 13(2), pp. 173-179.

Walzak, T. L. 1994. Adhesion Loss Mechanics of Epoxy Coatings on Rebar Surfaces. Final Report for the Ministry of Transportation Ontario and Concrete Reinforcing Institute, Ontario Canada.