Manufacturing and characterization of open-cell aluminum foam by powder metallurgy

Abstract

Metallic foams are classified into two groups based on their pore structure: closed and open pores. The variability of cell structures directly depends on the production method and the variability of parameters. Open – cell metallic foams are used as heat exchangers due to their large surface area, in filters and separators due to their properties such as high liquid/gas permeability and corrosion resistance, and in water purifiers to reduce the concentration of unwanted ions dissolved in water because they can provide liquid flow, and in silencers due to their sound absorbing feature. Due to their thermal conductivity, they are generally used in functional applications such as catalyst supports and flame arresters. In this study, open cell aluminum foams with different pore sizes were produced using the powder metallurgy method and polyurethane foam (PUF) replica technique. After the PUF model material of the foams was removed at 500 °C for 6 h, they were sintered at different temperatures such as 850, 900 and 950 °C for 6 h. Density measurement, XRD analysis, microstructure examination and compression testing were applied to the sintered open-cell foams. The highest pore ratio and compressive strength were determined in foams with a 20 ppi (porosity per inch) pore ratio sintered at 950 °C.

Keywords

open cell foam powder metallurgy metallic foam porosity compressive strength

Get full access to this article

View all access options for this article.

References

Sunar

. Production of open cell aluminum foam and development of it’s properties . PhD Thesis, 2019, pp.1–25.

Kalkan

. Production of open cell aluminum foam by vacuum casting method . MSc Thesis, Afyon Kocatepe University, Institute of Science and Technology, 2012, pp.1–12.

Özer

. Aluminum based foam metal production . MSc Thesis, Yıldız Technical University, Institute of Science and Technology, 2005, pp.12–26.

Banhart

. Manufacture, characterisation and application of cellular metal and metal foams. Prog Mater Sci 2000; 46: 559–632, 587–588.

Banhart

. Foam metal the recipe. Europhys News 1999; 30: 17–20.

Banhart

Baumeister

. Deformation characteristics of metal foams. J Mater Sci 1998; 33: 1431–1440.

Jozić

Lela

Krolo

, et al. Production of open-cell metal foams by recycling of aluminum alloy chips. Materials 2023; 16: 3930.

Banhart

Weaire

. On the road again: metal foams find favor. Phys Today 2002; 55: 37–42.

Gibson

. Mechanical behavior of metallic foams. Annu Rev Mater Sci 2000; 30: 191–227.

10.

Jiang

Zhao

Shi

, et al. A novel method for making open cell aluminum foams by powder sintering process. Mater Lett 2005; 59: 3333–3336.

11.

Sutygina

Betke

Scheffler

. Open-cell aluminum foams by the sponge replication technique. Materials 2019; 12: 3840.

12.

Zaman

. Production and characterization of open cell aluminum . MSc Thesis, Istanbul Technical University, Institute of Science and Technology, 2011, pp.4–102.

13.

Montanaro

Jorand

Fantozzi

, et al. Ceramic foams by powder processing. J Eur Ceram Soc 1998; 18: 1339–1347.

14.

Blitterswijk

CAV

Groot

. Factors having influence on the rheological properties of Ti6Al4V slurry. J Mater Sci: Mater Med 2004; 15: 951–958.

15.

Zhu

Jiang

Tan

. Reaction bonding of open cell SiC-Al2O3 composites. Mater Res Bull 2001; 36: 2003–2015.

16.

Sutygina

Betke

Scheffler

. Open-Cell aluminum foams by the sponge ReplicationTechnique: a starting powder particle study. Adv Eng Mater 2020; 22: 1901194..

17.

Pei

Zhou

Zhao

, et al. Low-temperature synthesis of α-Al2O3 single crystal platelets by one-step thermal decomposition of al-urea complex. J Therm Anal Calorim 2023; 148: 8841–8848..

18.

Kaya

. Effects of the cell number and anisotropy in the open cell metal foams on the energy absorption efficiency. Pamukkale Univ J Eng Sci 2020; 26: 45–50.