The effect of bio-fibres and bio-particles on the fracture toughness has been investigated. Epoxy resin is used as matrix material and different bio-fibers such as banana fiber, bagasse fiber, coconut fiber and particles such as silica and walnut shell particle with different wt% are added as reinforcing material. The mode I fracture toughness tests are conducted in a servo hydraulic universal testing machine. The results show that the fracture toughness of bio-composites reinforced with 20 wt% bagasse or 10 wt% coconut fiber are 1.108 MPa √m and 1.094 MPa √m, respectively which are about 8% and 7% higher than neat epoxy. Addition of 2 wt% of silica with 20 wt% of bagasse shows 60% increment of fracture toughness with respect to bagasse and 72% increment with respect to neat epoxy. Hybridisation of bagasse with banana fibers shows 54% decrease in fracture toughness as compared to bagasse and 13% increase as compared to banana. The overall fracture toughness of hybrid bio-composite of 10 wt% coconut fiber and 20 wt% of walnut shell particle is 1.367 MPa √m which is about 25% higher than coconut fiber reinforced bio-composite.
MohantyAKMisraMHinrichsenG. Biofibers biodegradable polymers and biocomposites: an overview. Macromol Mater Eng2000; 276/277: 1–24.
6.
Chaudhary AK, Gope PC, Singh VK, et al. Thermal analysis of epoxy based coconut fiber-almond shell particle reinforced biocomposites. Adv Manf Sci Tech 2014; 38.
7.
Verma D, Gope PC Maheshwari MK and Sharma RK. Mechanical Properties and Morphological Study of Fly-Ash-Bagasse Composites. J Inst Eng India Ser D 2012; 93(2): 65–71.
8.
VermaDGopePCShandilyaA. Evaluation of mechanical properties and morphological studies of bagasse fibre (chemically treated/untreated)-CaCO3 epoxy hybrid composites. J Inst Eng India Ser D2014; 95: 27–34.
9.
OhKHHanKS. Short-fiber/particle hybrid reinforcement: effects on fracture toughness and fatigue crack growth of metal matrix composites. Compo Sci Technol2007; 67: 1719–1726.
10.
LaffanMJPinhoSTRobinsonP. Translaminar fracture toughness testing of composites: a review. Polym Test2012; 31: 481–489.
ZhaoDBotsisJ. Experimental and numerical studies in model composites, part I: experimental results. Int J Fract1996; 82: 153–174.
13.
ChoiNSTakahashiK. Toughness and microscopic fracture mechanisms of unfilled and short-glass-fiber-filled poly(cyano arylether). J Mater Sci1996; 31: 731–740.
14.
BotsisJBeldicaC. Strength characteristics and fatigue crack growth in a composite with long aligned fibers. Int J Fract1995; 69: 27–50.
15.
ZunjarraoSuraj CSinghRaman P. Characterization of the fracture behavior of epoxy reinforced with nanometer and micrometer sized aluminum particles. Compos Sci Technol2006; 66: 2296–2305.
16.
Byung Chul KimSang Wook ParkDai Gil Lee. Fracture toughness of the nano-particle reinforced epoxy composite. Compos Struct2008; 86: 69–77.
17.
Milad ZamanianMehrzad MortezaeiBabak Salehnia. Fracture toughness of epoxy polymer modified with nanosilica particles: particle size effect. Eng Fract Mech2013; 97: 193–206.
18.
Gope PC and Rao DK. Fracture behavior of epoxy biocomposite reinforced with short coconut fibres (Cocos nucifera) and walnut particles (Juglans regia L.), J Thermoplast Compos Mater, 2014. DOI:10.1177/0892705714556835.
19.
ASTM E399-09E2. Standard test method for linear-elastic plane strain fracture toughness KIc of metallic materials. West Conshohocken: ASTM, 2011.
20.
ASTM-D5045, Standard test methods for plane-strain fracture toughness and strain energy release rate of plastic materials. West Conshohocken: ASTM, 2007.
21.
ShinichiS. Effects of forming processing conditions on the flexural properties of bagasse and bamboo plastic composites. BioResources2012; 7: 5381–5390.
22.
GuimarãesJLFrollini E da SilvaCGWypychF. Characterization of banana, sugarcane bagasse and sponge gourd fibers of Brazil. Ind Crops Products2009; 30: 407–415.
23.
Rao DK and Gope PC. Fracture toughness of walnut particles (Juglans regia L.) and Coconut Fiber-Reinforced Hybrid Biocomposite. Polym Compos 2015; 36(1): 167–173.
GopePCSinghVK. Effect of filler addition and strain rate on the compressive strength of silica- styrene butadiene rubber filled epoxy composites. J Poly Eng Sci2011; 51: 1130–1136.
26.
SinghVKGopePCChauhanS. Mechanical behavior of banana fiber based hybrid biocomposites. J Mater Environ Sci2012; 3: 185–194.
27.
AyatollahiMRAlihaMRMSaghafiH. An improved semi-circular bend specimen for investigating mixed mode brittle fracture. Eng Fract Mech2011; 78: 110–123.
28.
GopePCBishtNSinghVK. Influence of crack offset distance on interaction of multiple collinear and offset edge cracks in a rectangular plate. Theor Appl Fract Mech2014; 70: 19–29.
29.
NemliGDemirelSGumuokayaE. Feasibility of incorporating waste grass clippings (Lolium perenne L.) in particleboard composites Waste Manage. 2009. 29: 1129–1129.
30.
HaiwenGuYangboGuoSiew Yee Wonga. Effect of interphase and strain-rate on the tensile properties of polyamide 6 reinforced with functionalized silica nanoparticles. Comp Sci Technol2013; 75: 62–69.
31.
ShadlouSAlishahiEAyatollahiMR. Fracture behavior of epoxy nanocomposites reinforced with different carbon nano-reinforcements. Comps Struct2013; 95: 577–581.
32.
JohnsenBBKinlochAJMohammedRD. Toughening mechanisms of nanoparticle-modified epoxy polymers. Polymer2007; 48: 530–541.
33.
KinlochAJMaxwellDYoungRJ. Micromechanisms of crack propagation in hybrid-particulate composites. J Mater Sci Lett1985; 4: 1276–1279.
34.
SpanoudakisJYoungRJ. Crack propagation in a glass particle-filled epoxy resin. Part1 effect of particle volume fraction and size. J Mater Sci1984; 19: 473–486.
35.
EvansAGFaberKT. Crack growth resistance of micro cracking brittle materials, J. Am. Ceram Soc1984; 67: 255–260.