Flowing Performance,Microstructures,and Fracture Toughness of Dynamically Vulcanized PP/EPDM Blends

Abstract

The fracture behavior of polypropylene/ethylene—propylene— diene terpolymer (100/8) blends with different microstructure was investigated using the essential work of fracture approach. Ethylene—propylene—diene terpolymer and dicumyl peroxide were mixed in a single-screw extruder at 140°C, and the crosslinking reaction had hardly taken place at this temperature. Then the reactive extrusion of ethylene—propylene—diene terpolymer and polypropylene was performed on a twin-screw extruder at a temperature range of 160—210°C and ethylene—propylene—diene terpolymer was crosslinked in this process. Various crosslinking density of ethylene—propylene—diene terpolymer in polypropylene/ethylene—propylene—diene terpolymer (100/8) blends was obtained by varying the concentration of dicumyl peroxide. With increasing dicumyl peroxide concentration, melt flow rate of the blends gradually increased but the increasing trend was slowed up. The degradation reaction of polypropylene was markedly restrained by adopting such a processing method. From the result of scanning electron microscopy, the size of ethylene—propylene—diene terpolymer particles was reduced and a more uniform particle size distribution was obtained. The existence of polypropylene/ ethylene—propylene—diene terpolymer graft copolymer was demonstrated by differential scanning calorimetry and the negative effect of the graft copolymer on the crystalline rate of polypropylene macromolecules which were grafted onto ethylene—propylene—diene terpolymer chains was validated. The specific essential work of fracture (w_e) increased markedly with increasing dicumyl peroxide concentration for the blends prepared. When the concentration of dicumyl peroxide was 0.3 wt% of ethylene—propylene—diene terpolymer content, the value of w_e of the dynamic vulcanized blends was about 165% as that of polypropylene/ethylene—propylene—diene terpolymer simple blends or polypropylene, while the specific plastic work (βw_p) was still larger than that of polypropylene.

Keywords

polypropylene ethylene—propylene—diene terpolymer dynamic vulcanization essential work of fracture graft copolymer.

Get full access to this article

View all access options for this article.

References

Zebarjad, S.M. , Lazzeri, A. , Bagheri , R. , Seyed Reihani, S.M. and Frounchi, M. ( 2003). Fracture Mechanism Under Dynamic Loading of Elastomer-modified Polypropylene, Mater. Lett., 57: 2733-2741.

Arroyo, M. , Zitzumbo, R. and Avalos, F. ( 2000). Composites Based on PP/ EPDM Blends and Aramid Short Fibres: Morphology/Behaviour Relationship, Polymer, 41: 6351-6359.

Phan, T.T.M. , Denicolaand, A.J. and Schadler, L.S. (1998). Effect of Addition of Polyoxypropylenediamine on the Morphology and Mechanical Properties of Maleated Polypropylene/Maleated Rubber Blends, J. Appl. Polym. Sci., 68: 1451-1472.

Kim, B.C. , Hwang, S.S. , Lim , K.Y. and Yoon, K.J. (2000). Toughening of PP/ EPDM Blend by Compatibilization, J. Appl. Polym. Sci., 78: 1267-1274.

Kim, Y. , Cho, W.J. , Ha, C.S. and Kim, W. ( 1995). The Control of Miscibility of PP/EPDM Blends by Adding Lonomers and Applying Dynamic Vulcanization, Polym. Eng. Sci. , 35: 1592-1599.

Datta, S. , Naskar, K. , Jelenic, J. and Noordermeer, J.W.M. ( 2005). Dynamically Vulcanized PP/EPDM Blends by Multifunctional Peroxides: Characterization with Various Analytical Techniques, J. Appl. Polym. Sci., 98: 1393-1403.

Naskar, K. , Kokot, D. and Noordermeer, J.W.M. ( 2004). Influence of Various Stabilizers on Ageing of Dicumyl Peroxide-cured Polypropylene/Ethylene- Propylene-Diene Thermoplastic Vulcanizates, Polym. Degrad. Stabil., 85: 831-839.

Jiang, X.L. , Zhang, Y. and Zhang, Y.X. ( 2004). Study of Dynamically Cured PP/MAH-g-EPDM/Epoxy Blends, Polym. Test., 23: 259-266.

Ellul, M.D. , Tsouand, A.H. and Hu, W.G. ( 2004). Crosslink Densities and Phase Morphologies in Thermoplastic Vulcanizates, Polymer, 45: 3351-3358.

10.

Jang, B.Z. , Uhlmann, D.R. and Vander Sande, J.B. ( 1985). The Rubber Particle Size Dependence of Crazing in Polypropylene , Polym. Eng. Sci., 25: 643-651.

11.

Jafari, S.H. and Gupta, A.K. ( 2000). Impact Strength and Dynamic Mechanical Properties Correlation in Elastomer-Modified Polypropylene , J. Appl. Polym. Sci. , 78: 962-971.

12.

Jain, A.K. , Nagpal, A.K. , Singhal, R. and Gupta, N.K. ( 2000). Effect of Dynamic Crosslinking on Impact Strength and Other Mechanical Properties of Polypropylene/Ethylene-Propylene-Diene Rubber Blends, J. Appl. Polym. Sci., 78: 2089-2103.

13.

van der Wal, A. , Nijhof, R. and Gaymans, R.J. (1999). Polypropylene-Rubber Blends: 2. The Effect of the Rubber Content on the Deformation and Impact Behaviour, Polymer, 40: 6031-6044.

14.

Ha, C.S. , Cho, Y.W. , Go, J.H. and Cho, W.J. ( 2000). Dynamic Mechanical Properties of Polypropylene-g-maleic Anhydride and Ethylene-Propylene- Diene Terpolymer Blends: Effect of Blend Preparation Methods, J. Appl. Polym. Sci., 77: 2777-2784.

15.

Jiang, W. , Tjong, S.C. and Lia, R.K.Y. ( 2000). Brittle-Tough Transition in PP/EPDM Blends: Effects of Interparticle Distance and Tensile Deformation Speed, Polymer , 41: 3479-3482.

16.

Wang, Y. , Zhang, Q. , Na, B. , Du, R.N. , Fu, Q. and Shen, K.Z. ( 2003). Dependence of Impact Strength on the Fracture Propagation Direction in Dynamic Packing Injection Molded PP/EPDM Blends, Polymer, 44: 4261-4271.

17.

van der Wal, A. , Mulder, J.J. , Oderkerk, J. and Gaymans, R.J. (1998). Polypropylene-Rubber Blends: 1. The Effect of the Matrix Properties on the Impact Behaviour, Polymer, 39: 6781-6787.

18.

Ha, C.S. , Ihm, D.J. and Kim , S.C. (1986). Structure and Properties of Dynamically Cured EPDM/PP Blends, J. Appl. Polym. Sci. , 32: 6281-6297.

19.

van der Wal, A. and Gaymans, R.J. (1999). Polypropylene-Rubber Blends: 3. The Effect of the Test Speed on the Fracture Behaviour, Polymer, 40: 6045-6055.

20.

Yamazaki, T. and Seguchi, T. (2000). Electron Spin Resonance Study on Chemical Crosslinking Reaction Mechanisms of Polyethylene Using a Chemical Agent. V. Comparison with Polypropylene and Ethylene- Propylene Copolymer, J. Polym. Sci. Pol. Chem., 38: 3383-3389.

21.

Oksuz, M. and Eroglu, M. ( 2005). Effect of the Elastomer Type on the Microstructure and Mechanical Properties of Polypropylene, J. Appl. Polym. Sci. , 98: 1445-1450.

22.

van der Wal, A. , Verheul, A.J.J. and Gaymans , R.J. (1999). Polypropylene- Rubber Blends: 4. The Effect of the Rubber Particle Size on the Fracture Behaviour at Low and High Test Speed, Polymer , 40: 6057-6065.

23.

van der Wal, A. and Gaymans, R.J. (1999). Polypropylene-Rubber Blends: 5. Deformation Mechanism During Fracture, Polymer , 40: 6067-6075.

24.

Gupta, N.K. , Jain, A.K. , Singhal, R. and Nagpal, A.K. (2000). Effect of Dynamic Crosslinking on Tensile Yield Behavior of Polypropylene/Ethylene- Propylene-Diene Rubber Blends, J. Appl. Polym. Sci., 78: 2104-2121.

25.

Jain, A.K. , Guptaand, N.K. and Nagpal, A.K. ( 2000). Effect of Dynamic Cross-Linking on Melt Rheological Properties of Polypropylene/Ethylene- Propylene-Diene Rubber Blends, J. Appl. Polym. Sci., 77: 1488-1505.

26.

Wang, X.C. , Tzoganakis, C. and Rempel, G.L. ( 1996). Chemical Modification of Polypropylene with Peroxide/Pentaerythritol Triacrylate by Reactive Extrusion, J. Appl. Polym. Sci., 61: 1395-1404.

27.

Liang, J.Z. and Li, R.K.Y. ( 2000). Rubber Toughening in Polypropylene: A Review, J. Appl. Polym. Sci., 77: 409-417.

28.

Maspoch, M.L. , Gamez-Perez, J. , Gordillo , A. , Sanchez-Soto, M. and Velasco, J.I. ( 2002). Characterisation of Injected EPBC Plaques Using the Essential Work of Fracture (EWF) Method, Polymer, 43: 4177-4183.

29.

Arkhireyeva, A. and Hashemi, S. (2004). Effect of Temperature on Work of Fracture Parameters in Poly(Ether-Ether Ketone) (PEEK) Film, Eng . Fract. Mech., 71: 789-804.

30.

Gong, G. , Xie, B.H. , Yang, W. , Li, Z.M. , Zhang, W.Q. and Yang, M.B. ( 2005). Essential Work of Fracture (EWF) Analysis for Polypropylene Grafted with Maleic Anhydride Modified Polypropylene/Calcium Carbonate Composites, Polym. Test, 24: 410-417.

31.

Mouzakis, D.E. , Stricker, F. , Mulhaupt , R. and Karger-Kocsis , J. (1998 ). Fracture Behaviour of Polypropylene/Glass Bead Elastomer Composites by Using the Essential Work of Fracture Method, J. Mater. Sci., 33: 2551-2562.

32.

Karger-Kocsis, J. , Czigany, T. and Moskala, E.J. (1998). Deformation Rate Dependence of the Essential and Non-essential Work of Fracture Parameters in an Amorplous Copolyester, Polymer, 39: 3939-3944.

33.

Karger-Kocsis, J. and Moskala, E.J. (2000). Molecular Dependence of the Essential and Non-essential Work of Fracture of Amorphous Films of Poly(ethylene-2,6-naphthalate) (PEN), Polymer, 41: 6301-6310.

34.

Mouzakis, D.E. , Gahleitner, M. and Karger-Kocsis , J. (1998 ). Toughness Assessment of Elastomeric Polypropylene (ELPP) by the Essential Work of the Fracture Method, J. Appl. Polym. Sci., 70: 873-881.

35.

Marchal, Y. , Oldenhove, B. , Daoust , D. , Legras, R. and Delannay, F. (1998). Characterization of the Fracture Toughness of Rubber-Toughened Polypropylene Thin Plates, Polym. Eng. Sci., 38: 2063-2071.

36.

Xie, B.H. , Shen, Y.X. , Li , Z.M. , Yang, W. , Feng, J.M. and Yang, M.B. (2006). Fracture Behavior of Polypropylene/POE Blends with Different Mixed Ratios, Acta. Polym. Sin., 2: 335-339.

37.

Yokoyama, Y. and Ricco, T. (1998). Toughening of Polypropylene by Different Elastomeric Systems, Polymer , 39: 3675-3681.

38.

Mouzakis, D.E. , Mader, D. , Mulhaupt , R. and Karger-Kocsis , J. (2000 ). Relationship Between Morphology and Mechanical Properties of Polypropylene/Ethene-co-Butene Binary Blends with Various Butene Contents , J. Mater. Sci. , 35: 1219-1230.

39.

Yang, W. , Xie, B.H. , Shi, W. , Li, Z.M. , Liu, Z.Y. , Chen, J. , et al. (2006). Essential Work of Fracture Evaluation of Fracture Behavior of Glass Bead Filled Linear Low-Density Polyethylene, J. Appl. Polym. Sci., 99: 1781-1787.

40.

Yang, W. , Xie, B.H. , Shi, W. , Zuo, M. , Li, Z.M. and Yang, M.B. ( 2005). Essential Work of Fracture of Glass Bead Filled Low Density Polyethylene, J. Mater. Sci., 40: 5323-5326.

41.

Karger-Kocsis, J. , Barany, T. and Moskala, E.J. (2003). Plane Stress Fracture Toughness of Physically Aged Plasticized PETG as Assessed by the Essential Work of Fracture (EWF) Method, Polymer, 44: 5691-5699.

42.

Barany, T. , Karger-Kocsis, J. and Czigany, T. ( 2003). Effect of Hygrothermal Aging on the Essential Work of Fracture Response of Amorphous Poly(Ethylene Terephthalate) Sheets, Polym . Degrad. Stabil., 82: 271-278.

43.

Chen, H.B. , Karger-Kocsis, J. and Wu, J.S. ( 2004). Effects of Molecular Structure on the Essential Work of Fracture of Amorphous Copolyesters at Various Deformation Rates, Polymer, 45: 6375-6382.