Influence of microstructure in nitrile polymer on curing characteristics and mechanical properties of carbon black-filled rubber composite for seal applications

Abstract

Acrylonitrile butadiene rubber (NBR) is widely used in seal applications due to its excellent oil resistance. In this article, carbon black-filled NBR composites, which differed in their acrylonitrile (ACN) and butadiene content ratios, were prepared and their curing characteristics and mechanical properties were investigated. Curing characteristics were investigated by measuring chemical kinetics and onset temperature of cross-linking reaction. Cross-linking density was measured by the volume swelling test. Mechanical properties, oil resistance, and compression set (CS) tests were also conducted. From these results, it was found that the microstructure in NBR polymer is closely connected to the curing characteristics and mechanical properties of the composite. On increasing the ACN content, Shore A hardness, tensile strength at break, elongation at break, oil resistance, and CS were raised, while, on the other hand cross-linking density, kinetics of cross-linking reaction, and bound rubber content were decreased.

Keywords

NBR rubber microstructure curing behavior bound rubber mechanical property

Get full access to this article

View all access options for this article.

References

Mofidi

Kassfeldt

Prakash

. Tribological behavior of an elastomer aged in different oils. Tribol Int 2008; 41: 860–866.

Guan

Yang

Wang

. Study on evaluation index system of rubber materials for sealing. Mater Des 2011; 32: 2404–2412.

Bhowmick

Stephens

. Handbook of elastomers. New York: Marcel Dekker, 2001.

Yasin

Ahmed

Makkuchi

. Effect of acrylonitrile content on physical properties of electron beam irradiated acrylonitrile butadiene rubber. React Funct Polym 2003; 57: 113–118.

Palaty

Joseph

. Low temperature curing of NBR for property improvement. J Elastom Plast 2006; 38: 199–209.

Dick

. Rubber technology: compounding and testing for performance. Munich: Hanser publisher, 2001.

Choi

Kim

. Lifetime prediction and thermal aging behaviors of SBR and NBR composites using crosslink density changes. J Ind Eng Chem 2012; 18: 1166–1170.

Frohlich

Niedermeier

Luginsland

. The effect of filler–filler and filler–elastomer interaction on rubber reinforcement. Compos A 2005; 36: 449–460.

Sreeja

Najidha

Jayan

. Electro-optic material from co-polymeric elastomer-acrylonitrile butadiene rubber (NBR). Polymer 2006; 47: 617–623.

10.

Maurice

Rubber technology third edition. Netherlands: Kluwer Academic Publishers, 1999.

11.

Choi

Kim

. Influence of aging media and filler system on recovery behaviors of natural rubber composites. Elast Compos 2012; 47: 156–161.

12.

Choi

Kim

. Filler–polymer interactions in filled polybutadiene compounds. Eur Polym J 2002; 38: 1265–1269.

13.

Yasin

Ahmed

Yoshii

. Effect of acrylonitrile content on physical properties of electron beam irradiated acrylonitrile-butadiene rubber. React Funct Polym 2003; 57: 113–118.

14.

Duin

Dikland

. A chemical modification approach for improving the oil resistance of ethylene propylene copolymers. Polym Degrad Stabil 2007; 92: 2287–2293.

15.

Mostafa

Abouel-Kasem

Bayoumi

. Effect of carbon black loading on the swelling and compression set behavior of SBR and NBR rubber compounds. Mater Des 2009; 30: 1561–1568.

16.

Rattanasom

Prasertsri

. Relationship among mechanical properties, heat aging resistance, cut growth behaviour and morphology in natural rubber: partial replacement of clay with various types of carbon black at similar hardness level. Polym Test 2009; 28: 270–276.

17.

George

Knorgen

Thomas

. Effect of nature and extent of crosslinking on swelling and mechanical behavior of styrene-butadiene rubber membranes. J Membr Sci 1999; 163: 1–17.