Influence of Magnesium Hydroxide and Huntite Hydromagnesite on Mechanical Properties of Ethylene Vinyl Acetate Compounds Cross-linked by DiCumyl Peroxide and Ionizing Radiation

Abstract

Flame retardants including magnesium hydroxide (MH) and huntite hydromagnesite (HH) were used to develop halogen free flame retardant (HFFR) compounds based on ethylene vinyl acetate (EVA) for wire and cable applications. Cone calorimeter and limiting oxygen index (LOI) results show that cross-linking affects not only mechanical properties, but also flame retardancy. Consequently, flame retardancy is mainly influenced by type of flame retardants and mixing ratio of base polymers and to a lesser extent by cross-linking. Tensile strength increased with increase of MH, while elongation at break decreased with increase of MH in cross-linked formulations. On the other hand, elongation at break increased with increase of HH while tensile strength decreased with increase of HH in cross-linked formulations. HFFR compounds with tensile strength of 12 MPa, elongation at break of 200%, LOI of 40% was developed to meet the stringent specifications of wire and cable industry.

Keywords

magnesium hydroxide huntite hydromagnesite halogen free wire and cable EVA flame retardancy.

Get full access to this article

View all access options for this article.

References

Mans, V. and Tortosa, E. ( 1998). Flame Retardants Based on Ammonium Polyphosphate and Combinations for Plastics, Flame Retardants, 98: 183-193.

Rai, M. and Brown, S. ( 1998). Inorganic Flame Retardants - Alone and in Combinations , Flame Retardants, 98: 83-91.

Wei, P. , Han, Z. , Xu, X. and Li, Z. ( 2006). Synergistic Flame Retardant Effect of SiO2 in LLDPE/EVA/ATH Blends, Journal of Fire Sciences, 24(6): 487-498.

Luciana, R. , Estevao, M. , Le Bras, M. , Delobel, R. and Nascimento, R.S.V. ( 2005). Spent Refinery Catalyst as a Synergistic Agent in Intumescent Formulations: Influence of the Catalyst’s Particle Size and Constituents , Polymer Degradation Stability, 88(3): 444-455.

Cogen, J.M. , Lin, T.S. , Klier, J. and Whaley, P.D. ( 2006). International Patent, Improved Cross-linked Automotive Wire WO2006/026256A1.

Wanzke, W. , Goihl, A. and Nass, B. ( 1998). Intumescent Systems for Polyolefines-performance Profile in Electrical Applications, Flame Retardants, 98: 195-206.

Lomakin, S.M. and Zaikov, G.E. ( 2003). Modern Polymer Flame Retardancy, Brill Academic Publishers, Boston, pp. 159-177.

Chang, S. , Xie, T. and Yang, G. ( 2006). Effects of Polystyrene-encapsulated Magnesium Hydroxide on Rheological and Flame-retarding Properties of HIPS Composites , Polymer Degradation Stability, 91(12): 3266-3273.

Du, L. , Qu, B. and Xu, Z. ( 2006). Flammability Characteristics and Synergistic Effect of Hydrotalcite with Microencapsulate Red Phosphorus in Halogen-free Flame Retardant EVA Composite, Polymer Degradation Stability, 91(5): 995-1001.

10.

Liu, Y. and Wang, Q. ( 2006). Melamine Cyanurte-Microencapsulated Red Phosphorus Flame Retard Unreinforced and Glass Fiver Reinforced Polyamide 66, Polymer Degradation Stability, 91(12): 3103-3109.

11.

Laoutid, F. , Gaudon, P. , Taulemesse , J.M. , Lopez Cuesta , J.M. , Velasco, J.I. and Piechaczyk, A. ( 2006). Study of Hydromagnesite and Magneisum Hydroxide Based Fire Retardant Systems for Ethylene-vinyl Acetate Containing Organo-Modified Montmorillonite, Polymer Degradation Stability, 91(12): 3074-3082.

12.

Ma, H. , Xu, Z. , Tong, L. , Gu, A. and Fang, Z. ( 2006). Studies of ABS-graft-maleic Anhydride/Clay Nanocomposites: Morphologies, Thermal Stability and Flammability Properties, Polymer Degradation Stability, 91(8): 2951-2959.

13.

Szep, A. , Szabo, A. , Toth, N. , Anna, P. and Marosi, G. ( 2006). Role of Montmorillonite in Flame Retardancy of Ethylene-vinyl Acetate Copolymer, Polymer Degradation Stability , 9: 593-599.

14.

International Standard. (2004). Power Cables with Extruded Insulation and Their Accessories for Rated Voltages from 1 kV (Um = 1,2 kV) up to 30 kV (Um = 36 kV), Part 1: Cables for Rated Voltages of 1 kV (Um = 1,2 kV) and 3 kV (Um = 3,6 kV), 2nd edn, IEC 60502-1.

15.

British Standard, 600/1000V and 1900/3300V (1998). Armoured Electric Cables Having Thermosetting Insulation and Low Emission of Smoke and Corrosive Gases When Affected By Fire. BS 6724: 1997 and Thermosetting Insulated Cables for Electric Power and Lighting with Low Emission of Smoke and Corrosive Gases When Affected by Fire. BS7211.