Influence of Fiber-Matrix Adhesion on Mechanical Properties of Graphite/Epoxy Composites: II. Interlaminar Fracture and Inplane Shear Behavior

Abstract

A comprehensive experimental study was conducted to determine the effects of fiber-matrix adhesion on Mode I and Mode II interlaminar fracture toughness, interlaminar shear strength, and inplane shear properties of the graphite/epoxy composites with different fiber volume fractions. With the improvement of fiber/matrix adhesion by fiber surface treatment and sizing, Mode I and Mode II interlaminar fracture toughness, interlaminar shear strength and inplane shear strength of the composites were clearly increased. However, the interlaminar fracture properties were not so sensitive to the variation of fiber volume fraction. Only a slight increase in the interlaminar shear strength was found when the fiber volume fraction of the graphite/epoxy composites was increased. The results also indicate that although the fiber/matrix interface can play a role in controlling the interlaminar fracture behavior to a certain extent, the improvement of interlaminar fracture toughness resulting from interfacial modification is not as great as that obtained by the use of the toughened matrices.

Keywords

graphite/epoxy composites fiber-matrix adhesion interlaminar fracture toughness interlaminar shear strength inplane shear strength fiber volume fraction

Get full access to this article

View all access options for this article.

References

1. Herakovich, C. T. 1981. "On the Relationship Between Engineering Properties and Delamination of Composite Materials," J. Composite Materials, 15:336-348.

2. Reifsnider, K. L. 1991. "Damage and Damage Mechanics," Fatigue of Composite Materials, Composite Materials Series, 4, K. L. Reifsnider Ed., 4:11-77.

3. Sela, N. and O. Ishai . 1989. "Interlaminar Fracture Toughness and Toughening of Laminated Composite Materials: A Review," Composites, 20(5):423-435.

4. Hunston, D. L. , R. J. Moulton , N. J. Johnston and W. D. Bascom . 1987. "Matrix Resin Effects in Composite Delamination: Mode I Fracture Aspects," Toughened Composites ASTMSTP 937, N. J. Johnston , Ed., American Society for Testing and Materials, Philadelphia, pp. 74-94.

5. Yee, A. F. 1987. "Modifying Matrix Materials for Tougher Composites," Toughened Composites ASTMSTP 937, N. J. Johnston , Ed., American Society for Testing and Materials, Philadelphia, pp. 383-396.

6. Martin, R. H. and G. B. Murri . 1990. "Characterization of Mode I and Mode II Delamination Growth and Thresholds in AS4/PEEK Composites," Composite Materials, ASTM STP 1059, S. P. Garbo , Ed., American Society for Testing and Materials, Philadelphia, pp. 251-270.

7. Evans, R. E. and J. E. Masters . 1987. "A New Generation of Epoxy Composites for Primary Structural Applications: Materials and Mechanics," Toughened Composites ASTM STP 93 7, N. J. Johnston , Ed., American Society for Testing and Materials, Philadelphia, pp. 413-436.

8. Mignery, L. A. , T. M. Tan and C. T. Sun . 1985. "The Use of Stitching to Suppress Delamination in Laminated Composites," Delamination and Debonding, ASTMSTP 876, W. S. Johnson , Ed., American Society for Testing and Materials, Philadelphia, pp. 371-385.

9. Schwartz, H. S. and J. T. Hartness . 1987. "Effect of Fiber Coatings on Interlaminar Fracture Toughness of Composites," Toughened Composites ASTMSTP 937, N. J. Johnston , Ed., American Society for Testing and Materials, Philadelphia, pp. 150-178.

10.

10. Madhukar, M. and L. T. Drzal . 1992. "Fiber-Matrix Adhesion and Its Effect on Composite Mechanical Properties: IV. Mode I and Mode II Fracture Toughness of Graphite/Epoxy Composites," J. Composite Materials, 26(7):936-968.

11.

11. Lee, S. M. 1992. "Influence of Fiber/Matrix Interfacial Adhesion on Composite Fracture Behavior," Compos. Sci. Technol., 43:317-327.

12.

12. Goan, J. C. and S. P. Prosen . 1969. "Interfacial Bonding in Graphite Fiber-Resin Composites," Interfaces in Composites, ASTMSTP 452, American Society for Testing and Materials, pp. 3-26.

13.

13. Scola, D.A. and C. S. Brooks . 1970. "Surface Aspects of New Fibers, Boron, Silicon Carbide, and Graphite," J. Adhesion, 2:213-237.

14.

14. Tang, L. G. and J. L. Kardos . 1997. "A Review of Methods for Improving the Interfacial Adhesion Between Carbon Fiber and Polymer Matrix," Polym. Compos., 18(1):100-113.

15.

15. Kim, J. K. and Y. W. Mai . 1991. "High Strength, High Fracture Toughness Fiber Composites with Interface Control A Review," Composites Sci. Technol., 41:333-378.

16.

16. Deng, S. , L. Ye , Y.-W. Mai and H.-Y. Liu . 1998. "Evaluation of Fiber Tensile Strength and Fiber/Matrix Adhesion Using Fiber Fragmentation Tests," Composites A, 29A:423-434.

17.

17. Deng, S. , L. Ye and Y.-W. Mai . 1998. "Interfacial Shear Strength of Carbon Fiber/Epoxy Mode Composites Evaluated by a Single Fiber Pull-Out Test Method," Advanced Composite Materials, 7(2):169-182.

18.

18. Deng, S. and L. Ye . 1999. "Influence of Fiber-Matrix Adhesion on Mechanical Properties of Graphite/Epoxy Composites: I. Tensile, Flexure, and Fatigue Properties," J. Reinforced Plastics and Composites, this issue.

19.

19. Xiao, K. , L. Ye and Y. S. Kwok . 1998. "Effects of Pre-Cracking Methods on Fracture Behavior on An Araldite-F Epoxy and Its Rubber-Modified System," J. Mater. Sci., 33:2831-2836.

20.

20. Carlsson, L. A. , J. W. Gillespie and R. B. Pipes . 1986. "On the Analysis and Design of the End Notched Flexure (ENF) Specimen for Mode II Testing," J. Composite Materials, 20:594-604.

21.

21. Whitney, J. M. 1992. "Reflections on the Development of Test Methods for Advanced Composites," Composite Materials: Testing and Design (Tenth Volume), ASTMSTP 1120, American Society for Testing and Materials, Philadelphia, pp. 7-16.