Determination of Manufacturing Conditions for Hot-Gas-Aided Thermoplastic Tape Winding

Abstract

Carbon/PEEK (APC-2) thermoplastic composite rings are manufactured by the thermoplastic tape winding process using hot nitrogen gas as a heat source. In the tape winding process, localized melting causes a high rate of heating and cooling, which demands different manufacturing conditions from hot pressing and autoclave processing. Heating rate and cooling rate are found to be more than 20,000⁰C/min and 5,000⁰C/min, respectively, and melt time is found to be in the range of 1 to 4 seconds for hot gas processing. Shorter melt times and higher heating rate during the on-line consolidation process require higher processing temperatures (greater than 600'C) for sufficient molecular interdiffusion. Higher molecular interdiff-usion would produce better interlaminar properties.

During the production of thermoplastic composite parts using the thermoplastic tape winding process, several parameters such as heat intensity, tape speed, consolidation pressure, preheating temperature of tape and tool material, and cooling rate can affect the properties of an end product. A judicious selection of such parameters can produce a composite part which has fewer voids, better consolidation, minimum residual stress, desired crystallinity and high quality. Effects of dominant processing parameters such as heat intensity, tape speed, and consolidation pressure on temperature distribution, processinduced deformation, quality of consolidation, and crystallinity are examined.

Keywords

thermoplastic tape winding hot-gas processing manufacturing

References

1. Cogswell, F. N. 1992. "Thermoplastic Aromatic Polymer Composites," Butterworth Heinemann Ltd., publisher.

2. Ghasemi Nejhad, M. N. 1993. "Issues Related to Processability during the Manufacture of Thermoplastic Composites Using On-Line Consolidation Technique," Journal of Thermoplastic Composite Materials, 6(2):130-146.

3. Beyeler, E. P. and S. I. Guqeri . 1988a. "Thermal Analysis of Laser Assisted Thermoplastic Matrix Composite Tape Consolidation," Journal of Heat Transfer, 110:424-424.

4. Grove, S. M. 1988. "Thermal Modelling of Tape Laying with Continuous Carbon Fibre Reinforced Thermoplastic, Composites, 19:367-367.

5. Ghasemi Nejhad, M. N. , R. D. Cope and S. I. Guqeri . 1991. "Thermal Analysis of In-situ Thermoplastic Composite Tape Laying," Journal of Thermoplastic Composite Materials, 4(1):20-20.

6. Ghasemi Nejhad, M. N. 1992. "Three Dimensional Thermal and Residual Stress Analysis of Insitu Thermoplastic Composite Filament Winding," Ph.D. thesis, University of Delaware, Newark, DE, Department of Mechanical Engineering.

7. Mantell, S. C. and G. S. Springer . 1992. "Manufacturing Process Models for Thermoplastic Composites," Journal of Composite Materials, 26:16-16.

8. Beyeler, E. , W. Phillips and S. I. Guqeri . 1988b. "Experimental Investigation of Laser-Assisted Thermoplastic Tape Consolidation," Journal of Thermoplastic Composite Materials, 1:107-107.

9. Hauber, D. 1987. "Robotic Filament Winding with Advanced Thermoplastics," EM87-552, Society of Manufacturing Engineers.

10.

10. Hauber, D. E. and L. A. Hill . 1990. "Automated Fiber Placement of Thermoplastic Composites on Complex Shapes," EM90-658, Society of Manufacturing Engineers.

11.

11. Carpenter, C. E. and J. S. Colton . 1993. "On-Line Consolidation Mechanisms in Thermoplastic Filament Winding (Tape Laying)," 38th International SAMPE Symposium, Anaheim, p. 205-205.

12.

12. Werdermann, C. , K. Friedrich , M. Cirino and R. B. Pipes . 1989. "Design and Fabrication of an On-Line Consolidation Facility for Thermoplastic Composites," Journal of Thermoplastic Composite Materials, 2:293-293.

13.

13. Mazumdar, S. K. and S. V. Hoa . 1993a. "Experimental Determination of Process Parameters for Laser Assisted Processing of PEEK/Carbon Thermoplastic Composites," 38th International SAMPE Symposium, Anaheim.

14.

14. Agarwal, V. 1991. "The Role of Molecular Mobility in the Consolidation and Bonding of Thermoplastic Composite Materials," Ph.D. dissertation, University of Delaware, Newark, DE, Materials Science Program.

15.

15. Mazumdar, S. K. and S. V. Hoa . 1993b. "Comparative Effect of Processing by Hot Gas and Laser Heating on Properties of APC-2 (PEEK/Carbon) Composite Rings," ICCM-9, Madrid, Spain.

16.

16. Mazumdar, S. K. 1994. 'Automated Manufacturing of Composite Components by Thermoplastic Tape Winding and Filament Winding," Ph.D. thesis, Concordia University, Montreal, Canada, Department of Mechanical Engineering.

17.

17. Day, M. , J. D. Cooney and D. M. Wiles . 1989. "The Thermal Stability of Poly (aryl-Ether-EtherKetone) as Assessed by Thermogravimetry," Journal of Applied Polymer Science, 38:323-337.

18.

18. Saint-Royre, D. , D. Gueugnant and D. Reveret . 1989. "Test Methodology for the Determination of Optimum Fusion Welding Conditions of Polyethylene," Journal of Applied Polymer Science, 38:147-147.

19.

19. Blundell, D. J. , J. M. Chalmers , M. W. Mackanzie and W. P. Gaskin . 1985. "Crystalline Morphology of the Matrix of PEEK-Carbon Fiber Aromatic Polymer Composites, I Assessment of Crystallinity," SAMPE Quarterly, 16(4):22-30.

20.

20. Seferis, J. C. , C. Ahlstrom and S. H. Dillman . 1987. "Cooling Rate and Annealing as Processing Parameters for Semicrystalline Thermoplastic Based Composites," Proceedings of Society of Plastic Engineers, ANTEC, 33:1467-1467.

21.

21. Velisaris, C. N. and J. C. Seferis . 1986. "Crystallization of Polyetheretherketone (PEEK) Matrices$' Polymer Engineering and Science, 26:1574-1574.

22.

22. Velisaris, C. N. and J. C. Seferis . 1988. "Heat Transfer Effects on the Processing Structure Relationships of Polyetheretherketone (PEEK) Based Composites," Polymer Engineering and Science, 28(9):583-583.

23.

23. Lee, Y. and R. S. Porte . 1988. "Effect of Thermal History on Crystallization of Poly (ether-etherketone)," Macromolecules, 21:2770-2776.

24.

24. Jeronimidis, G. and A. T. Parkyn . 1988. "Residual Stresses in Carbon Fibre-Thermoplastic Matrix Laminates," Journal of Composite Materials, 22:401-401.