Ti–C:H coatings were deposited on original, nitrided, and polished-nitrided AISI 316L stainless steel substrates using a closed field unbalanced magnetron sputtering system. Sliding friction wear tests were performed in 0.89 wt.% NaCl solution under a load of 30 N against AISI 316L stainless steel, Si3N4, and Ti6Al4V balls, respectively. The electrochemical properties of the various specimens were investigated by means of corrosion tests performed in 0.89 wt.% NaCl solution at room temperature. Finally, the biocompatibility properties of the specimens were investigated by performing cell culturing experiments using purified mouse leukemic monocyte macrophage cells (Raw264.7). In general, the results showed that plasma nitriding followed by Ti–C:H coating deposition provides an effective means of improving the wear resistance, anti-corrosion properties, and biocompatibility performance of AISI 316L stainless steel.
CrysterLAParkerKGParkerTL. The effect of surface chemistry and nanotopography of titanium nitride (TiN) films on 3T3-L1 fibroblasts. J Biomed Mater Res A2003; 67: 138–147.
2.
LiuCLYangDLinG. Corrosion resistance and hemocompatibility of multilayered Ti/TiN-coated surgical AISI 316L stainless steel. Mater Lett2005; 59: 3813–3819.
3.
FossatiABorgioliFGalvanettoE. Glow-discharge nitriding of AISI 316L austenitic stainless steel: influence of treatment time. Surf Coat Technol2006; 200: 3511–3517.
4.
MingoloNTschiptschinAPPinedoCE. On the formation of expanded austenite during plasma nitriding of an AISI 316L austenitic stainless steel. Surf Coat Technol2006; 201: 4215–4218.
5.
ButlerEPBurkeMG. Chromium depletion and martensite formation at grain boundaries in sensitized austenitic stainless steel. Acta Mater1986; 34: 557–570.
6.
GellingsPJJonghMAD. Grain boundary oxidation and the chromium depletion theory of intercrystalline corrosion of austenitic stainless steels. Corros Sci1967; 7: 413–421.
7.
HashemiBYazdiMRAzarV. The wear and corrosion resistance of shot peened-nitrided 316L austenitic stainless steel. Mater Des2011; 32: 3287–3292.
8.
RusopMKinugawaTSogaT. Preparation and microstructure properties of tetrahedral amorphous carbon films by pulsed laser deposition using camphoric carbon target. Diam Relat Mater2004; 13: 2174–2179.
9.
MilneWITsaiJTHTeoKBK. Novel field emission structure based on tetrahedrally bonded amorphous carbon. Diam Relat Mater2003; 12: 195–200.
10.
FukuiHOkidaJOmoriN. Cutting performance of DLC coated tools in dry machining aluminum alloys. Surf Coat Technol2004; 187: 70–76.
11.
KaoWHSuYLYaoSH. The optimum composition of Me–C:H coatings on drills for cutting performance. Mater Sci Eng A2005; 398: 233–240.
12.
FirkinsPHaileyJLFisherJ. Wear of ultra-high molecular weight polyethylene against damaged and undamaged stainless steel and diamond-like carbon-coated counterfaces. J Mater Sci1998; 9: 597–601.
YinGFLuoJMZhengCQ. Preparation of DLC gradient biomaterials by means of plasma source ion implant-ion beam enhanced deposition. Thin Solid Films1999; 345: 67–70.
15.
SchroederAFranczGBruininkA. Titanium containing amorphous hydrogenated carbon films (a-C: H/Ti): surface analysis and evaluation of cellular reactions using bone marrow cell cultures in vitro. Biomaterials2000; 21: 449–456.
16.
DuCSuXWCuiFZ. Morphological behavior of osteoblasts on diamond-like carbon coating and amorphous C–N film in organ culture. Biomaterials1998; 19: 651–658.
17.
KimDHKimHELeeKR. Characterization of diamond-like carbon films deposited on commercially pure Ti and Ti–6Al–4V. Mater Sci Eng C2002; 22: 9–14.
18.
SuiJHGaoZYCaiW. DLC films fabricated by plasma immersion ion implantation and deposition on the NiTi alloys for improving their corrosion resistance and biocompatibility. Mater Sci Eng A2007; 454–455: 472–476.
19.
WangMZhaoYXuR. Direct formation of amine functionality on DLC films and surface cyto-compatibility. Diam Relat Mater2013; 38: 28–31.
20.
LiGJPengQLiC. Effect of DC plasma nitriding temperature on microstructure and dry-sliding wear properties of 316L stainless steel. Surf Coat Technol2008; 202: 2749–2754.
21.
ZhangZLBellT. Structure and corrosion resistance of plasma nitrided stainless steel. Surf Eng1985; 1: 131–136.
22.
SuYLKaoWH. Effect of thickness and carbon content on tribological behaviour and mechanical properties of Ti-C:H coatings. Wear1999; 236: 221–234.
23.
KaoWHSuYLYaoSH. Tribological property and drilling application of Ti–C:H and Cr–C:H coatings on high-speed steel substrates. Vacuum2006; 80: 604–614.
24.
YoshidaHFaustAWilckensJ. Three-dimensional dynamic hip contact area and pressure distribution during activities of daily living. J Biomech2006; 39: 1996–2004.
25.
ParkWWKimEKJeonJH. Wear of UHMWPE against nitrogen-ion-implanted and NbN-coated Co–Cr–Mo alloy formed by plasma immersion ion implantation and deposition for artificial joints. Appl Surf Sci2012; 258: 8228–8233.
26.
ChristiansenTSomersMAJ. Low temperature gaseous nitriding and carburising of stainless steel. Surf Eng2004; 21: 445–455.
27.
SunYLiXYBellT. X-ray diffraction characterisation of low temperature plasma nitrided austenitic stainless steels. J Mater Sci1999; 34: 4793–4802.
28.
DongH. S-phase surface engineering of Fe-Cr, Co-Cr and Ni-Cr alloys. Int Mater Rev2010; 55: 65–98.
29.
BaranowskaJArnoldB. Corrosion resistance of nitrided layers on austenitic steel. Surf Coat Technol2006; 200: 6623–6628.
30.
BhattacharyaAKNixWD. Analysis of elastic and plastic deformation associated with indentation testing of thin films on substrates. Int J Solids Struct1988; 24: 1287–1298.
31.
WalterKCKungHLevineT. Characterization and performance of diamond-like carbon films synthesized by plasma and ion-beam-based techniques. Surf Coat Technol1995; 75: 734–738.
RobertsonJ. Diamond-like amorphous carbon. Mater Sci Eng R2002; 37: 129–281.
34.
FerrariACRobertsonJ. Interpretation of Raman spectra of disordered and amorphous carbon. Phys Rev B2000; 61: 14095–14107.
35.
SuYLKaoWH. Tribology and application of Ti-C:H- and Cr-C:H-coated cemented tungsten carbide substrates. Surf Coat Technol2001; 137: 293–303.
36.
YangPHuangNLengYX. Wettability and biocompatibility of nitrogen-doped hydrogenated amorphous carbon films: effect of nitrogen. Nucl Instrum Methods Phys Res B2006; 242: 22–25.
37.
HasebeTIshimaruTKamijoA. Effects of surface roughness on anti-thrombogenicity of diamond-like carbon films. Diam Relat Mater2007; 16: 1343–1348.
38.
Costa-RodriguesJFernandesALopesMA. Hydroxyapatite surface roughness: complex modulation of the osteoclastogenesis of human precursor cells. Acta Biomater2012; 8: 1137–1145.