This study focuses on the analysis of influence of temperature and bolt torque on aeronautical joint behavior. A single-lap joint, according to ASTM D5961, with a titanium bolt and composite plates was considered. A numerical model based on FEM was developed to evaluate the stress in both bolt and composite plates. Load—displacement curves, stress fields, and induced damage showed, significantly, the influence of temperature combined with torque level on the joint. It was found that in the plate, both maximum and minimum levels of torque considered produced damage above critical threshold. This fact should be accounted for, during the design process of the joint.
Xiao Y. and Ishikawa T.Bearing strength and failure behavior of bolted composite joints, part I: experimental investigation. Compos Sci Technol2005; 65(7-8): 1022-1031.
2.
Thoppul SD, Finegan J. and Gibson RFMechanics of mechanically fastened joints in polymer-matrix composite structures - a review. Compos Sci Technol2005; 69(3-4): 301-329.
3.
Park H.-J. Bearing failure analysis of mechanical fastened joints in composite laminates . Compos Struct2001; 53: 199-211.
4.
Kelly G. and Hallstrom S.Bearing strength of carbon fibre/ epoxy laminates: effects of bolt-hole clearance . Composites Part B2004; 35(4): 331-343.
5.
McCarthy CT, McCarthy MA, Stanley WF and Lawlor VPExperiences with modeling friction in composite bolted joints. J Compos Mater2005; 39(21): 1881-1908.
6.
McCarthy MA, Lawlor VP, Stanley WF and McCarthy CTBolt-hole clearance effects and strength criteria in single-bolt, single-lap, composite bolted joints. Compos Sci Technol2002; 62(10-11): 1415-1431.
7.
Thomas FP and Zhao Y.Torque limit for composites joined with mechanical fastener. In: 46th AIAA/ASME/ ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference, Austin, Texas, 18-21 April 2005, pp. 18-21.
8.
Chutima S. and Blackie APEffect of pitch distance, row spacing, end distance and bolt diameter on multi-fastened composite joints. Composites Part A1996; 27(2): 105-110.
9.
Scarponi C., Marini G. and Montanari P.The importance of the temperature and lateral pressure on the CFRP joints strength under uniaxial loading. J Reinf Plast Compos1997; 16(9): 825-847.
10.
Camanho PP and Matthews FLA progressive damage model for mechanically fastened joints in composite laminates . J Compos Mater1999; 33(24): 2248-2280.
11.
Ekh J. and Schön J.Effect of secondary bending on strength prediction of composite, single shear lap joints. Compos Sci Technol2005; 65(6): 953-965.
12.
Sánchez-Sáez S., Barbero E. and Navarro C.Analysis of the dynamic flexural behaviour of composite beams at low temperature. Compos Sci Technol2007; 67(11-12): 2616-2632.
13.
Sánchez-Sáez S., Barbero E. and Navarro C.Compressive residual strength at low temperatures of composite laminates subjected to low-velocity impacts. Compos Struct2007; 85(3): 226-232.
14.
Hirano N., Takao Y. and Wang WXEffects of temperature on the bearing strength of CF/epoxy pinned joints. J Compos Mater2007; 41(3): 335-351.
15.
Turvey GJ and Wang P.Thermal preconditioning study for bolted tension joints in pultruded GRP plate . Compos Struct2007; 77(4): 509-513.
16.
Song MH, Kweon JH, Kim SK, et al. An experimental study on the failure of carbon/epoxy single lap riveted joints after thermal exposure. Compos Struct2008; 86(1-3): 125-134.
17.
Song MH, Kweon JH, Kim SK, et al. Standard test method for bearing response of polymer matrix composite laminates. West Conshohocken, PA: ASTM International, 2005.
18.
Soden PD, Hinton MJ and Kaddour ASLamina properties, lay-up configurations and loading conditions for a range of fibre-reinforced composite laminates. Compos Sci Technol1998; 58(7): 1011-1022.
19.
Abaqus explicit user’s manual. Version 6.5 edition. Hibbitt, Karlson & Sorensen Inc. HKS, 2005.
20.
Ekh J. and Schon J.Load transfer in multirow, single shear, composite-to-aluminium lap joints . Compos Sci Technol2006; 66: 875-885.
21.
Chen WH, Lee SS and Yeh JTThree-dimensional contact stress analysis of a composite laminate with bolted joint. Compos Struct1995; 30(3): 287-297.
22.
Hashin Z. and Rotem A.A fatigue criterion for fiber-reinforced materials. J Compos Mater1973; 7: 448-464.