Interactions of Nonaqueous Solvents with Textile Fibers Part III: The Dynamic Shrinkage of Polyester Yarns in Organic Solvents1

Abstract

'rhe broad spectrum of interactions hetween a polyester yarn and different organic solvents has been investigated with a new experimerltal methocl called dynamic shrinkage. This technique is based on the measurement of the length changes of polyester yarns immersed in a solvent at programmed rates of heating.

The dynamic shrinkage curves of a polyester yarn in various solvents are usually composed of a noncquilibrium and an equilibrium shrinkage region. From the former, it is possible to estimate the activation energies for the shrinkage process. From the equilibrium shrinkages, two analytical approaches have been used to estimate the glass-transition temperatures of about 22 polyester-solvent systems. The lowering of the glass-transition temperature of polyester by organic solvents is expressed as a function of their total solubility parameter. A bimodal distribution with interaction maxima at solu bitity parameter values of 10 and 12 is observed. 'I'he effects of solvent-induced crystallization on the transition tempera tures of polyester-solvent systems are discussed.

Keywords

Polyester yarns. Yarns shrinkage. Nonaqueous solvents polyester-solvent systems lolymer. Temperature heat ing rates glass-transition temperature. Solubility parameter diffusion shrinkage regions sotvent-induced crystalliza tion bimodal distribution activation energies. Dynamic shrinkage. Organic solvents.

Get full access to this article

View all access options for this article.

References

Ribnick, A.S. , Weigmann, H.-D. , and Rebenfetd , L. , Interactions of Nonaqueous Solvents with Textile Fibers. Part II. Isothermal Shrinkage Kinetics of a Polyester Yarn, Textile Res. J. 43, 123-130 (1973).

Dumbleton, J.H. , Spin Orientation Measurement in Polyethylene Terephthalate, Textile Res. J. 40, 1035-1041 (1970).

Ward, I.M. , 'rhe Molecular Structure and Mechanical Properties of Polyethylene Terephthalate Fibers, Textile Res. J. 31, 650-664 (1961).

Cobbs, W.H., Jr. , and Burton, R.L. , Crystallization of Polyethylene Terephthalate , J. Polymer Sci. 10, 275-290 (1953).

Ribnick, A. S. and Weigmann, H.-D., Unpublished results.

Hansen, C.M. , The Three Dimensional Solubility Parameter, J. Paint Technol . 39, No. 505, 104-117 (1967).

Burrell, H. , Solubility Parameters for Film Formers, Official Digest 27, 726 (1955).

Ribnick, A.S. , Weigmann, H.-D. , and Rebenfeld , L. , Interactions of Nonaqueous Solvents with Textile Fibers. Part I : Effects of Solvents on the Mechanical Properties of a Polyester Yarn, Textile Res. J . 42, 720-726 (1972).

Knox, B. H. and Weigmann, H.-D., To be published.

10.

Flory, P.J. , in "Principles of Polymer Chemistry," Chap. 12, Ithaca, N. Y., Cornell Univ. Press, 1953.

11.

Moore, W.R. and Sheldon, P.R. , The Crystallization of Polyethylene Terephthalate by Organic Liquids, Polymer 2, 315-321 (1961).

12.

Prevorsek, D. , Structure of Semicrystalline Fibers from Interpretation of Anelastic Effects, J. Polymer Sci., C, Polymer Symposia, No. 32, 343-375 (1971).