Effect of Particle Size and Alkali Treatment of Sugarcane Bagasse on Thermal,Mechanical,and Morphological Properties of PVC-Bagasse Composites

Abstract

This article evaluates the use of bagasse flour — a waste generated by sugarcane refinery—as a filler in the PVC matrix. The aim of the study is to develop a value-added product from the sugar mills. For this purpose, bagasse powder was obtained after grinding the dried waste from sugar mills having particle sizes of 100—150 µm and <50 µm. In order to evaluate the effect of filler content and alkali treatment of bagasse, several PVC formulations were obtained by dry-mixing PVC compound with filler of varying particle size. The compounds were obtained by blending on a hot roll mill followed by compression molding. The test specimens were punched out from the sheets and the effect of filler content, particle size, and alkali treatment of bagasse powder on the properties of PVC were evaluated. Tensile strength, percent elongation at break, and impact strength of composites decreased whereas stiffness, modulus, and hardness of the composites increased with increasing amount of filler. The particle size had a large effect on the properties of composites, and the filler having particle size <50 µm gave better properties as compared to filler with particle size of 100—150 µm. Some improvement in properties was observed when treated bagasse powder was used as filler. An increase of ∼48% in tensile modulus, ∼10% in thermal stability, and 14% in impact strength was observed as compared to neat PVC at a filler loading of 30 phr. Morphological characterization was done using a scanning electron microscopy. A uniform dispersion of filler was observed.

Keywords

polymer composites bagasse powder morphology PVC mechanical properties.

Get full access to this article

View all access options for this article.

References

Schut, J.H. ( 1999). For Compounding, Sheet & Profile, Wood is Good, Plastics Technology, March: 46-52.

Wolcott, M.P. and Smith, M.S. ( 2004). Opportunities and Challenges for Wood Plastic Composites in Structural Applications, In: Proceeding of Progress in Wood Fiber-Plastic Composites Conference, pp. 1-10, Toronto , Canada.

Saheb, D. and Jog, J. ( 1999). Natural Fiber Polymer Composites: A Review, Advances in Polymer Technology, 18: 351-363.

Morton, J. , Quarmley, J. and Rossi, L. ( 2003). Currest and Emerging Applications for Natural and Wood Fiber-Plastic Composites, In: Seventh International Conference on Wood Fiber-Plastic Composites, pp. 3-6, Madison, WI, USA.

Tajvidi, M. and Ebrahimi, G.H. ( 2003). Water Uptake and Mechanical Characteristics of Natural Filler Polypropylene Composites, Journal of Applied Polymer Science, 88: 941-946.

Chaudhary, D.S. and Jollands, M.C. (2004). Recycling Rice Hull Ash: A Filler Material for Polymeric Composites, Advances in Polymer Technology, 23: 147-155.

Swamy, R.N. ( 1990). Proceedings 2nd International Symposium on Vegetable Plants and their Fibers as Building Materials, Rilem Proceedings 7, pp. 3-8, Chapman and Hall, London.

Roger, M.R. ( 1998). Property Enhanced Natural Fiber Composite Materials based on Chemical Modification, In: Science and Technology of Polymers and Advanced Materials, pp. 717-732.

Belgacem, M.N. and Gandini, A. (2005). The Surface Modifications of Cellulose Fibres for use as Reinforcing Elements in Composite Materials , Composite Interfaces, 12: 41-75.

10.

Sain, M. , Suhara, P. and Law, S. ( 2005). Interface Modification and Mechanical Properties of Natural Fiber-Polyolefin Composite Products, Journal of Reinforced Plastic and Composites, 24: 121-130.

11.

Moldas, D. and Kokta, B. ( 1992). Performance of Hybrid Reinforcements in PVC Compoistes: III. Use of Surface Modified Glass Fiber and Wood Pulp as Reinforcements, Journal of Reinforced Plastics and Composites, 2: 1093-1102.

12.

Gassan, J. and Bledzki, A.K. ( 1999). Possibilities for Improving the Mechnaical Properties of Jute/Epoxy Composites by Alkali Treatment of Fibers, Composite Science Technology, 59: 1303-1309.

13.

Oksman, K. and Clemons, C. ( 1998). Mechanical Properties and Morphology of Impact Modified Polypropylene-Wood Flour Composites, Journal of Applied Polymer Science, 6: 1503.

14.

Bengtsson, M. , Gatenholm, P. and Oksmanm, K. (2005). The Effect of Cross Linking on the Properties of Polyethylene/Wood Flour Composites, Composite Science Technology 65: 1468-79.

15.

Jiao, C. , Wang, Z. , Liang, X. and Hu, Y. ( 2005). Non-isothermal Crystallization Kinetics of Silane Cross Linked Polyethylene, Polymer Test, 24: 71-80.

16.

Ramaraj, B. (2007). Mechanical and Thermal Properties of Polypropylene/Sugarcane Bagasse Composites, Journal of Applied Polymer Science, 103: 3827-3832.

17.

Mothe, C.G. , Araujo, C.R. and Oliveira, M.A. (2002). Thermal Decomposition Kinetics of Polyurethane Composites with Bagasse of Sugar, Journal of Thermal Analysis and Calorimetric, 67: 305-312.

18.

Edgar, G.H. , Angel, L.C. and Artiro, Z. (2004). Improvement of Interfacial Compatibility Between Sugar Cane Bagasse Fibers and Polystyrene for Composites , Polymer Composites, 2: 134-145.

19.

Aiello, C. , Ferrer, A. and Ledesma, A. ( 1996). Effect of Alkaline Pretreatment at Various Temperatures on Cellulase and Biomass Production using Submerged Sugarcane Bagasse Fermentation with Trichoderma Reesei QM-9414, Bioresource Technology, 57: 13-16.

20.

Saha, A.K. , Das, S. , Bhatta, D. and Mitra, B.C. ( 1998). Study of Jute Fiber Reinforced Polyester Composites by Dynamic Mechanical Analysis, Journal of Applied Polymer Science , 71: 1505-1513.