Delaminated Woven Fabric Composite Plates under Transverse Quasi-Static Loading: Experimental Studies

Abstract

Laminated composite plates are very sensitive to transverse loading because of weak interfaces between layers. During transverse loading, delamination can initiate and propagate at the interfaces. Also, in-plane failure of layers can initiate and grow further because of the in-plane stresses. Such damages can cause severe structural disintegration leading to a reduction in stiffness and strength. The delamination may be caused by manufacturing defects also. Such delamination can grow during service condition. Experimental studies have been carried out on the damage evolution in a typical plain weave fabric composite plate under transverse quasi-static loading. Studies have been carried out on composite plates with central artificial delamination of 5 mm, 10 mm and 15 mm diameter sizes, and also on undelaminated composite plates. Load-displacement behavior, damage evolution and damage sizes and damage shapes have been studied.

Keywords

composite plate plain weave fabric artificial delamination in-plane failure damage propagation quasi-static loading experimental study

Get full access to this article

View all access options for this article.

References

1. Lu, X. and D. Liu . 1991. “Finite Element Analysis of Strain Energy Release Rate at Delamination Front,” Journal of Reinforced Plastics and Composites, 10:279-293.

2. Doxsee, L. E. , P. Rubberecht , L. Li and L. Verpoest . 1993. “Delamination Growth in Composite Plates Subjected to Transverse Loads,” Journal of Composite Materials, 27:764-782.

3. Razi, B. and A. S. Kobayashi . 1993. “Delamination in Cross-Ply Laminated Composite Subjected to Low-Velocity Impact,” AIAA Journal, 31:1498-1502.

4. Chen, D. J. , W. S. Chan and B. P. Wang . 1996. “An Efficient Method to Simulate One and Two-Dimensional Delamination Growth in Composite Laminates,” Journal of Reinforced Plastics and Composites, 15:944-957.

5. Kamiya, S. , H. Sekine and Y. Yagishita . 1998. “Computational Simulation of Interlaminar Crack Extension in Angle-Ply Laminates due to Transverse Loading,” Journal of Composite Materials, 32:744-762.

6. Stout, M. G. , D. A. Koss , C. Liu and J. Idasetima . 1999. “Damage Development in Carbon/Epoxy Laminates under Quasi-Static and Dynamic Loading,” Composites Science and Technology, 59:2339-2350.

7. Pradhan, B. and D. Chakraborty . 2000. “Fracture Behaviour of FRP Composite Laminates with an Embedded Elliptical Delamination at the Interface,” Journal of Reinforced Plastics and Composites, 19:1004-1023.

8. Lammerant, L. and I. Verpoest . 1996. “Modeling of the Interaction between Matrix Cracks and Delamination during Impact of Composite Plates,” Composites Science and Technology, 56:1171-1178.

9. Naik, N. K. , Y. Chandra Sekher and M. Sailendra . 2000. “Polymer Matrix Woven Fabric Composites Subjected to Low Velocity Impact: Part I—Damage Initiation Studies,” Journal of Reinforced Plastics and Composites, 19:912-954.