This article investigates the dispersion of nanoclay and its effect on the properties of nanoclay/epoxy nanocomposites developed using a high-shear mixing technique. Epon 828, Nanomer 1.30 E, and a compatible amine-curing agent (Epikure W) were the materials used. The dispersion of nanoclay was studied using XRD and TEM at different levels of magnification. Even though nanoclays were found to have exfoliated based on XRD’s d-spacing data (>8 nm), they remained as tactoids based on TEM data. The effect of curing on the dispersion of nanoclay was also studied using XRD analysis, which showed polymerization of resin in-between the nanoclay layers during curing. This polymerization was only helpful for the exfoliation of nanoclay, it could not completely delaminate and disperse the individual nanoclay layers. The nanocomposites were characterized using dynamic mechanical analysis and ASTM standard fracture tests. Measured elastic modulus was compared with the predicted modulus using modified Halpin—Tsai model. The experimental value was less than the predicted value and the difference was attributed to the poor dispersion of nanoclays. However, addition of 5.3 wt% nanoclay increased the storage modulus and the fracture toughness of epoxy resin by 21 % and 16%, respectively. The fracture morphologies indicated that the major toughening mechanism was due to crack deflection around nanoclay tactoids.
Usuki A., Kojima Y., Kawasumi M., et al. Synthesis of Nylon 6-Clay hybrid. J Mater Res1993; 8(5): 1179-1184.
2.
Kojima Y., Usuki A., Kawasumi M., et al. Mechanical properties of Nylon 6-Clay hybrid. J Mater Res1993; 8(5): 1185-1189.
3.
Tjong SCStructural and mechanical properties of polymer nanocomposites. Mater Sci Eng2006; 53(3-4): 73-197.
4.
Zeng QH, Yu AB, Lu GQ and Paul DRClay-based polymer nanocomposites: research and commercial development. J Nanosci Nanotechnol2005; 5(10): 1574-1592.
5.
Hussain F., Hojjati M., Okamoto M. and Gorga REReview article: Polymer-matrix nanocomposites, processing, manufacturing, and application: an overview. J Compos Mater2006; 40(17): 1511-1575.
6.
Alexandre M. and Dubois P.Polymer-layered silicate nanocomposites: preparation, properties and uses of a new class of materials. Mater Sci Eng2000; 28(1-2): 1-63.
7.
Ray SS and Okamoto M.Polymer/layered silicate nanocomposites: a review from preparation to processing . Prog Polym Sci2003; 28(11): 1539-1641.
8.
Wang MS and Pinnavaia TJClay-polymer nanocomposites formed from acidic derivatives of montmorillonite and an epoxy resin. Chem Mater1994; 6(4): 468-474.
9.
Lan T. and Pinnavaia TJClay-reinforced epoxy nanocomposites. Chem Mater1994; 6(12): 2216-2219.
10.
Luo JJ and Daniel IMCharacterization and modeling of mechanical behavior of polymer/clay nanocomposites . Compos Sci Technol2003; 63(11): 1607-1616.
11.
Becker O., Varley R. and Simon G.Morphology, thermal relaxations and mechanical properties of layered silicate nanocomposites based upon high-functionality epoxy resins. Polymer2002; 43(16): 4365-4373.
12.
Yasmin A., Abot JL and Daniel IMCompounding of nanoclay/epoxy composites with a three-roll mill. Mater Res Soc Symp Proc2002; 740: 75-80.
13.
Zunjarrao SC , Sriraman R. and Singh RPEffect of processing parameters and clay volume fraction on the mechanical properties of epoxy-clay nanocomposites. J Mater Sci2006; 41(8): 2219-2228.
14.
Becker O., Cheng Y., Varley RJ and Simon GPLayered silicate nanocomposites based on various high-functionality epoxy resins: the influence of cure temperature on morphology, mechanical properties, and free volume. Macromolecules2003; 36(5): 1616-1625.
15.
Kornmann X. , Thomann R., Mulhaupt R., Finter J. and Berglund L.Synthesis of amine-cured, epoxy-layered silicate nanocomposites: the influence of the silicate surface modification on the properties. J Appl Polym Sci2002; 86(10): 2643-2652.
16.
Messersmith PB and Giannelis EPSynthesis and characterization of layered silicate-epoxy nanocomposites. Chem Mater1994; 6(10): 1719-1925.
17.
Zhang K., Wang L., Wang F., Wang G. and Li Z.Preparation and characterization of modified-clay-reinforced and toughened epoxy-resin nanocomposites. J Appl Polym Sci2003; 91(4): 2649-2652.
18.
Miyagawa H. , Rich MJ and Drzal LTAmine-cured epoxy/clay nanocomposites. II. The effect of the nanoclay aspect ratio. J Polym Sci, Part B: Polym Phys2004; 42(23): 4391-4400.
19.
Miyagawa H. , Foo KH, Daniel IM and Drzal LTMechanical properties and failure surface morphology of amine-cured epoxy/clay nanocomposites. J Appl Polym Sci2004; 96(2): 281-287.
20.
Chen C. and Curliss D.Preparation, characterization, and nanostructural evolution of epoxy nanocomposites . J Appl Polym Sci2003; 90(8): 2276-2287.
21.
Qi B., Zhang QX, Bannister M. and Mai YWInvestigation of the mechanical properties of DGEBAbased epoxy resin with nanoclay additives. Compos Struct2006; 75(1-4): 514-519.
22.
Tsai JL and Hsu SMInvestigating mechanical properties of epoxy/organoclay nanocomposites. J Chin Inst Eng2008; 31(1): 9-16.
23.
Yasmin A., Luo JJ, Abot JL and Daniel IMMechanical and thermal behavior of clay/epoxy nanocomposites. Compos Sci Technol2006; 66(14): 2415-2422.
24.
Wang K., Chen L., Wu J., Toh ML, He C. and Yee FAEpoxy nanocomposites with highly exfoliated clay: mechanical properties and fracture mechanisms. Macromolecules2005; 38(3): 788-800.
25.
Kinloch AJ, Shaw SJ, Tod DA and Hunston DLDeformation and fracture behaviour of a rubber-toughened epoxy: 1. Microstructure and fracture studies. Polymer1983; 24(10): 1341-1354.
26.
Hwang JF, Manson A., Hertzberg RW, Miller GA and Sperling LHStructure-property relationships in rubber-toughened epoxies. Polym Eng Sci1989; 29(20): 1466-1476.
27.
Butta E., Levita G., Marchetti A. and Lazzeri A.Morphology and mechanical properties of amine-terminated butadiene-acrylonitrile/epoxy blends. Polym Eng Sci1986; 26(7): 63-73.
28.
Zeng Y., Zhang M., Penc W. and Yu Q.Microstructure, mechanical properties, and fracture behavior of liquid rubber toughened thermosets. J Appl Polym Sci1991 ; 42(7): 1905-1910.
29.
Haris A., Adachi T. and Araki W.Viscoelasticity and fracture toughness of blended epoxy resins containing two monomers with different molecular weights. J Mater Sci2008; 43(9): 3289-3295.
30.
Wu SJ, Lin TK and Shyu SSCure behavior, morphology, and mechanical properties of the melt blends of epoxy with polyphenylene oxide. J Appl Polym Sci1999; 75(1): 26-34.
31.
Kinloch AJ and Taylor ACThe mechanical properties and fracture behavior of epoxy-inorganic micro- and nano-composites. J Mater Sci2006; 41(11): 3271-3297.
32.
Brown EN, White SR and Sottos NRMicrocapsule induced toughening in a self-healing polymer composite. J Mater Sci2004; 39(5): 1703-1710.
33.
Azimi HR, Pearson RA and Hertzberg REFatigue of hybrid epoxy composites: epoxies containing rubber and hollow glass spheres. Polym Eng Sci1996; 36(18): 2352-2365.
34.
Lee J. and Yee AFInorganic particle toughening I: Micro-mechanical deformations in the fracture of glass bead filled epoxies. Polymer2001 ; 42(2): 577-588.
35.
Kornmann X., Thomann R., Khaupt MJ, Finter J. and Berglund LAHigh performance epoxy-layered silicate nanocomposites. Polym Eng Sci2002; 42(9): 1815-1826.
36.
Liu W., Hoa SV and Pugh M.Organoclay-modified high performance epoxy nanocomposites. Compos Sci Technol2005; 65(2): 307-316.
37.
Liu T., Tjiu WC, Tong Y., He C., Goh SS and Chung T.Morphology and fracture behavior of intercalated epoxy/ clay nanocomposites . J Appl Polym Sci2004; 94(3): 1236-1244.
38.
Zerda AS and Lesser AJIntercalated clay nanocomposites: morphology, mechanics, and fracture behavior . J Polym Sci, Part B: Polym Phys2001; 39(11): 1137-1146.
39.
Swaminathan G.Development of nanofiller-reinforced epoxy resins and their dynamic and fracture properties, PhD Thesis, NC A&T State University, Greensboro, NC, USA, 2009.
40.
Swaminathan G. and Shivakumar KNA re-examination of DMA testing of polymer matrix composites. J Reinf Plast Compos2009 ; 28(8): 979-994.
41.
Astm.Standard test methods for plane-strain fracture toughness and strain energy release rate of plastic materials. In: Annual book of ASTM standards, 8.03West Conshohocken, PA, USA: ASTM International, 2000.
Miyagawa H. , Rich MJ and Drzal LTAmine-cured epoxy/clay nanocomposites. II. The effect of the nanoclay aspect ratio. J Polym Sci, Part B: Polym Phys2004; 42(23): 4391-4400.
44.
Seo KS and Kim DSCuring behavior and structure of an epoxy/clay nanocomposite system. Polym Eng Sci2006; 49(9): 1318-1325.
45.
Gledhill RA and Kinloch AJMechanics of crack growth in epoxide resins . Polym Eng Sci1979; 19(2): 82-88.