Synthesis and Characterization of a New Trimethacrylate Monomer with Low Polymerization Shrinkage and Its Application in Dental Restoration Materials

Abstract

In this study, a new trimethacrylate monomer α,α,α′-tri[4-(2′-hydroxy-3′-methacryloyloxy-propoxy)phenyl]-1-ethyl-4-isopropylbenzene (α,α,α′-THMPEIB) with a molecular weight of 850 and a large molecular volume was designed and synthesized. The structure of monomer α,α,α′-THMPEIB was confirmed by FT-IR, ¹H NMR, and elemental analysis. Degree of double-bond conversion, volume shrinkage, water sorption and solubility, diffusion coefficient value, and flexure strength of α,α,α′-THMPEIB/tri(ethylene glycol) dimethacrylate- (TEGDMA) based resin were measured. 2,2-Bis[4-(2′-hydroxy-3′-methacryloyloxy-propoxy)-phenyl]-propane (bis-GMA)/TEGDMA monomer mixture was used as reference. The result showed that the α,α,α′-THMPEIB/TEGDMA-based resin had the lower double-bond conversion, polymerization shrinkage, and water solubility than bis-GMA/TEGDMA-based resin. Water sorption and diffusion coefficient value of α,α,α′-THMPEIB/TEGDMA-based resin were nearly the same as those of bis-GMA/TEGDMA-based resin. Flexural strength of α,α,α′-THMPEIB/TEGDMA-based resin was higher than that of bis-GMA/ TEGDMA-based resin.