In industrial practice, it is known that the wire rod coils need to be descaled before drawing. Acid pickling by hydrochloric or sulphuric acidic solutions is the most common method. However, mechanical descaling could be preferred. According to this choice, the oxides type and morphology shall be different. The oxides nature can be controlled by the Stelmor parameters, that is, the temperature at the laying head and the cooling rate on the Stelmor conveyor. International standards and customer specifications prescribe precise requirements not only for the scale features, but also for the material mechanical resistance and deformability. So, a complicated plant set-up is needed to satisfy all the requirements. This research work is aimed at developing processing maps for the correct selection of the Stelmor parameters able to guarantee the required mechanical strength and surface scale suitable for acid pickling or mechanical descaling.
YoungD. High temperature oxidation and corrosion of metals. Oxford: Elsevier, 2008.
3.
ChenRYYuenWYD. Examination of oxide scales of hot rolled strips products. ISIJ International, 2005; 45(1).
4.
ChenRYYuenWYD. Oxide scales structure formed on commercial hot-rolled steel strip and their formation mechanism. Oxid Met2001; 56: 89–118.
5.
CampbellPCHawboltEBBrimacombeJK. Microstructural engineering applied to the controlled cooling of steel wire rod: Part I. Experimental design and heat transfer. Metall Trans A1991; 22: 2769–2778.
6.
ZorcMNagodeABurjaJ, et al.Surface decarburization of the hypo-eutectoid carbon steel C45 during annealing in steady air at temperatures T > AC1. Metals2018; 8: 25.
7.
GesmundoFVianiFNiuY. The possible scaling modes in the high temperature oxidation of two-phase binary alloys. Part I: High oxidant pressures. Oxid Met1994; 42: 409–429.
8.
GesmundoFVianiFNiuY. The possible scaling modes in the high temperature oxidation of two-phase binary alloys. Part II: Low oxidant pressures. Oxid Met1995; 43: 379–394.
9.
RivoltaB, et al.Influence of prior microstructure on the mechanical and microstructural properties of C–Mn–B steel after spheroidizing annealing. Ironmaking Steelmaking2021; 48: 1013–1021.
10.
RivoltaB, et al.Spheroidizing annealing of thermomechanically hot-rolled steel rods: Influence of the prior microstructure on the mechanical characteristic and phase transformations. Ironmaking Steelmaking2022; 49: 716–725.
11.
RivoltaB, et al.Reverse aging of pearlitic carbon steel wire rod. Ironmaking Steelmaking2023; 50: 630–636.
12.
CornellRMSchwertmannU. The iron oxides. Weinheim, Germany: VCH, 1996, p. 458.
13.
TominagaJWakimotoK-yMoriT, et al.Manufacture of wire rods with good descaling property. Trans ISIJ1982; 22: 646–656.
14.
ChenCSunMWangB, et al.Recent advances on drawing technology of ultra-fine steel tire cord and steel saw wire. Metals2021; 11: 1590.
15.
GillstromPJarlM. Mechanical descaling of wire rod using reverse bending and brushing. J Mater Process Technol2006; 172: 332–340.
16.
ChattopadhyayAKumarPRoyaD. Study on formation of “easy to remove oxide scale” during mechanical descaling of high carbon wire rods. Surf Coat Technol2009; 203: 2912–2915.
17.
EN ISO 16120-2, Non-alloy steel wire rod for conversion to wire – Part 2: Specific requirements for general purpose wire rod.
18.
EN ISO 16120-4, Non-alloy steel wire rod for conversion to wire – Part 4: Specific requirements for wire rod for special applications.
19.
ChenRYYuenWYD. Review of the high-temperature oxidation of iron and carbon steels in air or oxygen. Oxid Met2003; 59: 433–468.
20.
ChenRYYuenWYD. A study of the scale structure of hot-rolled steel strip by simulated coiling and cooling. Oxid Met2000; 53: 539–560.
21.
VillarsPCalvertLD. Pearson's handbook of crystallographic data for intermetallic phases. New York: ASM International,1991, vol. 3, pp. 3327–3329.
22.
BhattacharyaRJhaGKunduS, et al.Influence of cooling rate on the structure and formation of oxide scale in low carbon steel wire rods during hot rolling. Surf Coat Technol2006; 201: 526–532.
23.
CaoG-mWUT-zRongXU, et al.Effects of coiling temperature and cooling condition on transformation behavior of tertiary oxide scale. J Iron Steel Res Int2015; 22: 892–896.
24.
BiroscaSWestGDHigginsonRL. Microstructural investigation of the oxide scale of low carbon steel. Metal, 2005: 1–8.
25.
BiroscaS. Phase determination and microstructure of oxide scales formed on steel at high temperature. J Microsc2004: 122–129.
26.
MalikAU , WhittleDP. Oxidation of Fe–C alloys in the temperature range 600/850 °C. Oxid Met1981; 16.
27.
BaudJFerrierAManencJ. Study of magnetite film formation at metal-scale interface during cooling of steel products. Oxid Met1978; 12.
28.
DengGYZhuQTieuK, et al.Evolution of microstructure, temperature and stress in a high speed steel work roll during hot rolling: Experiment and modelling. J Mater Process Technol2017; 240: 200–208.
29.
DengGYZhuHTTieuAK, et al.Theoretical and experimental investigation of thermal and oxidation behaviours of a high speed steel work roll during hot rolling. Int J Mech Sci2017; 131–132: 811–826.
30.
DengGYTieuAKSuLH, et al.Characterizing deformation behaviour of an oxidized high speed steel: effects of nanoindentation depth, friction and oxide scale porosity. Int J Mech Sci2019; 155: 267–285.
31.
DengGYTieuAKSuLH, et al.Microstructural study and residual stress measurement of a hot rolling work roll material during isothermal oxidation. Int J Adv Manuf Technol2019; 102: 2107–2118.
32.
ISO 6507-1:2018, Metallic materials – Vickers hardness test – Part 1: Test method.
33.
ISO 6892-1, Metallic materials – Tensile testing – Part 1: Method of test at room temperature.