In this study, the kiln-dried oil palm trunk (OPT) was impregnated with phenol formaldehyde (PF) and urea formaldehyde (UF) resin as a matrix using high-pressure vaccum impregnation chamber. Different percentages of resin were loaded in oil palm trunk lumber (OPTL) and compared with kiln-dried OPT and rubberwood (RW). The physical, mechanical, and environmental properties were studied according to BS and ASTM standards. The morphology of resin-loaded OPTL was analyzed by scanning electron microscopy (SEM), while thermal characterization was carried out by thermogravimetric analysis. In general, the OPTL exhibited better values of physical and mechanical properties than dried OPT and OPTL (50% resin loading), which were slightly lower than RW; however, OPTL exhibited good thermal stability compared with dried OPT and RW. Furthermore, the OPTL exhibited a high resistance against termites. The observation of SEM micrograph showed that OPTL with PF resin loading exhibited better morphology than OPTL with UF resin loading, and full penetration of resin into OPT structures was observed.
Razak W., Hasyim WS, Aminuddin M., Othman S. and Rafidah S.Properties of veneers lumber from oil palm trunk. J Plant Sci2008; 3: 255-259.
2.
Mokhtar A., Hassan K., Aziz AA and Wahid MBTreatment of oil palm lumber. MPOB Information Series2008; 379.
3.
Abdul Khalil HPS , Bhat AH, Jawaid M., Parisa A., Ridzuan R. and Said MRAgro-wastes: mechanical and physical properties of resin impregnated oil palm trunk core lumber. Polym Compos2009; 31: 638-644.
4.
Flood J., Keenan L., Wayne S. and Hasan Y.Studies on oil palm trunks as sources of infection in the field. Mycopathologia2005; 159: 101-107.
5.
Abdul Khalil HPS , Hanida S. and Kang CWAgrohybrid composite: the effects on mechanical and physical properties of oil palm fiber (EFB)/glass hybrid. J Reinf Poly Compos2007; 26: 203-218.
6.
Lim SC and Gan KSCharacteristics and utilisation of oil palm stem. Timber Technol Bull2005; 53: 1-11.
7.
Othman S., Hashim R., Raza KW, Hashim WS and Azmy M.Evaluation on some finishing properties of oil palm plywood. Holz Roh Werkst2008; 66: 5-10.
8.
Abdul Khalil HPS , Nurul Fazita MR, Bhat AH, Jawaid M. and Nik Fuad NADevelopment and material properties of new hybrid plywood from oil palm biomass. Mater Des2010; 31: 417-424.
9.
Sreekala MS, Jayamol G., Kumaran MG and Thomas S.The mechanical performance of hybrid phenol-formaldehyde-based composites reinforced with glass and oil palm fibres. Compos Sci Technol2002; 62: 339-353.
10.
Abdul Khalil HPS , Ismail H., Ahmad MN, Ariffin A. and Hassan K.The effect of various anhydride modification on mechanical and water absorption properties of oil palm empty fruit bunches reinforced polyester composites. Polym Int2001; 50: 1-9.
11.
Henson IEComparative ecophysiology of oil palm and tropical rain forest. In: Singh G, Huan LK , Leng T and Kow DL (eds) Oil palm and the environment: a Malaysian perspective . Kuala Lumpur, Malaysia: Malaysian Oil Palm Growers’ Council, 1999, p.9-39.
12.
Edi Suhaimi B. , Paridah MT, Fauzi F., Hamami SM and Tang WCProperties enhancement through modified compreg method: a comprehensive solution to oil palm wood’s properties flaws . In: Proceedings of the 7th National Seminar on the Utilization of Oil Palm Tree. Kuala Lumpur, Malaysia: Oil Palm Tree Utilization Committee (OPTUC), 2008, p.99-112.
13.
Erwinsyah.Improvement of oil palm wood properties using bioresin, PhD Thesis, Technische UniversitätDresden, German, 2008.
14.
Bakar ES, Massijaya MY, Tobing LL and Makmur A.Utilization of oil-palm trees as building and furniture materials (III): treatability of oil palm wood with Basilit-CFK and Impralit-B1. Indonesian J For Prod Technol1999; 11: 13-20.
15.
Furuno T., Imamura Y. and Kajita H.The modification of wood by treatment with low molecular weight phenolformaldehyde resin: a properties enhancement with neutralized phenolic-resin and resin penetration into wood cell walls. Wood Sci Technol2004; 37: 349-361.
16.
Shams MI, Yano H. and Endou K.Compressive deformation of wood impregnated with low molecular weight phenol formaldehyde (PF) resin I: effects of pressing pressure and pressure holding . J Wood Sci2004; 50: 337-342.
17.
Hashim R., Boon JG, Sulaiman O., Kawamura F. and Lee CYEvaluation of the decay resistance properties of Cerbera odollam extracts and their influence on properties of particleboard 63. Int Biodet Biodeg2009; 63: 1013-1017.
18.
Ngee PS, Tashiro A., Yoshimura T., Jaal Z. and Lee CYWood preference of selected Malaysian subterranean termites (Isoptera: Rhinotermitidae, Termitidae). Sociobiology2004; 43: 535-550.
19.
Anthony HCUrea formaldehyde adhesives resins. Polymeric materials encyclopedia1996; 11: 8497-8501.
20.
Thanate R., Tanong C. and Sittipon K.An investigation on the mechanical properties of trunks of palm oil trees for the furniture industry. J Oil Palm Res2006; special issue: 114-121.
21.
Paridah MT and Anis M.Process optimization in the manufacturing of plywood from oil palm trunk. In: Proceedings of the 7th National Seminar on the Utilization of Oil Palm Tree, Kuala Lumpur, Malaysia, Oil Palm Tree Utilization Committee (OPTUC), 1998, p.12-24.
22.
Hoilifinger MS, Conner AH, Lorenz LF and Hill CGDifurfuryl diisocyanates - new adhesives derived from renewable sources. J Appl Polymr Sci1993; 49: 337-344.
23.
Sain MM, Ghosh A. and Banik I.Fiberboard composites from wood-fiber bonded with renewable wood resin . J Reinf Plast Compos2006; 35: 1701-1708.
24.
Joseph S., Sreekala MS, Oommen Z., Koshy P. and Thomas S.A comparison of mechanical properties of phenol formaldehyde composites reinforced with banana fibres and glass fibres. Compos Sci Technol2002; 62: 1857-1868.
25.
Marcovich NE , Reboredo MM and Aranguren MIModified wood flour as thermoset fillers II. Thermal degradation of woodflours and composites . Thermochim Acta2001; 372: 45-57.