Damage Evolution in Woven Fabric Composites: Transverse Static Loading

Abstract

Studieshave been carried out on the damage evolution in a typical plain weave fabric composite under transverse central static loading. The stress state has been evaluated throughout the composite plate using finite element analysis software. Possible failure of layers because of in-plane stresses and the delamination mode of failure at the interfaces because of interlaminar stresses have been monitored. It hasbeen observed that the damage initiation and propagation is because of in-plane stresses. The shape of the damage is quasi-lemniscate. Experimental studies have been carried out on a typical plain weave fabric E-glass–epoxy laminate. There is a good match between the predicted and the experimentally observed damage shapes and sizes.

Keywords

woven fabric composite plain weave fabric transverse static loading in-plane failure

Get full access to this article

View all access options for this article.

References

1. Lu, X. and Liu, D. (1991). Finite Element Analysis of Strain Energy Release Rate at Delamination Front, Journal of Reinforced Plastics and Composites, 10: 279–293.

2. Doxsee, L.E. , Rubberecht, P. , Li, L. and Verpoest, L. (1993). Delamination Growth in Composite Plates Subjected to Transverse Loads, Journal of Composite Materials, 27: 764–782.

3. Razi, B. and Kobayashi, A.S. (1993). Delamination in Cross-Ply Laminated Composite Subjected to Low-Velocity Impact, AIAA Journal, 31: 1498–1502.

4. Chen, D.J. , Chan, W.S. and Wang, B.P. (1996). An Efficient Method to Simulate One and Two-Dimensional Delamination Growth in Composite Laminates, Journal of Reinforced Plastics and Composites, 15: 944–957.

5. Kamiya, S. , Sekine, H. and Yagishita, Y. (1998). Computational Simulation of Interlaminar Crack Extension in Angle-Ply Laminates Due to Transverse Loading, Journal of Composite Materials, 32: 744–762.

6. Stout, M.G. , Koss, D.A. , Liu, C. and Idasetima, J. (1999). Damage Development in Carbon/Epoxy Laminates Under Quasi-Static and Dynamic Loading, Composites Science and Technology, 59: 2339–2350.

7. Pradhan, B. and Chakraborty, D. (2000). Fracture Behaviour of FRP Composite Laminates with an Embedded Elliptical Delamination at the Interface, Journal of Reinforced Plastics and Composites, 19: 1004–1023.

8. Jones, R.M. (1999). Mechanics of Composite Materials, Taylor & Francis Ltd., London.

9. Brewer, J.C. and Lagace, P.A. (1988). Quadratic Stress Criterion for Initiation of Delamination, Journal of Composite Materials, 22: 1141–1155.

10.

10. Naik, N.K. , Chandra Sekher, Y. and Sailendra, M. (2000). Polymer Matrix Woven Fabric Composites Subjected to Low Velocity Impact: Part I–Damage Initiation Studies, Journal of Reinforced Plastics and Composites, 19: 912–954.

11.

11. Lammerant, L. and Verpoest, I. (1996). Modeling of the Interaction Between Matrix Cracks and Delamination During Impact of Composite Plates, Composites Science and Technology, 56: 1171–1178.