Steel fibre–silicone rubber composites were prepared by two-roll mill method. Various weight fractions of fibres ranging from 20 phr (parts per hundred parts of rubber) to 90 phr, with a diameter of 7–8 μm and length of several metres were used and its influence on the surface resistance, physical properties, short-term and dynamic stress–strain properties of the composites were investigated. Addition of steel fibres renders a sharp decrease in resistance from MΩ to ~3–0.1 kΩ with the concentration from 20 phr to 90 phr, respectively. Addition of 20 phr of steel fibres yields composite with a resistance of 5–10 kΩ, other properties being negligibly altered.
XuQPangMZhuLZhangYFengS. Mechanical properties of silicone rubber composed of diverse vinyl content silicone gums blending. Mater Des2010; 31: 4083–4087.
2.
ZhangJFengSY. Effect of cross linking on the conductivity of conductive silicone rubber. J Appl Polym Sci2003; 89: 3471–3475.
3.
TangYTsingR. Rheological, extractive and thermal studies of the room temperature vulcanized polydimethylsiloxane. Polymer1999; 40: 6135–6146.
4.
HeinerJStenbergBPerssonM. Crosslinking of siloxane elastomers. Polym Test2003; 22: 253–257.
5.
LingCLuLWuDChenG. Silicone rubber/graphite nanosheet electrically conducting nanocomposite with a low percolation threshold. Polym Compos2007; 28: 493–498.
6.
MeunierLChagnonGOrgeasLVacherP. Mechanical experimental characterisation and numerical modelling of an unfilled silicone rubber. Polym Test2008; 27: 765–777.
7.
ParkES. Mechanical properties and processibility of glassfiber-, wollastonite-, and fluoro-rubber-reinforced silicone rubber composites. J Appl Polym Sci2007; 105: 460–468.
8.
HanYMZhangJYYangQYJinRG. Novel polymethoxylsiloxane based crosslinking reagent and its in-situ improvement for thermal and mechanical properties of siloxane elastomer. J Appl Polym Sci2008; 107: 3788–3795.
9.
ParkES. Processibility and mechanical properties of micronized polytetrafluoroethylene reinforced silicone rubber composites. J Appl Polym Sci2008; 107: 372–381.
10.
LiuPBLiuDLZouHWXuW. Structure and properties of closed-cell foam prepared from irradiation crosslinked silicone rubber. J Appl Polym Sci2009; 113: 3590–3595.
11.
ParkES. Mechanical properties and antibacterial activity of peroxide-cured silicone rubber foams. J Appl Polym Sci2008; 110: 1723–1729.
12.
SoltaniaRKatbabAA. The role of interfacial compatibilizer in controlling the electrical conductivity and piezoresistive behavior of the nanocomposites based on RTV silicone rubber/graphite nanosheets. Sens Actuators A2010; 163: 213–219.
13.
YongJZhangHTianL. Investigation into electrical conductivity and electromagnetic interference shielding effectiveness of silicone rubber filled with Ag-coated cenosphere particles. Polym Test2010; 29: 609–612.
14.
PhamGT. PhD Thesis, Characterization and modeling of piezo-resistive properties of carbon nanotube-based conductive polymer composites Department of Industrial and Manufacturing Engineering, Florida State University, 2008.
15.
RamMYavuzOAldissiM. CO gas sensing from ultrathin nanocomposite conducting polymer film. Sens Actuators B2005; 106: 750–757.
16.
ZribiKFellerJFElleuchB. Conductive polymer composites obtained from recycled poly(carbonate) and rubber blends for heating and sensing applicationsPolym Adv Technol2006; 17: 727–731.
17.
WooCLimCChoCLeeSU. Fabrication of flexible and transparent single-wall carbon nanotube gas sensors by vacuum filtration and poly(dimethyl siloxane) mold transferMicroelectron Eng2007; 84: 1610–1613.
18.
HieroldCStampferCHelblingT. Nano electromechanical sensors based on carbon nanotubesSens Actuators A2007; 136: 51–61.
19.
ChenLLuLUWuDChenG. Silicone rubber/graphite nanosheet electrically conducting nanocomposite with a low percolation thresholdPolym Compos2007; 28: 493–498.
20.
ShermanRDMiddlemanLMJacobsSM. Electron transport process in conductor-filled polymersPolym Eng Sci1983; 23: 36–45.
ZhangYLuHFengS. The curing retardation and mechanism of high temperature vulcanizing silicone rubber filled with superconductive carbon blacksPolym Eng Sci2011; 51: 170–178.
23.
BhattacharyaSKKathirgamanathanPDekkerM. Metal - filled polymers. Polymer1986; 34: 2907–2908.
24.
GwailySENasrGMBadawyMM. Thermal and electrical properties of irradiated styrene butadiene rubber-metal compositesEgypt J Sol2001; 24(2): 193–205.
25.
BrownRP. Physical testing of rubber. 2nd edn. Londonand New York: Elsevier Applied Science Publishers, 1986, pp. 54–67.
26.
In: MortonM (ed) Rubber technology. 3rd edn. New York: Van Norstrand Reinhold Company Inc., 1987, pp. 134–140.
27.
SmithLP. The language of rubber. 1st edn. Oxford: Butterworth–Heinemann Ltd, 1993, pp. 68–70.
28.
BlytheAS. Electrical resistivity measurements of polymer materialsPolym Test1984; 4: 195–209.
29.
Annual Book of ASTM Standards. 09.01 ASTM D 297–93, 2003.
30.
Annual Book of ASTM Standards. 09.01 ASTM D 2240–02b, 2003.
31.
MatthanRK. Rubber engineering. 1st edn. New Delhi: Tata McGraw-Hill, 1998.
32.
Annual Book of ASTM Standards. 09.01 ASTM D 412-98a, 2003.
33.
SmithLP. The language of rubber. 1st edn. Oxford: Butterworth–Heinemann Ltd., 1993, pp. 14–15.
34.
Annual Book of ASTM Standards. 09.01 ASTM D 5963–97, 2003.