Three types of polyamide 6 based blends are prepared, in which the intermolecular interactions are different, ranging from ‘no interaction’ to strong interaction. Under two extreme cooling conditions, the melts of the blends crystallized and then the crystalline structure and melting behaviors are examined, respectively. The results suggest that depending upon the degree of intermolecular interaction and the amount of the second component, PA6 may have different crystal forms.
Zhang, S. J. , Pang, C. , Yang, D. Z. and Zhao, J. Q. (2003). Study on Hygroscopic PA6/PEG Polyblends , China Synthetic Rubber Industry, 26(1): 40-40 .
2.
Zhang, S. J. , Yang, D. Z. and Zhao, J. Q. (2003). Structure and Property of Hygroscopic PA6/PVP Blend , China Plastics Industry, 31(1): 33-35 .
3.
Jefferson Chem Co Inc. (1972). US Patent, 3,654,370.
4.
Lofquist, R. A. and Saunders, P. R. (1985). Hydrophilic Nylon for Improved Apparel Comfort , Textile Research Journal, 55(6): 325-333 .
5.
Zahran, A. H. (1985). Dyeing and Hydrophilicity of Nylon-6/Polyacrylic Acid Grafting Copolymers , American Dyestuff Report, 74(6): 32-36 .
6.
Hutterer, E.G. (1965). US Patent, 1,381,123A.
7.
Masahiko, S. and Isao, K. (1989). σ- Potential and Surface Dyeability of Grafted Nylon 6 Fibers in Aqueous Solution of Methylene Blue , Journal of the Society of Fiber Science & Technology, 45(9): 394-398 .
8.
Seymour, H.R. (1957). US Patent, 341,773.
9.
Kato, H. (1971). JP Patent, 69-16198.
10.
Chen, F. and Gu, L. X. (1993). The Present Research Situation on High Hygroscopic Nylon , China Synthetic Fiber Industry, 16(3): 47-51 .
11.
Zhang, S. J. and Zhao, J. Q. (2004). Structure and Properties of Hygroscopic PA6-Inorganic Salt Blend , Journal of Elastomers and Plastics, 36(3): 241-250 .
12.
Holmes, D. , Bunn, C. and Smith, D. (1955). The Crystal Structure of Polycaproamide: Nylon 6 , J. Polym. Sci., 17(84): 159-177 .
13.
Donald, C. and Vogelsong, D. (1963). Crystal Structure Studies on the Polymorphic Forms of Nylons 6 and 8 and Other Even Nylons , J. Polym. Sci., Part A, 1(3): 1055-1068 .
14.
Arimoto, H. (1964). α-γ Transition of Nylon 6 , J. Polym. Sci., Part A, 2(5): 2283-2295 .
15.
Arimoto, H. , Ishibashi, M. and Hirai, M. (1965). Crystal Structure of the γ-form of Nylon 6 , J. Polym. Sci., Part A, 3(1): 317-326 .
16.
Gurato, G. , Fichera, A. , Grandi, F. , Zanetti, R. and Canal, P. (1974). Crystallinity and Polymorphism of 6-Polyamide , Makromol. Chem., 175(8): 953-975 .
17.
Arimoto, H. (1962). γ-α Transition of Nylon 6 by Drawing , Kobunshi Kagaku, 19(3): 212-218 .
18.
Kinoshita, Y. (1959). An Investigation of the Structures of Polyamide Series , Makromol. Chem., 33(1): 1-20 .
19.
Ito, M. , Mizuochi, K. and Kanamoto, T. (1998). Effects of Crystalline Forms on the Deformation Behaviour of Nylon-6 , Polymer, 39(19): 4593-4598 .
20.
Flory, P. J. (1969). Statistical Mechanics of Chain Molecules, p. 106-106, Wiley-Interscience, New York .
21.
Kohan, M. I. (1973). Nylon Plastics, p. 156-156, Wiley-Interscience, New York .
22.
Valenti, B. and Bianchi, E. (1973). Bulk Properties of Synthetic Polymer-Inorganic Salt Systems. Melting Behavior of Salted Poly(caproamide) , J. Physical Chemistry, 77(3): 389-395 .
23.
Fu, B. X. (1994). Polyamide Resin Handbook (in Chinese), p. 261-261, China Petrochemical Press, Beijing .
24.
Garcia, D. (1985). Hydrogen Bonding in Nylon 66 and Model Compounds , J. Polym. Sci., Polym. Phys. Ed., 23(3): 537-555 .